The effect of light rare earth element substitution in Yb14MnSb11 on thermoelectric properties

Abstract

After the discovery of Yb14MnSb11 as an outstanding p-type thermoelectric material for high temperatures (≥900 K), site substitution of other elements has been proven to be an effective method to further optimize the thermoelectric properties. Yb14−xRExMnSb11 (RE = Pr and Sm, 0 < x < 0.55) compounds were prepared by powder metallurgy to study their thermoelectric properties. According to powder X-ray diffraction, these samples are iso-structural with Yb14MnSb11 and when more than 5% RE is used in the synthesis the presence of (Yb,RE)4Sb3 is apparent after synthesis. After consolidation and measurement, (Yb,RE)Sb and (Yb,RE)11Sb10 appear in the powder X-ray diffraction patterns. Electron microprobe analysis results show that consolidated pellets have small (Yb,RE)Sb domains and that the maximum amount of RE in Yb14−xRExMnSb11 is x = 0.55, however, (Yb,RE)11Sb10 cannot be distinguished by electron microprobe analysis. By replacing Yb2+ with RE3+, one extra electron is introduced into Yb14MnSb11 and the carrier concentration is adjusted. Thermoelectric performance from room temperature to 1275 K was evaluated through transport and thermal conductivity measurements. The measurement shows that Seebeck coefficients initially increase and then remain stable and that electrical resistivity increases with substitutions. Thermal conductivity is slightly reduced. Substitution of Pr and Sm leads to enhanced zT. Yb13.82Pr0.18Mn1.01Sb10.99 has the best maximum zT value of ∼1.2 at 1275 K, while Yb13.80Sm0.19Mn1.00Sb11.02 has its maximum zT of ∼1.0 at 1275 K, respectively, ∼45% and ∼30% higher than Yb14MnSb11 prepared in the same manner.

Graphical abstract: The effect of light rare earth element substitution in Yb14MnSb11 on thermoelectric properties

Supplementary files

Article information

Article type
Paper
Submitted
29 iyl 2015
Accepted
31 iyl 2015
First published
31 iyl 2015

J. Mater. Chem. C, 2015,3, 10566-10573

Author version available

The effect of light rare earth element substitution in Yb14MnSb11 on thermoelectric properties

Y. Hu, S. K. Bux, J. H. Grebenkemper and S. M. Kauzlarich, J. Mater. Chem. C, 2015, 3, 10566 DOI: 10.1039/C5TC02326B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements