Issue 11, 2014

Enhancing oxygen permeation through hierarchically-structured perovskite membranes elaborated by freeze-casting

Abstract

Innovative asymmetric oxygen-transport membrane architectures were prepared by combining freeze-casting and film deposition techniques. Freeze-casting enabled the optimization of the gas transport through the support by creating a hierarchical porosity while a dense top-layer of 30 μm was coated over this support by screen printing. The versatility of this technique was demonstrated by preparing highly porous bodies made of fast ionic conductors, e.g. perovskites and doped ceria fluorites, with a large number of applications in catalysis, electrochemistry and gas separation. Permeation tests using an all-La0.6Sr0.4Co0.2Fe0.8O3−δ asymmetric membrane proved the beneficial effect of such porous supports over the O2 fluxes with a maximum value of 6.8 mL min−1 cm−2 at 1000 °C, markedly above the results achieved so far with conventional preparation techniques. Gas permeance study through the porous freeze-cast support showed that the particular pore structure allows the gaseous transport resistance to be minimized. The related pressure drop is found to be very low in comparison with conventional porous supports, e.g. tape-cast supports, with for example only 0.59 bar mm−1 with argon at 800 °C for an inlet flow of 400 mL min−1 cm−2. Finally, the stability of the asymmetric membrane has been evaluated under CO2 atmosphere during 48 hours and at 900 °C. The membrane is found to be stable without deactivation nor decrease in the O2 permeation flux.

Graphical abstract: Enhancing oxygen permeation through hierarchically-structured perovskite membranes elaborated by freeze-casting

Supplementary files

Article information

Article type
Paper
Submitted
10 Oct 2013
Accepted
16 Dec 2013
First published
16 Dec 2013

J. Mater. Chem. A, 2014,2, 3828-3833

Enhancing oxygen permeation through hierarchically-structured perovskite membranes elaborated by freeze-casting

C. Gaudillere, J. Garcia-Fayos and J. M. Serra, J. Mater. Chem. A, 2014, 2, 3828 DOI: 10.1039/C3TA14069E

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements