Direct synthesis of cobalt nanoparticle-imbedded mesoporous carbons for high-performance dye-sensitized solar cell counter electrodes

Abstract

Metal Co nanoparticle-imbedded ordered mesoporous carbon (Co-OMC) materials were synthesized by a facile low-temperature hydrothermal approach of making phenolic resin-F127 composites with various amounts of cobalt nitrate and their subsequent carbonization. The synthesized Co-OMCs possess a high BET surface area, uniform 2-D hexagonal ordered mesostructure and large pore volume, and the imbedded Co nanoparticles are homogeneously distributed with sizes of 2–5 nm. In comparison with the pristine OMC, the Co-OMCs exhibit a higher graphitization degree, which is beneficial for enhancing the electrical conductivity. The Co-OMCs were applied as counter electrode catalysts in dye-sensitized solar cells (DSSCs), revealing that the electrocatalytic activity for I3 reduction is improved due to a synergistic catalytic effect between the OMC and an appropriate amount of Co nanoparticles, and the electrical conductivity was also enhanced. The DSSCs based on Co-OMC counter electrodes exhibit an optimum energy conversion efficiency of 7.02%, which is larger than that of the cell based on a pure OMC counter electrode (6.18%), and comparable to that of the cell with a Pt counter electrode (7.10%) under the same experimental conditions. The high energy conversion efficiency, low cost and simple fabrication process make the Co-OMC counter electrode promising as a potential replacement of the conventional Pt electrode in DSSCs.

Graphical abstract: Direct synthesis of cobalt nanoparticle-imbedded mesoporous carbons for high-performance dye-sensitized solar cell counter electrodes

Article information

Article type
Paper
Submitted
09 Oct 2014
Accepted
17 Oct 2014
First published
23 Oct 2014

J. Mater. Chem. C, 2014,2, 10312-10321

Author version available

Direct synthesis of cobalt nanoparticle-imbedded mesoporous carbons for high-performance dye-sensitized solar cell counter electrodes

M. Chen, L. Shao, X. Qian, T. Ren and Z. Yuan, J. Mater. Chem. C, 2014, 2, 10312 DOI: 10.1039/C4TC02270J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements