Chemical vapor infiltration tailored hierarchical porous CNTs/C composite spheres fabricated by freeze casting and their adsorption properties

Abstract

Carbon nanotubes (CNTs) are one of the most promising candidates as adsorbents in many fields due to their unique structural characteristics. In this paper, hierarchical porous CNTs/carbon (CNTs/C) composite spheres were prepared and their strength and adsorption of vitamin B12 (VB12) were investigated. The initial porous CNT spheres were fabricated by freeze casting followed by freeze drying. Afterwards, the primary porous CNT spheres were further reinforced and tailored by chemical vapor infiltration (CVI) and steam activation. Consequently, the composite CNTs/C spheres with hierarchical porous structure and high strength were successfully fabricated. SEM and polarized light microscopy observations showed that, in addition to macro-sized radial through-pores in the spheres, many micro-sized pores were distributed uniformly in the wall of the radial tunnel-like through-pores. Mercury porosimetry and BET tests indicated that the width of the radial lamellar channels was about 5–15 μm, and the average diameter of the mesopores was about 3.8 nm. Adsorption of VB12 for these hierarchical porous CNTs/C spheres could reach 51.48 mg g−1, which is about 3.7 and 3.4 times those of traditional activated carbon beads and macroporous resin beads, respectively.

Graphical abstract: Chemical vapor infiltration tailored hierarchical porous CNTs/C composite spheres fabricated by freeze casting and their adsorption properties

Associated articles

Article information

Article type
Paper
Submitted
10 Dec 2014
Accepted
15 Jan 2015
First published
20 Jan 2015

RSC Adv., 2015,5, 16870-16877

Author version available

Chemical vapor infiltration tailored hierarchical porous CNTs/C composite spheres fabricated by freeze casting and their adsorption properties

J. Wang, Q. Gong, D. Zhuang and J. Liang, RSC Adv., 2015, 5, 16870 DOI: 10.1039/C4RA16082G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements