Mechanical and tribological characteristics of carbon nanotube-reinforced polyvinylidene fluoride (PVDF)/epoxy composites

Abstract

In this study, epoxy (EP) composites filled with different contents of polyvinylidene fluoride (PVDF) and carbon nanotubes (CNTs) were fabricated by the solvent evaporation and curing method. FT-IR and XRD analysis were performed to explore the discolorment mechanism of the PVDF/EP composites before and after curing. The effects of the PVDF and CNT content on the mechanical and tribological properties of the composites were investigated. Results revealed that 1.0% CNT/30% PVDF/EP composites exhibited a 36.2% and 10.1% increase in flexural strength and hardness, as compared to those of the 30% PVDF/EP composites. The wear rates of 1.0% CNT/30% PVDF/EP composites and 30% PVDF/EP composites were 92.1% and 86.8% lower than that of pristine EP under 1.0 MPa and 0.76 m s−1, respectively. Meanwhile, the fractured and worn surfaces of specimens were both analyzed by the observations of SEM. In addition, wear tests under various applied loads were conducted for pristine EP, 30% PVDF/EP and 1.0% CNT/30% PVDF/EP composites. The results showed that the wear properties of the two composites were both superior to those of pristine EP due to the formation of a transfer film as revealed by SEM-EDS analysis, which could effectively protect the worn surface from direct abrasion during the wear testing.

Graphical abstract: Mechanical and tribological characteristics of carbon nanotube-reinforced polyvinylidene fluoride (PVDF)/epoxy composites

Article information

Article type
Paper
Submitted
08 Jan 2016
Accepted
27 Apr 2016
First published
28 Apr 2016

RSC Adv., 2016,6, 45636-45644

Mechanical and tribological characteristics of carbon nanotube-reinforced polyvinylidene fluoride (PVDF)/epoxy composites

H. Wang, R. Wang, L. Sun, Z. Liu, Y. Zhu and Y. Zhu, RSC Adv., 2016, 6, 45636 DOI: 10.1039/C6RA00577B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements