Oxidized multiwall carbon nanotube modified separator for high performance lithium–sulfur batteries with high sulfur loading

Abstract

Recently, researchers have demonstrated that a thin conductive coating on a separator toward the cathode side of lithium–sulfur (Li–S) batteries can improve their electrochemical performance significantly. However, their experimental data are mostly based on cathodes with low sulfur mass loading, while the practical application of Li–S cells requires cathodes with high sulfur loading (≥4 mg cm−2) and high sulfur content (≥70 wt%). Thus, research on the effects of such coatings on Li–S cells with high sulfur loading is essential. Herein, we demonstrate the effectiveness of an oxidized multiwall carbon nanotube (o-MWCNT) coating (0.4 mg cm−2) for improving the electrochemical performance of cathodes with sulfur loading of 5.0 mg cm−2. Due to the physical and chemical trapping of polysulfides, efficient electron conduction and fast ion transport induced by the coating, the fabricated Li–S batteries show dramatically improved specific discharge capacities of up to 925 mA h g−1 (the areal capacity of the cathode is 4.6 mA h cm−2) at a current density of 100 mA g−1 after 50 cycles; they also show good rate performance.

Graphical abstract: Oxidized multiwall carbon nanotube modified separator for high performance lithium–sulfur batteries with high sulfur loading

Supplementary files

Article information

Article type
Paper
Submitted
05 Jun 2016
Accepted
07 Sep 2016
First published
08 Sep 2016

RSC Adv., 2016,6, 89972-89978

Oxidized multiwall carbon nanotube modified separator for high performance lithium–sulfur batteries with high sulfur loading

X. Cheng, W. Wang, A. Wang, K. Yuan, Z. Jin, Y. Yang and X. Zhao, RSC Adv., 2016, 6, 89972 DOI: 10.1039/C6RA14581G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements