Graphene formation at 150 °C using indium as catalyst

Abstract

Graphene is generally synthesized at high temperatures. Here we demonstrate a simple method to synthesize graphene at 150 °C. Carbon foils were irradiated with Ar+ ions at 1 keV with a simultaneous supply of catalyst metal without any intentional heating to survey the novel catalyst for graphene growth at low temperature. The ion irradiated surfaces were covered with densely distributed conical structures sometimes with a nanofiber on their respective tips. As revealed by high resolution (HR) transmission electron microscopy (TEM), the conical tips featured few layer graphene only for the newly selected catalyst metal, In, which is rarely used for the chemical vapor deposition (CVD) synthesis of graphene. This observation gives a new insight into the catalytic activity during graphene synthesis. Encouraged by this ion-induced graphene formation, samples of a thin, amorphous carbon film on SiO2 substrates overlaid with this novel catalyst film were prepared, and finally, graphene growth was achieved by simple vacuum heating at 150 °C.

Graphical abstract: Graphene formation at 150 °C using indium as catalyst

Article information

Article type
Paper
Submitted
18 Jul 2017
Accepted
27 Sep 2017
First published
09 Oct 2017
This article is Open Access
Creative Commons BY license

RSC Adv., 2017,7, 47353-47356

Graphene formation at 150 °C using indium as catalyst

M. I. Araby, M. S. Rosmi, R. Vishwakarma, S. Sharma, Y. Wakamatsu, K. Takahashi, G. Kalita, M. Kitazawa and M. Tanemura, RSC Adv., 2017, 7, 47353 DOI: 10.1039/C7RA07892G

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements