New ferrocenyl-containing organic hole-transporting materials for perovskite solar cells in regular (n-i-p) and inverted (p-i-n) architectures

Abstract

Three triphenylamine derivatives containing ferrocenyl groups (JW6, JW7 and JW8) were synthesized by facile syntheses. Their HOMO levels match the valence band energy of CH₃NH₃PbI₃. The introduction of ferrocenyl was aimed to obtain hole transporting materials with high mobility for perovskite solar cells. JW7 shows higher hole mobility (4.2 × 10⁻⁴ cm² V⁻¹ s⁻¹) than JW6 (1.3 × 10⁻⁴ cm² V⁻¹ s⁻¹) and JW8 (1.5 × 10⁻⁴ cm² V⁻¹ s⁻¹). Their film-forming properties are affected by their molecule structures. The methoxyl and N,N-dimethyl terminal substituents of JW7 and JW8 are beneficial for having better solubility than JW6. The regular mesoporous TiO₂-based perovskite solar cells (n-i-p) and the inverted planar heterojunction perovskite solar cells (p-i-n) fabricated using JW7 show the highest power conversion efficiency of 9.36% and 11.43% under 100 mW cm⁻² AM1.5G solar illumination. For p-i-n cells, the standard HTM PEDOT-based cell reaches an efficiency of 12.86% under the same conditions.