Colossal thermoelectric enhancement in Cu2+xZn1−xSnS4 solid solution by local disordering of crystal lattice and multi-scale defect engineering

Abstract

Polycrystalline sulfides are promising thermoelectric materials because of their abundance, non-toxicity, and low cost. However, their low thermoelectric performance hampers their possible large-scale industrial application. In this work, Cu self-doping in Cu2+xZn1−xSnS4, prepared using a simple processing route, realizes the decoupling of thermal and electric transport as follows. The additional copper ions occupy Zn sites and provide more carriers, which leads to excellent hole conductivity. Moreover, when x is above 0.125, the content of Cn/Zn disordered sites is beyond the percolation threshold (∼0.3) of thermal diffusivity. A maximum power factor (450 μW m−1 K−2) is obtained for Cu2.125Zn0.875SnS4. Combined with ultra-low specific heat below the theory predicted minimum for structural disordering on the copper and zinc sites, the κ of the material reduces to 0.22 W m−1 K−1 at 773 K, which is minimum in thermoelectric materials up to now. Moreover, hot forging (deformation strain ∼64% and maximum of displacement rate ∼18 mm min−1), a dynamic plastic deformation process, was employed to produce defects on different length scales (point defects, dislocations, stacking faults and deformation twins), that optimize the power factor and lattice thermal conductivity. Based on the above synergistic effects, a high ZT value of 1.1 has been achieved in Cu2.125Zn0.875SnS4 ceramics, and there is 18-fold increase in ZT value compared with that of conventionally processed intrinsic Cu2ZnSnS4.

Graphical abstract: Colossal thermoelectric enhancement in Cu2+xZn1−xSnS4 solid solution by local disordering of crystal lattice and multi-scale defect engineering

Supplementary files

Article information

Article type
Paper
Submitted
10 Feb 2020
Accepted
07 May 2020
First published
12 May 2020

J. Mater. Chem. A, 2020,8, 10909-10916

Colossal thermoelectric enhancement in Cu2+xZn1−xSnS4 solid solution by local disordering of crystal lattice and multi-scale defect engineering

Q. Jiang, H. Yan, Y. Lin, Y. Shen, J. Yang and M. J. Reece, J. Mater. Chem. A, 2020, 8, 10909 DOI: 10.1039/D0TA01595D

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements