Star polymer–TiO2 nanohybrids to effectively modify the surface of PMMA dielectric layers for solution processable OFETs

Abstract

Solution processable dielectric nanomaterials were prepared by the polymer-templated synthesis of hybrid nanoparticles containing TiO2. Well defined poly(styrene-co-acrylonitrile)-b-poly(acrylic acid)-poly(divinylbenzene) (PSAN-b-PAA-PDVB) star-shaped copolymers were prepared using activators regenerated by electron transfer atom transfer radical polymerization (ARGET ATRP) and then used as templates for the synthesis of nanoconfined TiO2. Unexpectedly, even very low inorganic loadings significantly modified the surface of the poly(methyl methacrylate), (PMMA), layers. Relatively thick (with a thickness of 0.6 μm, affordable for the inkjet printing method) PMMA layers comprising merely 0.4% wt. of the hybrid TiO2 nanoparticles were applied as gate dielectrics for organic field effect transistors (OFETs). Such a low content of hybrid nanoparticles, which essentially did not affect the dielectric properties of the PMMA layer, significantly improved the efficiency of the obtained OFETs, as compared with OFETs based on pure PMMA as gate dielectrics, e.g. charge carrier mobility has increased nearly 10-fold from ca. 0.06 to ca. 0.5 cm2 V−1 s−1. The improvement of OFET parameters may be explained by a significant decrease of roughness (root mean square roughness of the dielectric layer was reduced from 15.3 nm to 0.43 nm) and change of surface energy (from 32.4 to 45.5 mN m−1) of the gate dielectric layer induced by hybrid nanoparticles. OFETs with novel dielectric layers showed current–voltage characteristics with high drain currents and negligible hysteresis. The presented results showed that the physicochemical properties of the surface of the polymer layer may be easily modified by the addition of small amounts of new hybrid nanoparticles.

Graphical abstract: Star polymer–TiO2 nanohybrids to effectively modify the surface of PMMA dielectric layers for solution processable OFETs

Supplementary files

Article information

Article type
Paper
Submitted
02 Jul 2020
Accepted
11 Dec 2020
First published
12 Dec 2020

J. Mater. Chem. C, 2021,9, 1269-1278

Star polymer–TiO2 nanohybrids to effectively modify the surface of PMMA dielectric layers for solution processable OFETs

K. Budzalek, H. Ding, L. Janasz, A. Wypych-Puszkarz, O. Cetinkaya, J. Pietrasik, M. Kozanecki, J. Ulanski and K. Matyjaszewski, J. Mater. Chem. C, 2021, 9, 1269 DOI: 10.1039/D0TC03137B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements