A broadband near-infrared Cr3+-doped phosphor applied to near-infrared light-emitting diodes: enhanced luminescence and thermal stability by annealing

Abstract

Cr³⁺-activated phosphors with high quantum efficiency show excellent promise in the field of near-infrared (NIR) phosphor converted light-emitting diodes (pc-LEDs). Here, we design an annealing program for Cr³⁺-doped phosphors containing variable valence elements that cannot be prepared in a reducing atmosphere to enhance their luminescence efficiency and thermal stability. A novel phosphor, Li₂Mg₃SnO₆:Cr³⁺, developed by this annealing design, containing variable valence element Sn, exhibits higher quantum efficiency and better thermal stability than the one prepared by the conventional solid-state reaction. The Li₂Mg₃SnO₆:0.03Cr³⁺ sample exhibits broadband NIR emission with a full width at half-maximum (FWHM) of 201 nm. After annealing, the internal quantum efficiency (IQE) and external quantum efficiency (EQE) of the Li₂Mg₃SnO₆:0.03Cr³⁺ sample are enhanced from 48.5% to 84.7% and from 22.7% to 32.6%, respectively, and the thermal quenching temperature at which the luminescence intensity of the phosphor reduces to half of its initial value is promoted from ∼400 K to ∼425 K. The luminescence intensity of the optimized Li₂Mg₃SnO₆:0.03Cr³⁺ sample at 425 K (∼152 °C) remains 49.2% of its initial intensity at 300 K. A NIR pc-LED is fabricated by combining the optimized Li₂Mg₃SnO₆:0.03Cr³⁺ sample with a blue LED (455 nm blue chip), and the NIR radiant fluxes of 3.676 mW (at 10 mA) and 29.21 mW (at 100 mA), as well as a maximum NIR photoelectric efficiency of 14.2%, are obtained. The results show that this novel phosphor has great application potential in NIR pc-LEDs, and the annealing design exhibits huge potential for improving the optical properties of Cr³⁺-activated phosphors.