Ti3AlC2 MXene nanosheets as a novel corrosion inhibitor for carbon steel in 0.5 M sulfuric acid solution

Abstract

Herein we report that Ti3AlC2 MXene nanosheets were identified as a highly effective cathodic protection corrosion inhibitor for carbon steel in hydrochloric acid solution. Ti3AlC2 Mxene nanosheets form a stable inhibition layer on metal surfaces due to their high adsorption capacity and act as a barrier or protective film to prevent attacks from corrosive substances and thus lead to an extended metal service life.

Graphical abstract: Ti3AlC2 MXene nanosheets as a novel corrosion inhibitor for carbon steel in 0.5 M sulfuric acid solution

Supplementary files

Transparent peer review

To support increased transparency, we offer authors the option to publish the peer review history alongside their article.

View this article’s peer review history

Article information

Article type
Paper
Submitted
28 Oct 2023
Accepted
15 Jan 2024
First published
31 Jan 2024
This article is Open Access
Creative Commons BY license

RSC Adv., 2024,14, 4335-4338

Ti3AlC2 MXene nanosheets as a novel corrosion inhibitor for carbon steel in 0.5 M sulfuric acid solution

X. Min, S. Ma, Z. Zhou, D. Wu and B. Liao, RSC Adv., 2024, 14, 4335 DOI: 10.1039/D3RA07341F

This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. You can use material from this article in other publications without requesting further permissions from the RSC, provided that the correct acknowledgement is given.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements