Near room temperature thermoelectric performance improvement for Mg2Sn

Abstract

Mg2Sn is a promising medium-temperature thermoelectric material due to its superior performance and non-toxic, low-cost nature. Because of the divergence of band effective mass and degeneracy between the conduction and valence band, Mg2Sn is also promising to achieve superior performance near room temperature. To realize the desired bandgap and optimal carrier concentration, in this work, Mg2Pb is alloyed to reduce the bandgap of Mg2Sn, and Bi is adopted for carrier concentration optimization. Alloying with Mg2Pb makes the bandgap gradually tuned, and with the increase in carrier concentration, more conduction band valleys are involved for electronic transport as the Fermi level goes deeper. Besides, the phonon scattering is simultaneously enhanced because of the introduced large number of defects. Finally, a power factor as high as 52 μW cm−1 K−2 at 400 K, and 42 μW cm−1 K−2 at room temperature is obtained in this work, and the peak zT value for the Mg2.03Sn0.734Pb0.25Bi0.016 sample reaches 0.8 at 500 K, the average figure of merit is zTave ∼ 0.6 within the temperature range of 300–550 K, surpassing many Mg2Sn based materials near room temperature. The thermoelectric figure of merit can achieve a higher value if the lattice thermal conductivity is further reduced, which demonstrates that Mg2Sn is promising for near room temperature applications.

Graphical abstract: Near room temperature thermoelectric performance improvement for Mg2Sn

Supplementary files

Article information

Article type
Paper
Submitted
26 Feb 2024
Accepted
22 May 2024
First published
05 Jun 2024

J. Mater. Chem. C, 2024,12, 8935-8943

Near room temperature thermoelectric performance improvement for Mg2Sn

L. Zhang, J. Li, H. Chen, J. Feng and R. Liu, J. Mater. Chem. C, 2024, 12, 8935 DOI: 10.1039/D4TC00761A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements