Sung Il Ahn*a,
Kukjoo Kimb,
Jun Young Kima,
Eun Se Kima,
Ji Ye Hana,
Ji Won Eoma,
Kyeong-Keun Choic,
Jung-Chul Parka,
Sung-Hoon Kima,
Euh Duck Jeongd and
Kyung Cheol Choib
aDepartment of Engineering in Energy and Applied Chemistry, Silla University, Busan 617-736, Republic of Korea. E-mail: siahn@silla.ac.kr
bDepartment of Electrical Engineering, KAIST, Daejeon 305-701, Republic of Korea
cNational Center for Nanomaterials Technology (NCNT), Pohang 790-784, Republic of Korea
dHigh-Technology Components & Materials Research Center & Busan Center, Korea Basic Science Institute (KBSI), Busan 609-735, Republic of Korea
First published on 12th May 2014
Graphene oxide (GO) with an abnormal structure was isolated in an alcoholic solvent. An abnormally low C–O/C–C ratio and large red-shift of the CO vibration indicated that the GO was a reduction intermediate of graphene oxide, which could be reduced more easily under mild conditions, even without reducing chemicals.
Based on this simple concept, we analyzed for periodically exfoliated GO from the same graphite oxide in an alcoholic solvent and found that the exfoliated GO had an abnormal structure suspected as an oxidation intermediate of graphene, and/or a reduction intermediate of GO. In this study, we characterized the structure of the abnormal GO exfoliated in the alcoholic solvent (e-GO). In addition, partially reduced GO (rGO) was introduced to compare a reduction intermediate of GO. We then showed that the intermediates were made of an easily reducible GO sheet at low temperature, which could be applied to the printed electronics as an electrode material. Except for the direct reduction of GO film with hydrogen gas,18 which requires a high reaction temperature, the reduction of GO using chemical methods has a critical problem with the agglomeration of reduced GO (RGO; completely reduced form of GO). We had difficulty obtaining a high quality thin film with the coagulated RGO. For this reason, gaseous hydrazine has been applied to the reduction of thin film GO.19 However, it is hard to obtain complete RGO film due to the diffusion limit of gaseous hydrazine over a short reaction time.20 We considered how to obtain stable RGO or how to control the oxygen content of RGO using hydrazine in a solution without coagulation of the RGO sheet. If such a process is possible, we will be able to modify the electrical property of RGO with reasonable coating property for further applications. For this purpose, in this study, we developed and characterized e-GO and rGO with high stability in water.
A considerable amount of e-GO (about 0.11 g) was obtained, while the amount of exfoliated GO for 30 min sonication in distilled water from the same graphite oxide after the exfoliation of e-GO (ew-GO) was about 0.25 g. A dispersion study on graphite oxide in various solutions indicated that GO was hardly dispersed in the absolute ethanol.21 However, we found that some of GO from graphite oxide can be well dispersed in an ethanol solution with a small amount of distilled water as shown in Fig. 1f. Far from our expectation, the e-GO had an abnormally low C–O/C–C ratio compared to about 3:2 (including CO) of GOs reported in the literature as shown in Fig. 1b.22,23 The same result was obtained several times at different oxidation conditions (see ESI, Fig. S2†). Apparently, the heterogeneity of reaction mixture is the main reason for the formation of e-GO. In Fig. 1e, synthesized XPS spectra of C 1s from e-GO and ew-GO by a weight factor after normalization to C–C had a similar curve compared to the Ref. GO, which means that the e-GO and ew-GO are hardly affected by the exfoliation conditions. What is more, e-GO is the earliest portion detached from GO sheets of graphite oxide by sonication for 5 min. Imagine the frayed surface of graphite after oxidation. A common sense on GO exfoliation would be that highly oxygenated GO should be the first detached from graphite oxide. Interestingly, the peak position of the CO vibration of e-GO in Fig. 2b is red-shifted about 28 cm−1 (from 1725 cm−1 to 1697 cm−1) compared to ew-GO.
Considering the vibration of CO by unsaturated carboxylic group placed below 1700 cm−1, this result is indicating that e-GO is less oxidized than normal GO.
We had obtained intermediates of RGO through a weak reduction of GO using hydrazine and compared the peak position of CO. In Fig. 2c, we can clearly see the shifting of the CO vibration as the degree of reduction is increased by an increase of the reducing agent (added 0.034 (rGO1), 0.064 (rGO2), 0.102 (rGO3), 0.136 (rGO4), 0.170 (rGO5), and 0.34 ml (rGO6) of 0.8 wt% hydrazine to 30 ml of 0.02 wt% Ref. GO). Based on the FT-IR results, we consider the unusual e-GO as a kind of oxidation intermediate of graphene. In the cases of rGO4 and rGO5, reduced by more hydrazine, they showed a slightly blue-shifted (about 8 cm−1) CO vibration compared to rGO3 (Fig. 2d), which will be explained in the next section.
An uncommon behavior was observed during our investigation on the rGO. Reduction of GO in an aqueous solution gave only aggregated RGO due to the van der Waals forces between sheets of RGO, which is the same as with graphite24 and low polarity of RGO in polar aqueous media. Thus, we may be confident in our prediction that a reaction mixture of GO is more unstable in aggregation as the reductant increases. Naturally, we will say that a higher content of reducing agent will also result in faster aggregation of rGO. However, as shown in Fig. 3a, the lower end in a certain range of reducing agent content produces faster aggregation of rGO (added 0.034 (rGO1′), 0.064 (rGO2′), 0.102 (rGO3′), 0.136 (rGO4′), and 0.170 (rGO5′) of 8 wt% hydrazine to 30 ml of 0.2 wt% Ref. GO). The same experiments were carried out several times and had the same coagulation tendency. The surface image of spin coated rGO' samples showed a similar tendency of coagulation as seen in Fig. 3b. This interesting phenomenon appears to be related to the structure of reduction intermediates of GO, which have various SPCCs, the size of which is dependent on the concentration of the reducing agent.
As we mentioned, GO consists of non-oxygenated and oxygenated regions.16,17 When a small amount of reducing agent is reacted with GO, we can image that the hydrazine starts to seek oxygenated sites to reduce where they become a more stable intermediate of RGO. The moderately slow reaction rate of hydrazine in the reaction mixture apparently allows enough time to find those sites (see ESI, Fig. S3†). Consequently, the most likely sites on GO to be reduced are the sites near preexisting sp2 carbon, since the reduced sites are easily conjugated with them and thus stabilized thermodynamically. This gives a reduction intermediate with large SPCCs on GO, which leads to coagulation of rGO quickly. Increasing the hydrazine content seems to reduce most of the oxygenated sites of GO and to form new small SPCCs.16 It still has oxygenated regions surrounding the sp2 carbons, which obstructs and delays the coagulation between sheets of rGO in the solution. The blue-shifted CO vibration in Fig. 2d and the increasing D band of Raman spectra in Fig. 4a for rGO4 and rGO5 as the hydrazine content increases appears related to the reduction intermediate of GO with small SPCCs. On rGO6, further reduction using hydrazine creates giant SPCCs on GO by combining the small SPCCs and leads to faster coagulation than rGO5 due to an increase of the van der Waals force between rGO sheets in the solution.
The broadness and intensity of the G and D bands in Raman spectra from GO or rGO is related to the oxide concentration, the structural defects, and/or the disordered carbon bonds as has been reported in many studies.25,26 Thus, the degree of oxidation in GO can be estimated by the D/G intensity ratio and the broadness of the bands. In the case of rGO, the intensity of the D band depends mostly on the size of SPCCs in a similar C–O/C–C ratio of rGO because a SPCC is surrounded by non-sp2 carbons including oxygen. In other words, the size of SPCCs is determined by the number of SPCC in a similar C–O/C–C ratio of rGO (Fig. 4d). Thus, the D band increases as the number of SPCC increases if the SPCC has Raman active six-folded symmetries of condensed benzene rings: breathing mode of A1g symmetry activated by disordering.25 In Fig. 4b, we observe a fluctuation in the D/G intensity ratio as the hydrazine content increases, while the full width at half maximum (FWHM) of the D band decreases greatly. The Raman spectra of rGO1 and rGO2 have slightly lower D/G ratios and broader D bands than those of the reference GO, which indicates that the size of preexisting SPCCs on rGO1 and rGO2 is increased by reduction rather than new SPCCs being created. In contrast, rGO4 and rGO5 have higher D/G ratios and sharper D bands than the rGO1, rGO2 or reference GO. Considering the increase of the D band and supposing the decrease of FWHM is directly related to the number of SPCCs with similar six-folded symmetries, this result confirms that a significant number of small sized SPCCs with a similar six-folded symmetries is created on rGO reacted with a high content of hydrazine in this study.
During the investigation on the reduction intermediates of GO, we also found an unusual result regarding the electrical conduction of rGO. When hydrazine is added to the GO dispersion, we would expect that the higher content of hydrazine would produce RGO film with higher electrical conduction in a certain range of hydrazine content (before adding an excess of hydrazine to the GO dispersion). As shown in Fig. 5a and b, however, all the rGO, regardless of hydrazine content, had similar conductivities when they were spin-coated immediately after the preparation of rGO' samples. This result suggests that a drying temperature of 120 °C can drive every hydrazine in the solution to react with oxygenated sites immediately and form a small non-oxygenated region on a rGO sheet, but in large numbers. If the oxygenated area is sufficiently close and/or small to conjugate with the non-oxygenated regions of SPCCs, they can easily be reduced by a drying temperature of 120 °C and stabilized as part of the honeycomb structure of graphene. The sudden drop of the C–O/C–C ratio of rGO6 in Fig. 4d is seemingly related to this interconnection between SPCCs. A similar phenomenon is observed in electrical conductance of e-GO film. Generally, GO has been known as a non-conductor due to fact that its oxygenated carbons are hardly reduced at temperatures below 200 °C in a few minute.
In the case of e-GO, it is easily reduced by a heat treatment below 200 °C for a few minutes as shown in Fig. 5c. In addition, the TEM image of e-GO in Fig. 6 also supports the hypothesis by showing small SPCCs placed irregularly on e-GO.
Fig. 6 TEM image of exfoliated GO in the alcoholic solvent for 5 min sonication (e-GO). Inset is enlarged photo indicating SPCCs (yellow circles) and highly oxidized areas (white circles). |
Footnote |
† Electronic supplementary information (ESI) available: Materials and methods, supporting spectroscopic data. See DOI: 10.1039/c4ra01472c |