Tianyu Zhaoabc,
Hong Zhang*abc,
Pan Liabc and
Jinsheng Liang*abc
aKey Laboratory of Special Functional Materials for Ecological Environment and Information (Hebei University of Technology), Ministry of Education, Tianjin 300130, China. E-mail: zhanghong@hebut.edu.cn; liangjinsheng@hebut.edu.cn
bInstitute of Power Source and Ecomaterials Science, Hebei University of Technology, Tianjin 300130, China
cKey Laboratory for New Type of Functional Materials in Hebei Province, Hebei University of Technology, Tianjin 300130, China
First published on 4th January 2019
Tourmaline nanoparticles (TM NPs) were well dispersed in poly(L-lactide-co-caprolactone) (PLCL) fibers via electrospinning without a dispersant. Through the modification of TM NPs, the hydrophilicity and anticoagulant property of the composite electrospun fibrous membranes were improved. Compared with the PLCL membranes, the curve of dynamic clotting time in contact with the composite TM NPs/PLCL membranes descended more slowly. Particularly, the coagulation time of 8 wt% TM NPs/PLCL membrane was longer than 70 min, which was 174% higher than that of the PLCL membrane. At the same time, the cell compatibility and mechanical properties of TM NPs/PLCL membranes were analyzed. The cytotoxicity test showed that the grade of 8 wt% TM NPs/PLCL membrane was 0. The stretching experiments showed that the tensile strength of 8 wt% TM NPs/PLCL membrane (6.71 ± 0.30 MPa) was 267.33% higher than that of the PLCL membrane, and its elongation at break (141.83 ± 5.82%) was higher than the requirement of the coronary artery. These results indicated that the PLCL electrospun fibrous membranes modified with TM NPs have potential to be used in tissue engineering as small-caliber vascular grafts.
Tourmaline (TM) is a multi-element silicate mineral; the general chemical formula can be written as XY3Z6Si6O18(BO3)3W4 (where X can be Na, Ca, K or vacancies; Y can be Mg2+, Fe2+, Mn2+, Al3+, Fe3+, Mn3+, Li+; Z can be Al3+, Fe3+, Cr3+, Mg2+; W can be OH−, F−, O2−). TM crystals are symmetric about the c-axis, and there is neither a symmetric surface nor a symmetric center in the direction of the vertical c-axis. Thus the high asymmetry causes many molecular vibrations inside the crystal, which endows tourmaline with many properties such as spontaneously polarizable, pyroelectric, piezoelectric and radiating in the far infrared region.20,21 In our previous experiments, we found that tourmaline can regulate calcium salt deposition and slow down the crystal formation.22 After immersion in the simulated body fluid with shaking, the increasing ratio of calcium deposition on composite membranes containing TM was lower than that of a pure polymer membrane, thereby it may be an effective mean for retarding coagulation.
The electrospun technology is a method of preparing fibrous membranes through the electrostatic breakdown of polymer solution in a high voltage electrostatic field.23 The products of electrospun membranes have attracted wide attention because of their structure being similar to the extracellular matrices and excellent mechanical properties for vascular grafts.24 L. D. Tijing has obtained a dispersed homogeneous tourmaline/polyurethane antibacterial membrane with good mechanical properties by the electrospinning method.25 However, a high content of Triton X-100 was added as a dispersant, which makes this membrane unsuitable for tissue engineering. Therefore, the preparation method needs improvement for small-caliber vascular grafts.
In this study, TM particles with an average diameter of 100 nm were obtained and dispersed into the biocompatible poly(L-lactide-co-caprolactone) (PLCL) matrix without a dispersant. The uniformly dispersed tourmaline nanoparticle/PLCL composite membranes were prepared by electrospinning. Subsequently, the anticoagulant properties of the composites were mainly studied, including their morphology characterization and hydrophilicity. In addition, the cytotoxicity and mechanical properties of the composites were also tested in order to prepare the scaffolds for vascular tissue engineering.
Finally, 10 μL per well of MTT (5 mg mL−1) was added into the cell culture plate, and incubated at 37 °C for 4 h, after which the supernatant was removed and 180 μL DMSO was added. The optical density of each sample at a wavelength of 570 nm was measured by an enzyme-labeled instrument (Multiskan FC, Thermo Scientific, USA).
The viscosity, electrical conductivity and surface tension of the TM NPs/PLCL electrospinning solution are shown in Table 1. As the tourmaline content increased, the viscosity of the electrospinning solution increased from 79.80 cP to 230.40 cP and the conductivity of the electrospinning solution increased from 4.67 μS cm−1 to 12.36 μS cm−1, while the surface tension of the solution did not change significantly. The increase in solution viscosity was attributed to the surface effect of TM NPs capable of adsorbing the polymer chain in the electrospinning solution,26,27 which transmits its own excessive energy, hindering the movement of the segments to enhance the entanglement between the polymer segments. In addition, each of the tourmaline nanoparticles in the solution were equivalent to an electric dipole due to its spontaneous polarization effect,28 which led to the increase in the conductivity of the whole solution.
Samples | Viscosity (cP) | Conductivity (μS cm−1) | Surface tension (mN m−1) |
---|---|---|---|
PLCL | 79.80 | 4.67 | 29.63 |
2% TM NPs/PLCL | 103.50 | 6.88 | 29.35 |
4% TM NPs/PLCL | 142.20 | 9.21 | 29.20 |
6% TM NPs/PLCL | 180.80 | 10.82 | 29.09 |
8% TM NPs/PLCL | 230.40 | 12.36 | 29.22 |
Fig. 2 displays the SEM patterns for the PLCL and composite membranes. The electrospun membrane was composed of a large number of randomly oriented fibers, which were interconnected to create a three-dimensional porous network structure. The morphology of the electrospun fibers was not affected by the introduction of tourmaline nanoparticles. All the electrospun membranes consist of uniform ultrafine fibers. Using Image J, the average diameter of the electrospun fibers fall in the range from 751.7 ± 324.3 nm (PLCL) to 532.4 ± 372.8 nm (8 wt% TM NPs/PLCL). This was attributed to the charging jet that does not break up into small droplets due to chain entanglements of higher viscosity, thereby allowing the coulombic stress to elongate the charged jet to form into thinner fibers. Furthermore, because of the highly conductive solution, the fiber jet would get more stretched by the electric field force, causing the diameter of the fiber to be reduced.
Fig. 2 SEM images of different electrospun membranes ((a) PLCL, (b) 2 wt% TM NPs/PLCL, (c) 4 wt% TM NPs/PLCL, (d) 6 wt% TM NPs/PLCL, (e) 8 wt% TM NPs/PLCL). |
Fig. 3 shows the TEM images of the PLCL and TM NPs/PLCL nanofibers containing 2 wt%, 4 wt%, 6 wt% and 8 wt% TM NPs. It is found that the PLCL sample displayed smooth and cylindrical fibers. Additionally, the TM NPs can be dispersed in the PLCL fiber without a dispersant because the high surface charge density of TM NPs causes electrostatic repulsion among them, which contributes to their dispersion in PLCL solution.29 Therefore, the uniform dispersion was directly related to the increase in TM NP contents in the composite solution and spun fibers. Additionally, the crystal structure of TM NPs in 8 wt% TM NPs/PLCL was detected (ESI Fig. S2†), which was consistent with XRD characterization (Fig. 1b).
Fig. 3 TEM images of different electrospun membranes ((a) PLCL, (b) 2 wt% TM NPs/PLCL, (c) 4 wt% TM NPs/PLCL, (d) 6 wt% TM NPs/PLCL, (e) 8 wt% TM NPs/PLCL). |
The wettability of the samples could be evaluated by the contact angle (Fig. 4). It was clear that the contact angle of the membranes decreased with the loading of TM NPs into the fibers. When the tourmaline nanoparticle content was 8 wt%, the contact angle was 70.5 ± 3.7°, which was 47° lower than that of the PLCL membrane (117.2 ± 3.1°). This decrease was directly attributed to the better hydrophilicity of TM. Moreover, hydrogen bonds in water clusters were destroyed by the electric field of TM NPs.20,21 Therefore, the surface tension of water was reduced, and the hydrophilicity of composite membrane was improved.
Fig. 4 Contact angle of different electrospun membranes ((a) PLCL, (b) 2 wt% TM NPs/PLCL, (c) 4 wt% TM NPs/PLCL, (d) 6 wt% TM NPs/PLCL, (e) 8 wt% TM NPs/PLCL). |
Blood clotting measurements were often used to assess the influence of materials on the process of the intrinsic coagulation pathway. When the membranes come in contact with blood, intrinsic coagulation occurrs and the degree of coagulation increases following the contact time (Fig. 5). The optical density curves reflected the trend of the number of free hemoglobin in the blood supernatant. Generally, the optical density value equal to 0.1 was taken as the initial clotting time. The values of the control and the samples except 8 wt% TM NPs/PLCL exhibited a similar rapidly decreasing profile. The initial clotting time of the control, PLCL, 2 wt% TM NPs/PLCL, 4 wt% TM NPs/PLCL and 6 wt% TM NPs/PLCL samples were 41.1 min, 41.9 min, 43.1 min, 44 min and 45 min, respectively. The clotting time of the 8 wt% TM NPs/PLCL sample was more than 70 min, which was much longer than the other samples. These data indicated that the composite membranes with TM NP additives reduced the activation of intrinsic clotting factors in the blood and prolonged the dynamic clotting time.
From the existing literatures, it was believed that TM NPs could improve the anticoagulant properties of the materials by the following three aspects. First, the diameter of electrospun fibers was reduced by adding TM NPs, thus a smoother membrane surface was constructed, which reduced the blood flow resistance. Second, the hydrophilicity of the composite membrane was improved, which could hinder protein adhesion. Finally, the negative potential of TM NPs led to the electrostatic repulsion of platelets, which reduced the possibility of platelets sticking to the membrane surface.
Cytotoxicity tests were also carried out to determine whether the composite membrane had the potential to act as a small-caliber vascular graft. The MTT assay was based on the reaction between MTT and mitochondrial succinate dehydrogenases in living cells to form a purple formazan, which was soluble in DMSO but insoluble in water. The OD value of the formazan–DMSO solution was considered to be proportional to the number of living cells. Therefore, it was often used to evaluate cytotoxicity. After 3 days of treatment, the optical density of L929 cells on the negative control, positive control, PLCL and 8 wt% TM NPs/PLCL membranes are shown in Fig. 6. In the positive control group, the RGR of L929 is 39.81%, the cytotoxicity grade is 3, which is moderately cytotoxic. For 100% extracts of samples, the RGR of 8 wt% TM NPs/PLCL (116.53%) was 1.18 times that of the RGR of PLCL (98.53%), showing the positive effect on cell proliferation following tourmaline addition. Besides, the cytotoxicity grade of PLCL and 8 wt% TM NPs/PLCL membrane were 1 and 0, respectively. For other percent extracts, the RGR of L929 cells on PLCL and 8 wt% TM NPs/PLCL membranes increased with decreasing extract concentration, and the cytotoxicity grade of both PLCL and 8 wt% TM NPs/PLCL membranes was 0. Compared with the positive control group and negative control group, the two samples showed no toxicity and had potential application in biological systems.
Fig. 6 Cytotoxicity of different samples (PLCL, 8 wt% TM NPs/PLCL, positive control and negative control). |
Fig. 7 displays the SEM patterns for L929 cells on the control, PLCL and 8 wt% TM NPs/PLCL membranes. In the control group, L929 cells were fusiform, solitary and had distinct pseudopods. In the PLCL group, the L929 cells were spindle-shaped and polygonal. In the 8 wt% TM/PLCL group, L929 cells were also fusiform or polygonal. However, unlike the control group, the cells grew continuously and the number of cells was more than the control group. In addition, the pseudopods were mainly covered by electrospun fibers and had a tendency to grow into the membrane.
Fig. 7 Cell morphologies of L929 cultured on different membranes (control, PLCL and 8 wt% TM NPs/PLCL). |
Fig. 8 shows the tensile strength and elongation at the break of different TM NPs/PLCL composite membranes. The tensile strength increased from 2.51 ± 0.25 MPa to 6.71 ± 0.30 MPa with the increase in TM NPs content, which meant that the tensile strength increased by 267.33% on the PLCL membrane. This enhancement was attributed to the following points: first, the added TM NPs provided a nucleation particle for the polymer solution during electrospinning, which helped to improve the crystallinity of the composite (confirmed through DSC, Fig. S3 in ESI†). Secondly, the unique surface and small size effect of the nano-size could impact the physical and chemical interaction between uniformly distributed nanoparticles.29 When the substrate was subjected to an external force, the entanglement point inhibited the sliding of the molecular chain.30 Finally, nanoparticles could also act as stress concentration points to prevent further cracking.31
Fig. 8 Mechanical properties of different electrospun membranes ((a) PLCL, (b) 2 wt% TM NPs/PLCL, (c) 4 wt% TM NPs/PLCL, (d) 6 wt% TM NPs/PLCL, (e) 8 wt% TM NPs/PLCL). |
The elongation at the break of the composite membrane showed a trend of fall-rise, when the TM NPs content was 2 wt%, the elongation at break of the composite film was the lowest (72.65 ± 6.85%), which could not meet the requirement for the coronary artery (99%).32 The composite membrane containing 6 wt% or 8 wt% of TM NPs had good toughness with an elongation at break of more than 100%. The introduction of TM NPs aggravated the brittleness of fibers, causing a decrease in the elongation at break. However, with the increase in TM NPs content, the incorporation could not only transmit the external stress, but also cause the matrix yielding to consume a large amount of energy, thus achieving the toughening of the composite membranes.
Footnote |
† Electronic supplementary information (ESI) available. See DOI: 10.1039/c8ra07700b |
This journal is © The Royal Society of Chemistry 2019 |