Chang Ki Kim‡
,
Jung-Min Ji‡,
M. Aftabuzzaman and
Hwan Kyu Kim*
Global GET-Future Laboratory, Department of Advanced Materials Chemistry, Korea University, 2511 Sejong-ro, Sejong 339-700, Korea. E-mail: hkk777@korea.ac.kr
First published on 24th February 2021
Tellurium-doped mesoporous carbon composite materials (Te/NMC) have been prepared by a facile intercalation method in the presence of nitrogen-doped mesoporous carbon (NMC) with tellurium powder, for the first time. The effects of the co-doped N and Te in the mesoporous carbon matrix on the physical/chemical properties and capacitance performances were investigated via the use of various characterization methods and electrochemical studies. The as-prepared NMC and Te/NMC materials were found to mainly be composed of mesopores and maintained the 3D hierarchical graphite-like structure with lots of defect sites. By intercalation of Te atoms into the NMC materials, 2.12 at% (atom%) of Te was doped into NMC and the specific surface area of Te/NMC (261.07 m2 g−1) decreased by about 1.5 times compared to that of NMC (437.96 m2 g−1). In electrochemical measurements as a supercapacitor (SC) electrode, the Te/NMC based electrode, even with its lower porosity parameters, exhibited a higher capacitive performance compared to the NMC-based electrode. These results for Te/NMC arise due to the pseudo-capacitive effect of doped Te and the increase in the capacitive area available from the formation of interconnections in the mesoporous carbons through Te–O bonds. As a result, the synergetic effect of the Te and N atoms enables Te/NMC to exhibit the highest specific capacitance of 197 F g−1 at a current density of 0.5 A g−1. Moreover, remarkable long-term cycling stability with the retention of more than 95% of the initial capacitance is observed for Te/NMC at a current density of 5 A g−1 and also for 1000 charge–discharge cycles.
As one of the EES technologies, electrochemical capacitors, i.e. supercapacitors (SCs), have attracted considerable attention because of their remarkable power performance, long-term cycling stability (>106 cycles), low maintenance costs, ease of integration into electronics and good safety.11 Their advantages arise from their charge storage mechanisms, which can be generally classified into two categories: (i) electric double layer capacitance (EDLC) and (ii) pseudocapacitance (PC).12,13 EDLCs electrostatically store charge by forming a Helmholtz double layer at the interface between the electrode and electrolyte, i.e., a non-faradaic process occurs,14 while PCs faradaically store charge via reversible electrochemical reactions on the surface of redox-active materials, i.e., a faradaic process occurs. In practice, the EDLC and PC mechanisms coexist in SCs, contributing in different proportions.15 According to each mechanism, the specific capacitance (CS) of an EDLC depends on the accessible surface area and properties of the electrode materials, and the CS of a PC is strongly related to the valence state change of the redox-active materials.16 Many electro-active materials, such as conducting polymers,17,18 metal oxides,19–21 noble metals22 and carbons,12 and preparation methods23–25 have been developed and tested for more efficient supercapacitors.26 Among them, carbon-based materials, such as commercial active carbons,14,27 carbon nanomaterials,28,29 graphene,30–32 and templated carbons,33,34 are the most extensively examined and studied as electro-active materials for the EDLC mechanism. This is ascribed to their high specific surface area, electrochemical stability, and open porosity to electrolyte ions. However, carbon-based materials have relatively low rate capability and cycling stability, because the capacitive charge storage mainly occurs at the micropores (<2 nm).35 Therefore, the porosity control of carbon-based materials is one of the main themes to guarantee better performance in terms of power delivery and energy storage.35,36 However, to overcome the low capacitance performance of carbon-based materials, metal oxides and heteroatoms, such as boron,37 nitrogen,38,39 oxygen,40 phosphorous41,42 and sulfur,43 are incorporated into the surface of carbon-based materials.44–48 The incorporation of metal oxides and heteroatoms has led to an improvement in the capacitive performance of such materials, as shown in Table S1.†36 In our previous study, we developed a preparation method of soft-templated nitrogen-enriched mesoporous carbon (NMC) with controlled pore size and volume as a counter electrode in dye-sensitized solar cells (DSSCs).49,50 The preparation method was beneficial to tailoring the pore structures of carbon materials by controlling the temperature of pyrolysis and the composition of the PAN-b-PBA copolymer, which consists of polyacrylonitrile (PAN) as a carbon source and poly(n-butyl acrylate) (PBA) as a sacrificial block.51 Based on the preparation method, very recently, we reported Ru-doped carbon materials as supercapacitor materials, which showed outstanding capacitive performance and cycling stability.46 This can be attributed to the PC and well-organized distribution of Ru throughout the NMC.
In this study, we prepared a tellurium-doped mesoporous carbon composite material (Te/NMC), for the first time, via a facile intercalation method in the presence of nitrogen-doped mesoporous carbon (NMC) and tellurium powder to investigate the capacitive behaviour of tellurium and nitrogen dual-doped carbon materials. The effect of Te and N atoms on the structural properties was carefully scrutinized using various characterization methods, such as elemental analysis (XPS and EDS), Raman spectroscopy, nitrogen sorption isotherm measurements (BET), and field emission scanning electron microscopy (FE-SEM). We also demonstrate that the incorporation of Te in carbon-based nanomaterials is a good strategy to improve the capacitive performance of carbon materials and that the incorporation of two types of atoms improves the overall capacitive performance of the materials due to their synergetic effect.
To investigate the specific surface area and porosity of NMC and Te/NMC, nitrogen sorption isotherm measurements were conducted. The nitrogen adsorption–desorption isotherm plots of NMC and Te/NMC are displayed in Fig. 2a, and the parameters are tabulated in Table 1. As shown in Fig. 2a, the isotherm plots of both NMC and Te/NMC exhibit type IV isotherms with a H1 hysteresis loop. This indicates a well-developed mesopore and inter-connected pore carbon structure. The specific surface areas of the NMC and Te/NMC materials were calculated to be 437.96 and 261.07 m2 g−1 with total pore volumes of 0.80 and 0.63 cm3 g−1, respectively. The pore sizes were estimated to be 11.28 and 11.37 nm for NMC and Te/NMC, respectively. Interestingly, despite the surface areas and total pore volumes of Te/NMC being lower than those of NMC, the pore sizes of NMC and Te/NMC are almost the same. This indicates that the Te metalloid was intercalated into the NMC well and does not block the inner-pores of the NMC.
Fig. 2 (a) Nitrogen adsorption–desorption isotherms, (b) XRD diffraction patterns and Raman spectra of (c) NMC and (d) Te/NMC. |
Sample | SBET (m2 g−1) | Vtotal (cm3 g−1) | Vmicro (cm3 g−1) | Vmeso (cm3 g−1) | Pore size (nm) |
---|---|---|---|---|---|
a SBET: BET surface area, Vtotal: total pore volume, Vmicro: micropore volume, Vmeso: mesopore volume. | |||||
NMC | 437.96 | 0.80 | 0.10 | 0.68 | 11.28 |
Te/NMC | 261.07 | 0.63 | 0.03 | 0.60 | 11.37 |
To assess the structural characteristics of the two carbon materials, X-ray diffraction (XRD) measurements and Raman spectroscopy were carried out (Fig. 2b–d). Fig. 2b displays the XRD patterns of the two materials. These patterns show broad diffraction peaks at 25° and 43°, which correspond to the (002) and (100) planes of graphitic carbon, indicating their amorphous and disordered structures.51,52 However, there are no crystal peaks for Te, indicating the atomically dispersed Te in the carbon network. Fig. 2c and d display the Raman spectra of NMC and Te/NMC, respectively. The spectra for both materials exhibit three distinct peaks at around 1350, 1590, and 1510 cm−1, which are assigned to the defect-induced band (D), in-plane vibrational graphitic-induced band (G), and amorphous structure band (A) of carbon, respectively.53 In general, it is well known that the D band becomes active as a result of defects occurring in the carbon lattice from the Raman inactive mode (A1g), and the G band (E2g) presents as a result of the stretching vibration mode of the C–C bond. Therefore, the intensity ratio of the D and G bands (ID/IG) in carbon materials is often used to estimate the level of disorder in graphitic structures.54,55 The ID/IG ratios for NMC and Te/NMC were determined to be 2.81 and 2.90, respectively, which implies that both of the as-prepared materials contain semi-graphitic carbon with many defect sites.54
To observe the surface morphology and porous structure of NMC and Te/NMC materials, field emission scanning electron microscopy (FE-SEM) measurements were conducted. The SEM images at high magnification exhibit the 3D bi-continuous structure of NMC and Te/NMC with mesopores (see Fig. 3a and b). In addition, the doping of elements into the samples was detected by SEM-EDS (Fig. 3c–e for NMC and Fig. 3f–i for Te/NMC). The EDS elemental mapping results of NMC display that the N (Fig. 3d) and O (Fig. 3e) atoms are uniformly distributed in the carbon matrix, while those of Te/NMC also display the homogeneous distribution of N (Fig. 3g), O (Fig. 3h) and Te (Fig. 3i) atoms in the carbon matrix. This demonstrates that Te atoms were successfully introduced into the carbon framework of NMC.50,56
X-ray photoelectron spectroscopy (XPS) was carried out to determine the elemental composition and the bonding characteristics of the C, N, O, and Te atoms in the two materials. In Fig. 4, the X-ray survey spectra indicate the presence of C, N and O atoms in NMC, while Te/NMC exhibits the presence of C, N, O and Te atoms. Their elemental composition results are summarized in Table 2. The Te content of Te/NMC was estimated to be approximately 2.12 atomic percentage (at%). To further understand the bonding characteristics of NMC and Te/NMC, high-resolution XPS was performed. Fig. 5 displays the bonding characteristics of the C, N, O and Te atoms. After the deconvolution of C1s for NMC, four major peaks were displayed at 290.8, 286.9, 285.8 and 284.6 eV that correspond to OC–OH, –C–O, –CN/–C–N and –C–C/-CC bonding, respectively (Fig. 5a).57 Meanwhile, after the deconvolution of C1s for Te/NMC, there were five peaks: four peaks at 290.8, 286.9, 285.8 and 284.6 eV corresponding to OC–OH, –C–O, –CN/–C–N and –C–C/-CC bonding, respectively, and another peak at around 283 eV corresponding to C–Te bonding (Fig. 5d). Deconvolution of the N1s spectra of NMC and Te/NMC led to four different peaks being displayed, which are consistent with pyridinic-N (397.9 eV), pyrrolic-N (400.2 eV), graphitic-N (400.6 eV), and pyridinic-N oxide (402.3 eV), as shown in Fig. 5b and e.58 The charge-transfer ability and overall wettability were improved by the N-heteroatoms (mainly pyridinic-N and graphitic-N) incorporated into the carbon matrix, enhancing the PC. The high-resolution O1s spectrum of NMC deconvoluted into two peaks at around 533.9 and 531.6 eV, which can be assigned to C–O-R and –CO bonds, respectively (Fig. 5c), while those of Te/NMC deconvoluted into three peaks at around 534.8, 532.6 and 530.8 eV, which are consistent with to C–O-R, CO and O–Te bonds, respectively (Fig. 5f).51 Deconvolution of the Te3d spectrum of Te/NMC displays four peaks (Fig. 5g). Two of the peaks at around 586.2 and 575.9 eV, can be characterized as two splitting orbitals, 3d5/2 and 3d3/2, of the Te–O bond.56 The other two peaks, at around 584.2 and 573.8 eV, are characterized as the splitting orbitals, 3d5/2 and 3d3/2, of the Te–C bond. Interestingly, the intensities of the Te–O bond peaks are much greater than those of the Te–C bond peaks. This can be explained by the Te atoms being intercalated with a Te–O bond rather than by a Te–C bond in the carbon matrix.49
Sample | Element (at%) | |||
---|---|---|---|---|
C | O | N | Te | |
NMC | 86.31 | 7.23 | 5.41 | — |
Te/NMC | 85.04 | 5.86 | 6.99 | 2.12 |
Fig. 5 High-resolution deconvoluted XPS spectra of NMC ((a) carbon, (b) nitrogen, (c) oxygen) and Te/NMC ((d) carbon, (e) nitrogen, (f) oxygen, (g) tellurium). |
The electrochemical performances of the NMC and Te/NMC electrodes were investigated in 6 M KOH electrolyte using a three-electrode system containing an Ag/AgCl reference electrode (Fig. 6). The cyclic voltammetry (CV) plots were recorded at different scan rates from 10 to 100 mV s−1 over a potential window of −1.0 to 0 V. The CV plots of NMC display a typical quasi-rectangular-like shape with a bulge. This is assigned to the N of the porous carbon (Fig. 6a).54,55 This slight bulge at around −0.85 V indicates the presence of PS with EDLC, which is associated with the electrochemical reaction of the doped nitrogen functional group. Moreover, a quasi-rectangular-like shape after increasing the scan rate from 10 to 100 mV s−1 was observed in the CV plots, which indicates a fast charge transfer rate and facile ion passage within the NMC electrodes. In the case of Te/NMC (see Fig. 6b), the CV plots of Te/NMC are similar to those of the NMC, but they exhibit a slightly broadened PC peak with increasing current density compared to the NMC electrodes. This represents the PC intensification as a result of the incorporation of Te atoms and the increase in the capacitive area available as a result of the formation of interconnections in the mesoporous carbons through Te–O bonds.44
The gravimetric capacitances (i.e., CS) of the electrodes were measured by carrying out galvanostatic charge–discharge (GCD) measurements at different current densities (0.5, 1, 2, 3, 5, and 10 A g−1). The CS values were estimated using the equation CS = I × Δt/m × ΔV, where I is the current, Δt the discharging time, m the mass of the active material, and ΔV is the potential window. In general, the symmetric charge–discharge plots of the electrodes indicate the reversible behavior of surface redox reactions. Fig. 6d and e display the symmetric GCD plots of NMC and Te/NMC at current densities of 2–10 A g−1, but at the current densities of 0.5 and 1 A g−1 bent GCD plots are observed. These phenomena can be explained due to the PC that arises due to the incorporation of hetero-atoms and metal oxides.35 In addition, the intercalation of Te atoms can result in a plateau in the charge–discharge plots due to the PC of N, which corresponds to the CV results. However, the charge–discharge time in the Te/NMC materials increased, indicating a higher CS value via the PC of Te, and the limitation of accessibility of ion migration inside the pore structures by the interconnections between the mesoporous carbons through Te–O bonds (Fig. 6e). The projected CS values for NMC and Te/NMC are 118 and 197 F g−1, respectively. A comparison of the GCD plots of the two different electrodes at 0.5 A g−1 is presented in Fig. 6f.
Rate capability is one of the most important properties for SCs, since their main application field requires a fast charge–discharge rate and quick energy transfer.16 Therefore, the rate capability of electrodes at different current densities (0.5, 1, 2, 3, 5, and 10 A g−1) is shown in Fig. 7a. By increasing the current density from 0.5 to 10 A g−1, the CS values of both prepared NMC and Te/NMC electrodes decreased. This behaviour can also be attributed to the insufficient time for electrolyte transport into the entire pore structure and the PC of the doped elements.54 In particular, the reduction of CS for the Te/NMC electrode between a current density of 0.5 to 10 A g−1 is greater than that of the NMC electrode, which indicates the PC intensification via the incorporation of Te atoms and the increase in the interconnection in the mesoporous carbons through Te–O bonds. However, the retention of CS for Te/NMC was significantly higher than that of NMC at all current densities (see Fig. 7a). To investigate the conductive and diffusion behavior of NMC and Te/NMC based electrodes, EIS was performed. The Nyquist plots of the NMC and Te/NMC electrodes are shown in Fig. 7b and were fitted with an appropriate equivalent circuit.46 In the Nyquist plots, the intercepts on the real axis at higher frequencies indicate the equivalent series resistance (RS), which is associated with the ohmic resistance of the electrode and electrolyte distribution resistance.46 The arcs at the high- and mid-frequency imply the charge transfer resistance at the electrode/electrolyte interface (RCT). The vertical graphs at the low-frequency indicate the good capacitive properties. As shown in Fig. 7b, the Nyquist plots display vertical graphs for the NMC and Te/NMC electrodes, which means the good capacitive properties of the electrodes. The inset of Fig. 7b displays that the RS values of the two electrodes are 0.35 and 0.27 Ω for the NMC and Te/NMC electrodes, respectively, as determined by estimating the vertical lines and real axis. The smaller the RS value of the Te/NMC electrode can be attributed to the enhancement of charge transport in the carbon matrix by the formation of interconnected mesoporous carbons through Te–O bonds. The smaller arc of the Te/NMC electrode at high frequency than that of the NMC electrode indicates the efficient PC mechanism by the incorporation of Te atoms, because the incorporation of Te atoms can reduce the activation energy for inner-path charge transfer between the electrolyte and Te-doped carbon materials, according to the previous results.44
Furthermore, the cycling stability of the NMC and Te/NMC electrodes was tested in a standard three-electrode configuration via continuous charge–discharge measurements at a current density of 5 A g−1 over a potential window of −1 to 0 V. As shown in Fig. 7c, it can be observed that NMC and Te/NMC electrodes exhibit excellent retention of specific capacity for 1000 cycles. However, the phenomenon of increasing capacitance after 100 cycles may be due to increase of wettability of the electrode materials and feasible accessibility of the pores by electrolyte ions.59 In particular, the Te/NMC electrode shows around 115% relative capacitance after 1000 cycles. This can be attributed to the increased capacitive area in the carbon matrix as a result of the intercalation of Te atoms.
Footnotes |
† Electronic supplementary information (ESI) available: Information and details of GPC data, electrochemical measurement and the related equations are available. See DOI: 10.1039/d0ra10374h |
‡ These authors contributed equally to this work. |
This journal is © The Royal Society of Chemistry 2021 |