Open Access Article
This Open Access Article is licensed under a
Creative Commons Attribution 3.0 Unported Licence

Copper(I) iodide organic–inorganic hybrid luminescent inks for anti-counterfeiting application

Hua Tong , Zhennan Zhou , Yi Lv , Haibo Li , Wei Liu * and Gangfeng Ouyang *
School of Chemical Engineering and Technology, Sun Yat-sen University, Zhuhai, 519082, Guangdong, P. R. China. E-mail: liuwei96@mail.sysu.edu.cn; cesoygf@mail.sysu.edu.cn

Received 7th October 2022 , Accepted 27th November 2022

First published on 1st December 2022


Abstract

An efficient and universal method has been developed for the preparation of copper(I) iodide incorporated organic–inorganic hybrid coating materials. These materials exhibit potential as solvent-free anti-counterfeiting inks, with the advantages of facile prepration method, low-cost, uniform and bright light emissions, long service life, high stability, water resistance, and strong wearability.


Manufacturers today are increasingly seeking high-quality inks and coating materials to help produce products that are smaller, lighter, and more technologically advanced. Nowadays, anti-counterfeiting technology has strengthened information security protection by taking its unique advantages in photochemistry, electromagnetism, printing and spectral technology, etc. Modern anti-counterfeiting techniques include materials, digital information, printing technology, biological characteristics and other types of anti-counterfeiting methods.1–3 Therefore, environmentally friendly luminescent inks with low toxicity, good optical performance, strong stability and mechanical performance are in great demand.

Organic–inorganic hybrid materials have rich structural types and can be used in a variety of areas, among which functional inks and coating materials are one of their important applications.4–8 Organic–inorganic hybrid coatings are typically silicon oxide based resins, which are mainly prepared by sol–gel method.9,10 In these hybrid materials, the inorganic component is silicon oxides, the organic components are polymers.11 Such composite structures maintain the good hardness, scratch resistance, weather resistance properties from the inorganic species, and the flexibility, compactness and processability properties from the organic components.9,12 Hybrid coating materials have many advantages, such as tunable structures and performance, facile synthesis and environmental friendliness, showing great potential for large-scale commercialization.9,13

With the improvement of living standards, coating materials are required to have more functions and specialties.14–17 Luminescent coatings are one of the most important functional coatings since they can be used not only as decorative coatings, smart coatings, as well as anti-counterfeiting inks.18–20 Silicon oxide based resins are generally non-luminescent, and lighting-emitting coating of this type are typically prepared by adding luminous substances such as phosphors and organic dye molecules into the resin materials.20–23 Such mixing process is physical blending since there is no chemical bond between the added luminescent compounds and the coating materials, which may result in many problems, such as uneven luminescence distribution, and easy sedimentation of luminous particles, etc.24,25

Copper(I) iodide hybrid molecular clusters have excellent luminescence properties.26–31 Generally, the reaction of copper(I) iodide with organic ligands leads to the formation of three types of structures, such as Cu2I2(L)x dimer based compounds, Cu4I4(L)x cubane based compounds, CuI(L)x staircase infinite chain based compounds.32 Among them, Cu4I4(L)4 cubane clusters are the most common in literature and demonstrate remarkable photoluminescence behavior.33 Typically, 0D-Cu4I4(L)4 molecular clusters emits strong yellow light under UV irradiation, with impressive internal quantum yields (IQYs) as high as 100%. Their emissions have been found to result from a cluster-centered (CC) mechanism, and is due to the strong Cu–Cu interaction within the Cu4I4 core.34,35 A bottom-up precursor approach has been developed with the goal of keeping the inorganic core intact in the ligand-exchanged products.36 Typically, a Cu4I4 based molecular cluster was selected as the precursor, and was well-dispersed in the solvent for ligand substitution. Through the: “bottom-up” method, small molecules with specific copper(I) iodide clusters can be used as precursors to controllably synthesize multi-dimensional hybrid structures with the identical inorganic cluster structure, and such multi-dimensional hybrid structures can typically maintain the optical properties of the precursors.37 Under such method, the copper(I) iodide core can be effectively incorporated into multidimensional structures, forming hybrid structures that are both highly luminescent and stable.

Based on the previous studies, an efficient “bottom-up” synthetic strategy has been developed to synthesize cross-linked organic–inorganic hybrid coatings with unique luminescent properties while the emissive Cu4I4 core has been incorporated into the resin materials through Cu–P coordination bonds (Fig. 1).36,38 A Cu4I4 based precursor, Cu4I4-dpes, has been synthesized by using CuI and a phosphine ligand 2-(diphenylphosphino)ethyltriethoxysilane (dpes). Then, four different kinds of such coatings (represented by c-TEOS, c-VTES, c-MTES, c-PTES respectively) have been prepared by ligand exchange of the precursor molecules Cu4I4-dpes with the coupling reagents of tetraethyl orthosilicate (TEOS), triethoxyvinylsilane (VTES), methyltriethoxysilane (MTES) and phenyltriethoxysilane (PTES) (Fig, S1, ESI and Fig. 1), proving the universality of this synthetic method. In such multi-core based organic–inorganic hybrid functional coating materials, the inorganic components include both silicon oxide clusters and copper(I) iodide clusters with specific structures. The former species maintain the superior protection performance of the original hybrid resin and the high stability of the silicon-based coatings, while the latter gives the coatings superior optical properties. These hybrid coatings all emit strong yellow light under UV-light irradiation (Fig. 1). These novel hybrid materials are facile to prepare free-standing luminescent films on different substrates, displaying potential as a new type of anti-counterfeiting inks.


image file: d2ma00956k-f1.tif
Fig. 1 Diagram of the synthetic process of the hybrid coatings.

SEM image of the cross section of glass-based c-PTES prepared by spin coating (3000 rpm, 30 s) demonstrates the thickness of the coating is about 3 μm (Fig. S2, ESI). The X-ray diffraction (XRD) analyses (Fig. 2a) show that the as-made crosslinked networks of all four coatings are totally amorphous structure. No peak of CuI is detected, indicating that CuI has been successfully incorporated into the resin structures. The Fourier transform-infrared (FT-IR) spectroscopy spectra were obtained by testing the powdery samples of coatings. As shown in Fig. 2b, each of the coatings has an obvious absorption peak at about 3418 cm−1, which corresponds to intramolecularly associated –OH. The absorption peaks at about 2980 cm−1 and 2930 cm−1 correspond to the antisymmetric stretching vibrations of –CH3 and –CH2–. Affected by different silane coupling agents involved in the reactions, the absorption peak of c-VTES at 3062 cm−1 should correspond to the terminal C[double bond, length as m-dash]CH, and several absorption peaks near 3072 cm−1 of c-PTES should correspond to the stretching vibrations of [double bond, length as m-dash]CH in the phenyl within PTES. In addition, four spectra show strong absorption peaks at about 1091 cm−1, 770 cm−1 and 443 cm−1, corresponding to the antisymmetric stretching vibration of Si–O–Si, symmetric stretching vibration of Si–O and bending vibration of Si–OH, respectively. The UV-vis absorption spectra (Fig. 2c) indicate that four coatings show no absorption in the visible light region, corresponding to their transparency as films under nature light. Their thermal stability has been evaluated by the thermogravimetric analyses, which is shown in Fig. 2d. The thermogravimetric analysis plots demonstrate that the decomposition temperature (TD) of c-TEOS, c-VTES, c-MTES, and c-PTES are 370 °C, 406 °C, 455 °C and 400 °C, respectively.


image file: d2ma00956k-f2.tif
Fig. 2 (a) XRD patterns, (b) FT-IR spectra, (c) UV-vis absorption spectra and (d) TG plots of c-TEOS, c-VTES, c-MTES, and c-PTES. (e) PL excitation and emission spectra of c-TEOS (1), c-VTES (2), c-MTES (3), and c-PTES (4). (f) CIE coordinates of c-TEOS, c-VTES, c-MTES, and c-PTES. (g) Plots of PL intensity ratios of c-PTES over time (I0 and I are luminescent intensity measured on day 0 and every 20 days, respectively). Insets are the images taken on day 0 and day 180 in the air under 254 nm UV irradiation.

The room temperature solid-state photoluminescence spectra of the four coating materials were recorded. As shown in Fig. 2e all four coating materials exhibit a single-band emission, with emission peaks at around 560 nm. The full width at half maximum (FWHM) of the spectra are around 120 nm. The Commission International de L’ Eclairage (CIE) chromaticity coordinates (Fig. 2f) of c-TEOS, c-VTES, c-MTES and c-PTES were calculated to be (0.49, 0.48), (0.49, 0.48), (0.46, 0.49) and (0.45, 0.49) respectively, confirming their yellow light emissions. The lifetime values of c-TEOS, c-VTES, c-MTES and c-PTES have been determined to be 2.93, 4.04, 6.16 and 5.99 μs by monoexponential fitting, respectively (Fig. S3, ESI). The decay lifetimes in microseconds suggest that they are phosphorescent emission. The results are consistent with other reported Cu4I4 based structures.27,34,35 The major photophysical properties of these coating materials have been summarized in Table 1. The IQYs of c-TEOS, c-VTES, c-MTES, and c-PTES are measured to be 17.6%, 24.5%, 53.3% and 57.1% respectively under 300 nm excitation, indicating that different coupling reagents affect the luminescent properties of the coatings and aromatic groups could increase emission intensity of the hybrid coatings. The stability of the coatings have been evaluated by placing the coated pattern in the air. The “SYSU” (logo pattern of Sun Yat-sen University) pattern was printed on the glass sheet, and the luminescent intensity of the pattern lost ∼20% after being placed in the moist air at room temperature for 180 days (Fig. 2g), indicating the good stability of the coating materials.

Table 1 Photophysical properties of the hybrid coatings
Coating c-TEOS c-VTES c-MTES c-PTES
Exmax (nm) 260 245 240 265
Emmax (nm) 595 580 580 575
τ (μs) 2.93 4.04 6.16 5.00
CIE (0.49, 0.48) (0.49, 0.48) (0.46, 0.49) (0.45, 0.49)
IQY 17.6% 24.5% 53.3% 57.1%
T D (°C) 370 406 455 400


These coatings have the advantages of uniform film formation, bright luminescence, facile preparation method, low-cost and large-scale preparation, and have the potential to be the solvent-free anti-counterfeiting inks. We chose c-PTES with the strongest luminescence among the four coatings as the solvent-free hybrid anti-counterfeiting ink material. Screen printing is an economical and widely used thin film deposition technology, which has been commonly used in various decorative printing and flexible electronic products, biosensors, intelligent security and other fields.39 Screen printing is applicable to various types of inks and is not limited by the size and shape of the substrate. Fig. 3a is an illustration of screen printing process. The c-PTES ink was poured into one end of the screen printing plate, and a certain pressure on the ink part of the screen printing plate was applied with a scraper. The scraper was moved towards the other end of the screen printing plate at a constant speed. During the movement, the ink has been pressed by the scraper from the mesh of the patterned part onto the substrate. The solvent-free c-PTES ink can take glass, poly(ethylene terephthalate) (PET), paper, cloth and other materials as substrates and a variety of patterns can be painted on these substrates.


image file: d2ma00956k-f3.tif
Fig. 3 (a) Schematic diagram of the process of screen printing by using hybrid luminescent anti-counterfeiting inks c-PTES. (b) Photos of fluorescent patterns printed on different base materials (commercial glass, PET, paper and cloth) under natural light (left) and 254 nm UV light (right).

After curing, the patterns emit uniform and bright yellow light under ultraviolet light of 254 nm in the dark, while they are colorless and transparent under natural light, displaying strong concealment properties (Fig. 3b). Even in the daytime, they emit distinct yellow light under ultraviolet light of 254 nm (Fig. S4, ESI). The logo pattern of Sun Yat-sen University is printed on the transparent and flexible PET polyester film, and it can be seen that the pattern is clear and bright under UV light (Fig. S5a, ESI). After 500 times of manual bending, there is no damage of the pattern, indicating that the printed pattern has strong mechanical performance (Fig. S5a, ESI). The pigeon pattern printed on the paper was rubbed with eraser for 100 times, and there was no damage and no obvious change in brightness of the pattern, indicating that the printed pattern had strong friction resistance (Fig. S5b, ESI). The water stability of anti-counterfeiting ink is also very important in the application of flexible textile anti-counterfeiting labels. As shown in Fig. S5c (ESI), the small bee pattern printed on the textile has not been damaged or deformed after 10 times of scrubbing with detergent and water, indicating that c-PTES ink has excellent water and chemical stability.

Conclusions

In this work, a new type of anti-counterfeiting ink is prepared, which is very different from the traditional anti-counterfeiting inks. By synthesizing the luminescent precursor with specific structure, the crosslinked photoluminescent coating materials are obtained by the sol–gel method. In the coating structures, the light-emitting substance is combined with the cross-linked resin material through covalent bonds, so that the coatings have uniform light emission and high brightness. The hybrid coatings have the advantages of strong mechanical performance, strong water stability and friction resistance, showing the potential to be a new type of solvent-free anti-counterfeiting ink.

Author contributions

H. T. was responsible for performing all experiment; Z. Z. and Y. L. were responsible for the revision of the manuscript; H. L. was responsible for the characterization of the compounds and the editing of the manuscript; W. L. was responsible for the reviewing and editing the manuscript; G. O. was responsible for the supervision of the project, and reviewing and editing the manuscript. All authors have given approval to the final version of the manuscript.

Conflicts of interest

There are no conflicts to declare.

Notes and references

  1. F. Zhang, Z. Shi, S. Li, Z. Ma, Y. Li, L. Wang, D. Wu, Y. Tian, G. Du, X. Li and C. Shan, ACS Appl. Mater. Interfaces, 2019, 11, 28013–28022 CrossRef CAS.
  2. Y. Liu, F. Han, F. Li, Y. Zhao, M. Chen, Z. Xu, X. Zheng, H. Hu, J. Yao, T. Guo, W. Lin, Y. Zheng, B. You, P. Liu, Y. Li and L. Qian, Nat. Commun., 2019, 10, 2409 CrossRef PubMed.
  3. R. Kwok, D. Kenny and G. A. Williams, Forensic Sci. Int.: Genet. Suppl. Ser., 2019, 7, 438–440 Search PubMed.
  4. T. P. Chou, C. Chandrasekaran, S. J. Limmer, S. Seraji, Y. Wu, M. J. Forbess, C. Nguyen and G. Z. Cao, J. Non-Cryst. Solids, 2001, 290, 153–162 CrossRef CAS.
  5. P. Salazar-Bravo, D. Del Ángel-López, A. M. Torres-Huerta, M. A. Domínguez-Crespo, D. Palma-Ramírez and A. B. López-Oyama, Prog. Org. Coat., 2019, 135, 51–64 CrossRef CAS.
  6. A. Rahimi and S. Amiri, J. Coat. Technol. Res., 2015, 12, 587–593 CrossRef CAS.
  7. K. K. Jena, T. K. Rout, R. Narayan and K. V. S. N. Raju, Polym. Int., 2012, 61, 1101–1106 CrossRef CAS.
  8. M. Saveleva, A. Vladescu, C. Cotrut, L. Van der Meeren, M. Surmeneva, R. Surmenev, B. Parakhonskiy and A. G. Skirtach, J. Mater. Chem. B, 2019, 7, 6778–6788 RSC.
  9. R. B. Figueira, C. J. R. Silva and E. V. Pereira, J. Coat. Technol. Res., 2015, 12, 1–35 CrossRef CAS.
  10. Ö. Kesmez, Chem. Pap., 2020, 74, 673–688 CrossRef.
  11. I. J. Zvonkina and M. D. Soucek, Curr. Opin. Chem. Eng., 2016, 11, 123–127 CrossRef.
  12. R. Goswami, Discovery, 2015, 29, 201–210 Search PubMed.
  13. W. A. Zoubi, J. H. Min and Y. G. Ko, Sci. Rep., 2017, 7, 7063 CrossRef.
  14. N. Kim, J. Coat. Technol. Res., 2017, 14, 21–34 CrossRef CAS.
  15. M. F. Montemor, Surf. Coat. Technol., 2014, 258, 17–37 CrossRef CAS.
  16. P. J. Rivero, J. A. Garcia, I. Quintana and R. Rodriguez, Coatings, 2018, 8, 76 CrossRef.
  17. S. K. Ghosh, Functional Coatings, 2006, pp. 1–28 DOI:10.1002/3527608478.ch1.
  18. L. Gong, F. Huang, Z. Zhang, Y. Zhong, J. Jin, K.-Z. Du and X. Huang, Chem. Eng. J., 2021, 424, 130544 CrossRef CAS.
  19. J.-J. Wang, C. Chen, W.-G. Chen, J.-S. Yao, J.-N. Yang, K.-H. Wang, Y.-C. Yin, M.-M. Yao, L.-Z. Feng, C. Ma, F.-J. Fan and H.-B. Yao, J. Am. Chem. Soc., 2020, 142, 3686–3690 CrossRef CAS PubMed.
  20. P. Kumar, S. Singh and B. K. Gupta, Nanoscale, 2016, 8, 14297–14340 RSC.
  21. X. Yu, H. Zhang and J. Yu, Aggregate, 2021, 2, 20–34 CrossRef.
  22. S. Zhao, M. Gao and J. Li, J. Lumin., 2021, 236, 118128 CrossRef CAS.
  23. J. Li, D. Xia, M. Gao, L. Jiang, S. Zhao and G. Li, Inorg. Chim. Acta, 2021, 526, 120541 CrossRef CAS.
  24. Y. Ma, Y. Zou, Z. Zhang, J. Fang, W. Liu, Y. Ni, L. Fang, C. Lu and Z. Xu, Cellulose, 2020, 27, 561–573 CrossRef CAS.
  25. O. Younis, E. E. El-Katori, R. Hassanien, A. S. Abousalem and O. Tsutsumi, Dyes Pigm., 2020, 175, 108146 CrossRef CAS.
  26. V. W.-W. Yam, V. K.-M. Au and S. Y.-L. Leung, Chem. Rev., 2015, 115, 7589–7728 CrossRef CAS.
  27. W. Liu, Y. Fang and J. Li, Adv. Funct. Mater., 2018, 28, 1705593 CrossRef.
  28. R. Peng, M. Li and D. Li, Coord. Chem. Rev., 2010, 254, 1–18 CrossRef CAS.
  29. K. Tsuge, Y. Chishina, H. Hashiguchi, Y. Sasaki, M. Kato, S. Ishizaka and N. Kitamura, Coord. Chem. Rev., 2016, 306(Part 2), 636–651 CrossRef.
  30. X. Hei, W. Liu, K. Zhu, S. J. Teat, S. Jensen, M. Li, D. M. O’Carroll, K. Wei, K. Tan, M. Cotlet, T. Thonhauser and J. Li, J. Am. Chem. Soc., 2020, 142, 4242–4253 CrossRef CAS.
  31. H. Li, Y. Lv, Z. Zhou, H. Tong, W. Liu and G. Ouyang, Angew. Chem., Int. Ed., 2022, 61, e202115225 CAS.
  32. W. Liu, W. P. Lustig and J. Li, EnergyChem, 2019, 1, 100008 CrossRef.
  33. Y. Fang, W. Liu, S. J. Teat, G. Dey, Z. Shen, L. An, D. Yu, L. Wang, D. M. O'Carroll and J. Li, Adv. Funct. Mater., 2017, 27, 1603444 CrossRef.
  34. P. C. Ford, E. Cariati and J. Bourassa, Chem. Rev., 1999, 99, 3625–3648 CrossRef CAS.
  35. K. R. Kyle, C. K. Ryu, P. C. Ford and J. A. DiBenedetto, J. Am. Chem. Soc., 1991, 113, 2954–2965 CrossRef CAS.
  36. H. Tong, H. Li, H. Li, Cidanpuchi, F. Wang and W. Liu, Inorg. Chem., 2021, 60, 15049–15054 CrossRef CAS.
  37. W. Liu, Y. Fang, G. Z. Wei, S. J. Teat, K. Xiong, Z. Hu, W. P. Lustig and J. Li, J. Am. Chem. Soc., 2015, 137, 9400–9408 CrossRef CAS.
  38. C. Tard, S. Perruchas, S. Maron, X. F. Le Goff, F. Guillen, A. Garcia, J. Vigneron, A. Etcheberry, T. Gacoin and J.-P. Boilot, Chem. Mater., 2008, 20, 7010–7016 CrossRef CAS.
  39. A. M. Musa, J. Kiely, R. Luxton and K. C. Honeychurch, TrAC, Trends Anal. Chem., 2021, 139, 116254 CrossRef CAS.

Footnote

Electronic supplementary information (ESI) available: Experimental details, structural plots of the coupling reagents, luminescent decay plot. See DOI: https://doi.org/10.1039/d2ma00956k

This journal is © The Royal Society of Chemistry 2023
Click here to see how this site uses Cookies. View our privacy policy here.