Sadia Hassan*a,
Namra Bilalb,
Tooba Javaid Khana,
Murtaza Najabat Alia,
Bakhtawar Ghafoora and
Khawaja Usman Saifc
aSchool of Mechanical and Manufacturing Engineering (SMME), National University of Sciences and Technology, Islamabad, Pakistan. E-mail: shassan.phd20smme@student.nust.edu.pk
bNencki Institute of Experimental Biology, Poland
cIsra University, Islamabad, Pakistan
First published on 1st July 2024
Endowing implanted biomaterials with better hemocompatibility, anticoagulation, antioxidant and antiplatelet adhesion is necessary because of their potential to trigger activation of multiple reactive mechanisms including coagulation cascade and potentially causing serious adverse clinical events like late thrombosis. Active ingredients from natural sources including Foeniculum vulgare, Angelica sinensis, and Cinnamomum verum have the ability to inhibit the coagulation cascade and thrombus formation around biomedical implants. These properties are of interest for the development of a novel drug for biomedical implants to potentially solve the current blood clotting and coagulation problems which lead to stent thrombosis. The objective of this study was to incorporate different anticoagulants from natural sources into a degradable matrix of chitosan with varying concentrations ranging from 5% to 15% and a composite containing all three drugs. The presence of anticoagulant constituents was identified using GC-MS. Subsequently, all the compositions were characterized principally by using Fourier transform infrared spectroscopy and scanning electron microscopy while the drug release profile was determined using UV-spectrometry for a 30 days immersion period. The results indicated an initial burst release which was subsequently followed by the sustained release pattern. Compared to heparin loaded chitosan, DPPH and hemolysis tests revealed better blood compatibility of natural drug loaded films. Moreover, the anticoagulation activity of natural drugs was equivalent to the heparin loaded film; however, through docking, the mechanism of inhibition of the coagulation cascade of the novel drug was found to be through blocking the extrinsic pathway. The study suggested that the proposed drug composite expresses an optimum composition which may be a practicable and appropriate candidate for biomedical implant coatings.
There has been extensive research for decades to improve the surfaces and materials of medical implants to decrease the rate of rejections which were caused by the host immune response, thrombo-inflammatory cascades, infections, mechanical and biocompatibility issues and allergic reactions.4 Therefore, the materials of implants, their framework and surfaces are modified in such a way that these do not protect their structural and compositional integrity against well-orchestrated thrombo-inflammatory cascades but also inhibit the activation of the coagulation cascade, complement system, cellular inflammatory mechanisms, and platelets.5 There are many ways to enhance the compatibility of medical devices with the body, i.e., structural, or chemical modifications of implant surfaces, and these modifications have already been proposed in literature. For example, Asadi et al. used a combination of silk fibroin and cellulose nanocrystals to increase the corrosion resistance orthopedic implants.6 In our previous study, we used graphite-based hard materials to enhance the anticoagulation and biocompatibility of the medical implants.7 There are also bioactive strategies which use pharmacologic active ingredients for the inhibition of the coagulation and immune response by local drug delivery or permanent immobilization of an active agent on the surface.8,9
Thrombosis is one of the major issues which are responsible for the adverse effects of implants and their failure. The platelet activation and coagulation around the implant can block the blood flow and isolate the implant from the surrounding environment rendering it unable to perform its functions. To reduce the chances of thrombus formation, different anticoagulation based materials are used i.e., heparin which has been found to be most efficient in reducing the thrombus formation by over 70%.10 Despite of its efficiency, it has been associated with heparin-induced thrombocytopenia which can increase the risk of clots forming around the coated surface.11 Many other anticoagulants including warfarin,12 aspirin,13 and acenocoumarol14 have been reported to be used for biomedical implants applications to reduce the rate of thrombosis. Nevertheless, these molecules have high potency, short-term effects and chances of severe bleeding which makes them an unfavorable choice.
In recent years, scientists have provided alternatives to heparin by introducing low molecular weight heparin,15,16 antithrombin heparin17,18 and natural anticoagulants.19 There has been a keen interest in natural anticoagulants because of the lower risks of adverse events. Among natural anticoagulants includes A. sativum,20 C. longa,21 C. cassia,22 A. sinensis,23 P. ginseng24 and O. tenuiflorium25 which are well reported for their effectiveness and feasibility in biomedical applications. In our latest study, we reported the anticoagulation effects of individual and combined effects of C. cassia, O. tenuiflorium and P. ginseng for biomedical applications9 and in this study, we focused on C. verum, A. sinensis and F. vulgare based drugs and tried to explore their suitability for biomedical implants applications.
Plant based drugs have always been a point of focus because of their mild efficacy, effectiveness and compatibility with human body. C. verum (Cinnamomum verum) is an Asian spice and commonly found in Indian, Chinese and Sri Lankan regions. It has been famous for its antioxidant, anti-inflammatory, and antimicrobial properties. There are different studies in literature which demonstrated the benefits of this spice in different diseases including diabetes,26 infections,27 cancer,28 and wound healing.29 These properties come from its components including cinnamaldehyde, cinnamic acid, coumarins, diterpenoids, and polyphenols.30,31 Like cinnamon, A. sinensis has many medicinal properties due to ferulic acid and Z-ligustilide being the major actives in the extract. It has anti-inflammatory and anti-platelet aggregation abilities. It has been famously used for the treatment of female irregular menstruation and amenorrhea.32 Lastly, Foeniculum vulgare (commonly known as fennel) is a widely used herb and spice. The Fennel seeds are considered an important source of trans-anethole, fenchone, estragole and other ingredients which are responsible for providing protection from infections, digestive problems and reduce inflammation.33 There are many studies on literature which showed its therapeutic effects against cardiovascular ailments and cancer.34,35
The selection of a suitable drug carrier is a critical step as it works synergistically with the drug to ensure effectiveness of functions of biomedical implants. Looking at commercial coronary implants, initial stents (cypher and taxus) had non-degradable polymeric drug carriers including polyethylene vinyl acetate36 and poly(styrene-block-isobutylene-block-styrene),37 respectively. After recognizing the limitations of permanent polymers in first generation of stents, researchers directed their focus towards biodegradable alternatives. Amomg different polymer poly(lactic acid) (PLA) and its derivatives, particularly poly(lactic-co-glycolic acid) (PLGA), poly(L-lactic acid) (PLLA), and poly(D,L-lactic acid) (PDLLA), grabbed the attention due to their biocompatibility, flexibility and degradation properties.36 These polymers are used in contemporary drug-eluting stents (DES) like orsiro and synergy, which currently dominate the market. A key challenge associated with stents which has PLA is a drug carrier is the discrepancy between degradation time of drug carrier (18–24 months) and the desired drug release window (4–12 months).38 Now, extensive research efforts are aimed at using those polymers whose degradation profiles closely align with optimal drug release kinetics i.e., poly(glycolic acid),39 chitosan40 and polyvinyl alcohol.41 Chitosan is a commonly used in biomedical applications due to hydrophilicity, biocompatibility, biodegradability, and bioactivity. Use of chitosan for coronary stents have already been reported in various studies because it has heparin-like polysaccharide structure. In literature, Qiu et al.42 used chitosan to create the structure of bioresorbable coronary stents. In their study, chitosan was successfully used to develop bioresorbable coronary stents using 3D printing and these stents exhibited a promising degradation profile, with only 10% degradation observed within the first 30 days. This finding highlighted the potential use of chitosan for controlled degradation in biomedical devices. In another study, Meng et al.43 reported the use of chitosan for coronary stents by making a composite of chitosan with a strong anticoagulant (heparin). This study was aimed to develop a similar composite material utilizing natural anticoagulants instead of synthetic ones. Yang et al.44 also used Chitosan a drug carrier for coronary stents by combining it with anti-CD34 antibody and sirolimus. The evidence presents in the literature regarding the application of chitosan as a drug carrier for various biomedical applications established its potential for our study. Consequently, chitosan was selected as a polymeric drug carrier for novel anticoagulants in this investigation.
The coating of antiplatelet or anticoagulant drugs on medical implants have gained interest as these drugs are able to either block the coagulation cascade or decrease the platelet adhesion capability and ultimately decreasing the rate of thrombus formation.45–47 In this study, we are exploring the anticoagulation behavior of, A. sinensis, F. vulgare and C. verum for the application of biomedical implants coatings to avoid the issue of thrombosis at the implant site. There have been numerous studies in which their anticoagulation and anti-oxidative behavior potential was investigated;48–51 nevertheless, there is a lack of literature on the applications for biomedical implants as coating material. In this study, drug loaded polymeric matrixes were fabricated and optimized to impart the anticoagulation properties in medical implants. The novelty of the project lies in the drug-polymer combinations and their applications in medical implants. Lastly, these novel polymeric compositions may be served as an alternative to synthetic drugs and reduce the issues associated with them. Furthermore, this will also give us an opportunity to explore the behavior and interaction of drugs which is still an untapped field.
Sample ID | Chitosan (%) | Cinnamomum verum (%) | Angelica sinensis (%) | Foeniculum vulgare (%) | Heparin (%) |
---|---|---|---|---|---|
C | 2 | — | — | — | — |
CC5 | 5 | — | — | — | |
CC10 | 10 | — | — | — | |
CC15 | 15 | — | — | — | |
CD5 | — | 5 | — | — | |
CD10 | — | 10 | — | — | |
CD15 | — | 15 | — | — | |
CF5 | — | — | 5 | — | |
CF10 | — | — | 10 | — | |
CF15 | — | — | 15 | — | |
CCDF | 5 | 5 | 5 | — | |
CH | — | — | — | 5 |
(1) |
(2) |
All results were estimated from the data of three individual experiments, and the reported data were expressed as mean ± SD.
(3) |
Now, the pellet of red blood cells was exposed to the S1 solution for 4 hours at room temperature. After incubation, the S1 solution was centrifuged at 5500 rpm for 5 minutes. The supernatant was collected for UV-vis spectrophotometry analysis at 540 nm.56
The PBS solution was used as blank, and 0.5% Triton X-100 solution was used as positive control. Following eqn (4) was used for calculation.60
(4) |
For PT test, platelet-poor plasma was obtained by the centrifugation of fresh blood at 2500 rpm for 10 min. Now, the samples were placed in Thrombolyzer (Behnk Elektronik GmbH & Co. Germany) along with 1 mL plasma and PT reagent (CaCl2 + plasmathrombin) at 30 min at 37 °C.61 The machine automatically measured the PT time and gave a reading on the machine display.
Similar process was repeated for APTT test in which APTT reagent was used instead of PT reagent.62,63 The APPT time was displayed on the screen of machine.
The structural data of anticoagulation proteins including thrombin (3u69), factor V(7kve), factor VIIa (1qfk) and factor IXa (6mv4) were downloaded from Worldwide Protein Data Bank67 and saved in format *.pdb ready for docking simulation. The structures of drug ligands were downloaded from PubChem database and saved in format *.sdf.
The structure of proteins and ligands were submitted to CB DOCK and predicted poses were retrieved. For the selection of best pose and interaction, the values of free energy were utilized. For the analysis of drug protein interaction PyMol (The PyMOL Molecular Graphics System, Version 2.0 Schrödinger, LLC) and LigPlot++68 were used. For the 3D visualization of macromolecules, PyMole and 2D ligand–protein interaction LigPlot++ was employed.9 In addition, ligand conformation and orientation in its inhibited-protein active site was visualized on 2D planes.69–71
The films loaded with drugs demonstrated a rough surface having drug particles on the surface. To explain briefly, the C. verum loaded film (CC15) showed the presence of a few drug particles on the surface. In addition, the surface seemed rougher as compared to bare chitosan film which may be an indication of a structural change caused by drug loading in the polymeric chains of the matrix. In literature, it was observed that addition of cinnamon essential oil in the chitosan matrix resulted in emergence of pore and holes;73,74 however, in this study a lack of porous surface was observed which indicated that drug particles only integrated themselves inside the matrix and did not damage the surface of films. Therefore, it can be speculated that pure extract of C. verum had better compatibility with chitosan matrix as compared to its oil-based emulsions.75
Similarly, F. vulgare and A. sinensis loaded films CD15 and CF15, respectively flaunted the presence of drug particles on the surface as well as inside the polymeric matrix. The particles on the surface of CD15 had small, round and protruding shape which were similar to the appearance of particles of pure A. sinensis described by Wu et al.76 From literature, it was found that the essential oils of F. vulgare were not compatible with chitosan-based films because it damaged the surface and made small pores.77 The reason could be the weakening of the cohesive forces of matrix due to oil-based formulations of essential oils; however, these challenges were not posed by extracts of drugs. In this study, the use of pure F. vulgare extract did not pose any harmful effects which could compromise the integrity of the matrix; therefore, matrix retained its flat surface.
The morphology of CCDF was unexpected as a stark difference was found between the appearance of neat Chitosan films and CCDF films as shown in Fig. 1. The CCDF films had a granny appearance similar to the appearance reported by Ashvini et al. and Čalija et al. which indicated presence of high amount of drug on the surface.78,79 Although CCDF had 15% drug concentration just like other thin film samples (CF15, CD15 and CC15), the amount of drug on CCDF was far more than the amount present on other thin films. In addition, the appearance of CCDF was also different from other individual compositions and it was speculated that the affinity of drugs with the matrix decreased upon incorporating them in the form of composite. This can cause an initial burst release and then a sustained drug release kinetics.
After evaluating the morphology of thin films, compositional analysis was performed to map out the drug–polymeric interactions. First, FTIR spectrum for each thin film was obtained and compared with each other in Fig. 1(B). This figure explains the effects of different drugs and their concentrations on polymeric matrix and demonstrated the characteristic bands of chitosan in the frequency range between 4000 and 400 cm−1.
Upon the observation of neat chitosan film, the presence of sharp peaks was confirmed at 564 cm−1 (out-of-plane bending NH, out-of-plane bending C–O), 901 cm−1 (amines), 1013 cm−1 (C–N stretch), 1069 cm−1 (C–O stretching), 1174 cm−1 (stretching of the C–O–C), 1389 cm−1 (amide III region), 1410 cm−1 (C–C stretch), 1562 cm−1 (amide II, stretching vibrations of C–O), 1656 cm−1 (CC stretch), 2149 cm−1, 2858 cm−1, 2939 cm−1 and 3386 cm−1 (dimeric OH stretch).80–83
The peaks at 1013 cm−1 and 1069 cm−1 indicating C–N stretch, C–O stretching, respectively was present in all the compositions; however, their intensity decreased by the addition of drugs (Fig. 1(B)) and in composite of drugs, it was almost flattened. The intensity of peaks at 2930 and 2863 cm−1 in chitosan remained intact in CD15 composition and reduced in all the other compositions; nevertheless, it disappeared completely in the composite. As these peaks indicated dimeric OH stretching, the reduction in intensity may show the hydrogen bonding between functional groups of drugs and NH and OH groups of chitosan. In addition, same pattern was observed at peaks between 3000 to 3500 cm−1 which represented the presence of free hydroxyl groups.84
By looking at individual compositions of drugs, it was found that F. vulgare-chitosan films demonstrated an increase in peak intensity by increasing the F. vulgare concentration. The peaks at 650, 1260 and 1640 indicated the presence of anethol (which is major constituent of F. vulgare) and other phenolic groups of F. vulgare.83 In addition, J. Hussein, Hadi, & Hameed, 2016 proved the presence of aliphatic fluoro compounds at 1029 cm−1, alcohols at 1244 cm−1 and phenols and hydroxyl groups at 3244, 3275 and 3361 cm−1 in F. vulgare.85 Furthermore, the FTIR spectra of each film containing F. vulgare were similar in composition and no chemical reaction occurred that produced new substances. The results of FTIR spectroscopy explained the intermolecular interaction and molecular compatibility between the functional groups in F. vulgare and hydroxyl and amino groups in the chitosan chain.
The A. sinensis and C. verum loaded films at varying concentration showed similar patterns to the F. vulgare loaded films. The spectra demonstrated an increase in the intensity of peaks with an increase in concentration of A. sinensis in the chitosan matrix. The intensity of bands at 1004–1050 cm−1, 1400–1600 cm−1 and 2800–3000 cm−1 increased and these peaks exhibit the presence of pyranose monomers, carboxylic group and C–H asymmetric stretching vibration of the methyl group, respectively.86 Above 3000 cm−1, lesser peak intensity identified the decreased number of free –OH groups proving the string hydrogen bonding between A. sinensis and chitosan.
In Fig. 1(C), the effects of loading of different drugs in chitosan matrix were observed. It was found that addition of A. sinensis had a negligible impact on the intestines of the chitosan spectrum showing a weakest bonding between A. sinensis and chitosan. In comparison, F. vulgare and C. verum showed a significant impact on the composition of chitosan and a prominent decrease in intensities of chitosan matrix was observed. It showed that both C. verum and F. vulgare had a strong compatibility with chitosan matrix. A particularly conspicuous decrease in peak intensities was observed in CCDF specimen as the interaction between drug molecules and chitosan matrix was so strong that it flattened many peaks. It also proves the compatibility of all three drug molecules with each other and with polymeric matrix.
The difference between the compositions of neat chitosan film and CCDF specimen is shown in Fig. 1(D). It showed a sharp decrease in the peak intensities of polymeric matrix after addition of the drug extracts. It also showed a strong interaction between drug particles and polymeric matrix which ensured that drug was not just loosely present on the surface (as shown in SEM analysis) but also embedded inside the matrix and was interacted with polymeric chains.
Overall, the morphological and structural analysis showed that drug molecules not only attached themselves on the surface of the thin films but also interacted with polymeric chains of the matrix and made hydrogen bonding. This kind of interaction helps in an initial burst release followed by a sustained release drug kinetics. In addition, no new peaks emerged in spectrum indicating intact chemical structure of chitosan matrix and absence of any compositional modifications.
In Fig. 2(D’), it was observed that pure chitosan lost more than 20% matrix in 24 hours and after that the rate of degradation was slowed down and roughly 70% mass was lost in 30 days. The degradation pattern of chitosan matrix was just like one reported by Bryuzgina et al. for chitosan films.87 The initial degradation was attributed to the hydrolysis of polymeric chains which opened the cavities on the surface of thin films and lost mass. With the passage of time, these cavities kept increasing in size and number which caused the loss of structural integrity of films leading towards the complete degradation of matrix.
It was observed that the incorporation of drug extracts into matrix affected the degradation rates of the chitosan films. As shown in Fig. 2, among all the compositions, A. sinensis loaded films had the most obvious effects on the chitosan matrix as it degraded the whole matrix within 5 days. Overall degradation rate was A. sinensis > F. vulgare > C. verum > composite.
The patterns of degradation of C. verum loaded films remained the same for all three compositions; however, it affected the rate of weight loss as shown in Fig. 2(A’). The CC5 exhibited the fastest polymer degradation rate indicating 84% weight loss in 30 days. The rate of weight loss reduced when the concentration of drugs was increased in CC10 and CC15 specimens as the depicted 77% and 75% degradation in a month. The results indicated that addition of C. verum loosened the chains of polymeric matrix and occupied the new gaps in the matrix; thus, it made the film vulnerable to hydrolytic degradation. Nevertheless, increase in drug concentration decreased the degradation of matrix. The reason may be that at higher drug concentrations, the volume of drug particles occupying open spaces inside matrix increased which reduced the catalytic sites for hydrolysis resulting in a sturdier specimen that resisted degradation for longer period of time.88
The F. vulgare loaded films (CF5, CF10, CF15) demonstrated degradation patterns similar to the patterns of C. verum loaded films as presented in Fig. 2(C’). The sequence of degradation was CF5 > CF10 > CF15. The CF5 films degraded within 5 days demonstrating fastest weight loss among all the specimens. In a study, Yulizar et al. reported the catalytic activity of F. vulgare in a nanocomposite which promoted the cleavage of the polymeric chains of drug carrier.89 This activity may have role in unstableness of the chitosan matrix in CF5 specimen which resulted in complete loss of weight of polymeric films within 5 days. The remaining compositions CF10 and CF15 demonstrated that only 17% and 22% matrix remained respectively, after 30 days which was similar to C. verum loaded films.
Surprisingly, the situation was different for A. sinensis loaded films which exhibited 85%, 78% and 76% matrix degradation after 24 hours for CD5, CD10 and CD15 specimens, respectively (Fig. 2(B’)). The A. sinensis is rich in polysaccharides and other components which may have interfered with the three-dimensional polymeric structure of chitosan resulting in weakening of intermolecular forces and degradation of matrix. The ions and drug components released from A. sinensis initiated the drug-mediated hydrolysis of matrix and caused the scission of polymeric chains.90
The results of CCDF degradation (Fig. 2(D’)) revealed slower weight loss of chitosan matrix. The results demonstrated that 15% and 23% CCDF matrix was degraded in 24 hours and 48 hours, respectively. It was observed that the rate of matrix degradation became slower after 2 days and only 30% and 34% matrix could be degraded within 15 and 30 days, respectively. These results indicated that the composite of three drugs had strong affinity with the polymeric chains of matrix and protected the cleavage side from the attacks of ions or other catalytic moieties. Secondly, FTIR analysis in Fig. 1(D) showed that the intermolecular forces i.e., covalent bonds, H-bonds and van der Waals forces were stronger between chitosan and drug molecules as compared to intramolecular forces of chitosan which resulted in slower degradation rates of CCDF versus neat chitosan matrix.
If we compare these results with commercially available implants, this degradation rate is comparable to Orsiro cardiac implant [Biotronik Germany] and Ultimaster cardiac implant [Terumo, Japan].36 Clinical studies have shown that the Orsiro implant system utilized PLA material as a drug carrier. This PLA material underwent a slow degradation, with approximately 6% degrading within the first 30 days. Like the Orsiro implant, Terumo exhibited a degradation profile where roughly 20% degraded within the first 30 days, with complete degradation in 150 days.91 The results of CCDF are little faster than these systems as roughly 34% matrix was degraded in 30 days which shows that CCDF system holds promise as a viable drug delivery platform.
The drug release of polymeric matrix greatly depends upon the degradation rate and affinity between drug and polymer. The effects of different concentrations of drug and different types of drugs on the release kinetics had been observed in this study and presented in Fig. 2(A)–(D). The results indicated that all compositions underwent an initial burst release which was followed by a sustained drug release from the matrix. It was found that varying the drug type affected the release kinetics differently and overall pattern of drug release was A. sinensis > C. verum > F. vulgare > composite.
As shown in Fig. 2(A), the C. verum loaded films had intermediate drug release kinetics among other compositions and by increasing the amount of drug in the matrix, the release became slower. The trend of C. verum release from matrix was CC5 > CC10 > CC15. The drug release kinetics were heavily dependent upon the polymer degradation rate because hydrolytic cleavage of chains generated free spaces and voids that opened up the drug pockets inside the matrix and released it into the solution. Therefore, polymeric matrix of CC5, CC10 and CC15 degraded 27%, 16% and 14%, respectively within 24 hours, 5%, 1% and 3% drug was released. After one month, the remaining drug in the matrix was 9%, 20% and 27%, respectively.
The A. sinensis loaded matrix demonstrated unusual drug release pattern (Fig. 1(B)) as compared to the drug release kinetics of other drugs; however, it was translated according to the degradation of matrix exhibited in Fig. 2(B’). The CD5 specimen released 100% drug within 7 days which was due to complete degradation of polymeric matrix containing the drug. The other two compositions released 84% and 70% drug within 30 days. Although the matrix was completely dissolved, the remaining drug could not be detected in the solution. The reason may be the strong attachment of A. sinensis particles with polymeric broken chains which did not allow the release of drug into the solution even after the matrix degradation. At lower concentration, F. vulgare loaded films (CF5) degraded fast and released all the drug within a short span of time as shown in Fig. 2(C) and (C’); however, the CF10 and CF15 specimens exhibited a steady drug release up to 50% in 30 days.
When the drugs were combined and incorporated into the matrix (CCDF), it not only slowed down the rate of polymer degradation but also made the matrix strong to hold the drug for longer period of time as presented in Fig. 2(D). There was an initial burst release within 24 hours which was followed by the sustained drug release pattern. Looking at the drug release patterns of commercially available drug eluting coronary stents, it was found that initial burst release of drug followed by a sustained drug release is necessary for appropriate healing of lesion at target site.36 The reason is that when medical devices are implanted inside human body, these create a lesion at target side to open the blocked area; hence, creating a lesion at the site which invites a plethora of platelets and growth factors to heal the lesion and can trigger the coagulation cascade leading to the early thrombus formation and device failure.92 If an anticoagulant is coated on the medical device, it will be able to suppress the early thrombus formation through burst release of drug and once critical window is passed, it will keep releasing the drug in sustained manner.
In conclusion, chitosan-based drug loaded matrix demonstrated appropriately slower degradation rate as compared other polymers including poly lactic acid and poly vinyl school which made it suitable for drug coated biomedical implants. In addition, increasing the drug in the matrix slowed down the degradation rate. The free drug particles on the surface of matrix not only cause the initial burst release but also their removal from the surface expose the matrix to external environment and give an opportunity to water molecules to seep inside matrix and accelerate the degradation pattern. Furthermore, the degradation of matrix creates voids and spaces in the matrix which further increases the degradation rate. The results of chitosan-based matrixes were a bit surprising due to strong interaction between drug and protein molecules which caused a very slow release of drug from the matrix.
All the films exhibited a significant scavenging ability in a dose dependent manner. To explain further, the films of F. vulgare, CF15, CF10 and CF5, demonstrated the highest ability of ROS scavenging which increased in ascending manner along with drug concentration i.e., 61, 69.2 and 70.9, respectively. CF15 had 70.9% (p = 0.0001) antioxidant activity and it was significantly better than heparin loaded films which were used as experimental control throughout the study. The higher antioxidative properties may be associated with the presence of phenolic compounds and trans-anethole in F. vulgare. In addition, the increase in F. vulgare concentration in matrix may increase the concentration of antioxidative compounds which ultimately enhanced the antioxidation properties. These results were in line with the findings of Oktay et al. who reported up to 99% of antioxidant activity of F. vulgare and showed that its free radical scavenging activity increased with increasing drug concentration.93
The thin films loaded with A. sinensis showed significant antioxidation capability [CD5 = 48.3% (p = 0.0001), CD10 = 48.6 (p = 0.0001) and CD15 = 50% (p = 0.0001)]; however, it was the lowest among other drug loaded thin films. A. sinensis had phenols, ferulic acid and caffeic acid that were responsible for the antioxidation properties.94 In a study, Huang et al. demonstrated a positive relationship between phenols and antioxidant properties of A. sinensis;95 nevertheless the processing conditions (like time or ethanol concentration) during extraction may affect the antioxidation capabilities.
It is notable that chitosan itself has good antioxidation capacities (62%) and literature has suggested replacing the synthetic antioxidants with chitosan-based material [580, 581]. In this study, the antioxidation abilities of drug loaded chitosan matrix were elevated which were observed on all films particularly in consortium of different drugs (CCDF) as it demonstrated 76.1% (p = 0.0001) antioxidation capability. In contrast, loading of heparin into chitosan decreased (40% p = 0.0001) the antioxidation capabilities. The antioxidative capabilities of heparin are debatable as Lapenna et al. and Mohanty et al. had reported that heparin did not possess the antioxidation capabilities.96,97 Compared to CCDF and other specimens, commercially available synthetic anticoagulants heparin and aspirin exhibited lower antioxidant potential. Oliveira et al.98 reported that aspirin demonstrated less than 20% antioxidant activity as measured by the DPPH radical scavenging capacity assay. In contrast, CCDF specimen demonstrated more than 70% antioxidative potential. Higher antioxidative potential helps to neutralize ROS and reduce oxidative stress which ultimately lessens the inflammatory cascades. It also enhances the biocompatibility of materials and in case of bone implants, it reduces periprosthetic osteolysis and promote bone healing.
Overall, CCDF showed excellent antioxidation properties as compared to synthetic drug in this study and ability to protect the body from harmful effects of ROS species during thrombo-inflammatory reactions.
The highest hemolysis potential (2%) was demonstrated by CF15 specimen; however, this value comes under the range of non-hemolytic materials. The lowest hemolytic potential was shown by CF5 which shows that lesser concentrations of F. vulgare does not cause the disruption of RBCs; however, the increasing concentrations have effects on the rupture of RBCs. These results were in agreement with Sharopov et al. who reported that the essential oil of F. vulgare can lyse the membranes of cells at higher concentrations. At lower concentration, it does not have any harmful effects on blood cells.99 Similarly, Qui et al. described the non-hemolytic behavior of fennel oils in literature and proved the safety of F. vulgare for medical applications.100
The hemolytic potential of pure chitosan was 1.1% (as shown in Fig. S6 in ESI†) which was not affected by the addition of C. verum; however, it increased to 1.2%, 1.7% and 1.8% by the incorporation of 5%, 10% and 15% A. sinensis into the matrix (CD5, CD10, and CD15 respectively). In literature, Salehi et al. provided results similar to this study and proved that increasing concentration of C. verum can enhance hemolytic potential, but it was not significant.101 López-Mata et al. provided the insights about cinnamon loaded chitosan films and found them non-hemolytic.102 Chang et al. evaluated the effects of ethanolic AS extract on blood parameters of rats and found it to be a promising therapeutic candidate for biomedical applications.103 The consortium of the drugs (CCDF) also demonstrated a non-hemolytic behavior by showing 1.5% blood hemolysis. In conclusion, all the drugs either individually or in the composite form were non-hemolytic and potentially invulnerable for biomedical applications.
According to ISO standard 10993, determining the biocompatibility of medical implants is necessary and one crucial test mandated by this standard is the evaluation of hemolytic potential of the implant. All the specimens in this study had non-hemolytic potential just like the results demonstrated by Kuznetsov et al.104 when they tested their biomedical implant specimens in rabbit iliac artery. Reassuringly, similar results were observed when Meng et al.105 evaluated the hemolytic potential of magnesium alloy, a promising material currently under investigation for erodible biomedical implants. The concordance of results of this test with prior research from literature suggests that specimens of this study possess promising qualities for biomedical implant applications.
Specimen ID | APTT | PT | INR |
---|---|---|---|
Chitosan | 31 ± 0.4 | 14.5 ± 0.4 | 1.1 |
CC5 | 30 ± 0.1 | 14.6 ± 0.1 | 1.1 |
CC10 | 30 ± 0.3 | 14.8 ± 0.3 | 1.2 |
CC15 | 30.9 ± 0.1 | 15 ± 0.1 | 1.2 |
CD5 | 30.2 ± 0.3 | 14.6 ± 0.3 | 1.1 |
CD10 | 30.2 ± 0.1 | 15 ± 0.1 | 1.2 |
CD15 | 40.7 ± 0.2 | 15.5 ± 0.2 | 1.2 |
CF5 | 30.1 ± 0.1 | 14.5 ± 0.1 | 1.1 |
CF10 | 30.2 ± 0.1 | 14.8 ± 0.1 | 1.2 |
CF15 | 31.1 ± 1.1 | 15.2 ± 1.1 | 1.2 |
CCDF | 30 | 135 | 13.1 |
CH | 135 | 45.8 ± 1 | 3.99 |
The results of the anticoagulation test showed that all the thin film samples have anticoagulation activity. Among all the drugs, A. sinensis had the highest ability of blocking coagulation cascade and could delay the blood coagulation more than two seconds (15.5 s) as compared to normal blood coagulation (13 s). Also, the anticoagulation potential of directly related to the concentration of drug loading in films as CD15 exhibited highest anticoagulation activity. These results are in line with the findings reported by Lee et al. in a clinical study in which anticoagulation potential of A. sinensis was reported along with a few other herbs was evaluated in 75 patients106 and results showed that A. sinensis has a significant impact on anticoagulation of blood and even found to reduce the epinephrine-induced aggregation in 2 subjects. In another study, Wang et al. analyzed the constitutes of A. sinensis and reported that its anticoagulation activity potential comes from the constitutes from petroleum ether-soluble fraction. Upon further analysis, 26 components were found which belonged to phenol acids, the phthalides, and the aliphatic acids and among these components, phthalic acid, vanillic acid, ferulic acid, senkyunolide I, butylphthalide, ligustilide, linolenic acid, senkyunolide D and senkyunolide F were majorly responsible for the anticoagulation activity.107
The F. vulgare also demonstrated mild anticoagulation potential as it was able to delay the blood coagulation by a few seconds in both PT and APTT test (described in Table 2). The trend of anticoagulation activity was directly related to the concentration of drug loaded in thin films as CF5 was able to delay the coagulation time by 2.5 seconds in comparison to anticoagulation potential of CF15 which delayed the coagulation time by 3.2 seconds. In literature, anticoagulation effects of F. vulgare have already been proven through different clinical studies in which a delay in coagulation time was observed after orally taking F. vulgare.108 Even Farid et al. reported immune enhancement, and antimutagenic efficacy of F. vulgare by using human blood cultures.109
The anticoagulation potential C. verum was similar to other two drugs as it also demonstrated an increase the anticoagulation activity with an increase in the drug concentration in the polymeric matrix. Cinnamon has been historically famous herbal medicine and an anti-inflammatory dietary supplement which has proven antidiabetic,110 anti-inflammatory111 and anticoagulant properties9 due presence of components like cinnamaldehyde, coumarin, limonene, α-terpineol and many others.112 In a study, antithrombotic and antiplatelet effects of plant-derived compounds were analyzed by Kubatka et al. and it was reported that cinnamic acid which is an essential component of cinnamon has a strong ability of anticoagulation113 and could delay the blood coagulation time by 18.2 s.114 In our study, it was able to delay the coagulation time by a few seconds and it could be retardation of the activity could be related to drug polymer relationship as embedding a drug in polymeric matrix may affect the pharmacological activities of drug components. Overall, all the polymeric matrixes loaded with C. verum demonstrated mild anticoagulation activities.
When all the drugs were combined in single matrix (CCDF), a sudden rise in anticoagulation activities was observed. For individual drugs, the coagulation time was prolonged for only a few seconds; however, the consortium of drugs prolonged the time for more than 130 seconds. This phenomenon was surprising; nevertheless, in depth deliberation showed that all three drugs were compatible each other and instead of affecting each other's structure and functions, these complemented each other and enhanced the functionality. We also found the evidence from literature that one of drug component A. sinensis does not have a strong anticoagulation potential; however, when combined with other anticoagulants, it significantly enhances the overall activity of the drugs.115 This phenomenon is line with herb–herb combination theory and multi-item concoction which explained that factors like synergistic multi-target effects receptors and proteins, change in pharmacokinetic or physiochemical effects based on improved solubility, resorption rate, and enhanced bioavailability and neutralization of adverse effects other substances present in the mixture may be associated with enhanced activity of herbs in a combined dosage form.116
In this study both PT and APTT analysis were performed and interestingly, the individual thin films loaded with A. sinensis showed a gradual increase in anticoagulation activity in PT test with increasing the drug concentration in the matrix; however, no activity was observed in lower concentrations of drug during APTT testing and only CD15 showed an anticoagulant activity. It is known that drugs can inhibit the coagulation cascade either by blocking extrinsic pathway or intrinsic pathway. The lack of activity during APTT testing showed that these drug molecules are unable to affect the proteins of intrinsic pathway (factors XII, XI, IX, and VIII). Similar results were found in other individual drug-polymer compositions; however, CCDF specimen did not show an activity in APTT analysis and a high activity in PT analysis exhibiting a lack of interaction with proteins of intrinsic pathway and a strong relationship with proteins of extrinsic pathway and vis versa was true for heparin loaded polymeric matrix. This information was helpful for mapping out the inhibitory pathway for our proposed drug.
The first successful human trials of Palmaz-Schatz coronary stents were coated with the strong anticoagulant heparin117 and in our study, natural drugs with potent anticoagulation potential were used because heparin is associated with the risk of spontaneous bleeding and thrombocytopenia. Therefore, Lu et al. developed heparin-like anticoagulant polypeptides which had anticoagulative and clot solubilities properties.118 A previous study by Ozaltin et al.119 proposed polyethylene terephthalate (PET) surfaces modified with plasma-immobilized fucoidan as a material for medical implants because this modification extended the PT of surface more than 20 seconds which demonstrated that it gained anticoagulant properties. Our surface exhibited an anticoagulation potential exceeding theirs by more than tenfold. Thus, biomedical implants with anticoagulant properties demonstrably enhance clinical outcomes and device performance.
As CCDF specimen demonstrated best anticoagulation potential among all the specimens, it was selected for further analysis.
In literature it was found that components like ferulic acid,120 senkyunolide121 and phthalide derivatives from A. sinensis are responsible for anticoagulation activities of the drug extract; therefore, it was assumed that in CCDF specimen, these two components are playing a role in blocking extrinsic coagulation pathway and their interaction with VII, III, X, V, II, I, and XIII was analyzed. The interaction of ferulic acid with different proteins is demonstrated in results Fig. 4 and ESI Fig. S1.† It was found that ferulic acid had the strongest interaction with Xa protein by making more than 10 hydrophobic bonds and two covalent bonds (Fig. 4(A)–(C)). In comparison, it was making seven hydrophobic and two covalent bonds with factor V and II and nine hydrophobic bonds and one covalent bond with factor VIIa; therefore, it was speculated that ferulic acid was able to block the activity of factor Xa and Fig. 4(C) showed that it was not just a surface level interaction but the drug ligand was able to snuggle inside the cleft of factor Xa and completely block the activity. In the case of senkyunolide, it strongly interacted with VIIA protein through three covenant and more than five hydrophobic bonds (Fig. 4(A’)–(C’)). In ESI figures (Fig. S2†), it was shown that senkyunolide did not make any covalent bond with factor V and II and only made hydrophobic bonds demonstrating a rather week interaction with proteins other than factor VIIa. It was also able to penetrate in a cleft present at the surface of protein to block the activity. Overall, it was suggested that components of A. sinensis were able to block the extrinsic coagulation pathway by inhibiting the activity of factor Xa and VIIa.
For C. verum, it was found from literature that cinnamaldehyde122 and camphene123 may be responsible for the anticoagulation activities. Their interaction with proteins of extrinsic pathway were analyzed and demonstrated in Fig. 5A, ESI Fig. S3 and S4.†
Camphene is cinnamon polyphenol and its interaction with factor Xa of extrinsic coagulation pathway is depicted in Fig. 5(A)–(C) showing the presence of more than five hydrophobic bonds. Further analysis with other proteins showed that it only made hydrophobic bonds with all the proteins of coagulation cascade and did not make any hydrogen bond. In comparison, cinnamaldehyde strongly interacted with all the proteins as shown in ESI Fig. S4;† however, strongest interaction was observed with factor Xa in Fig. 5(A’)–(C’) by making multiple hydrophobic and covalent bonds. The disparity in interaction of camphene and cinnamaldehyde with factor Xa was also observed in their energy scores which were −4.6 and −5.6 kcal mol−1 (described in ESI Table 1†), respectively for both of them showing higher ligand efficiency of cinnamaldehyde. Similar analysis was performed by Khadke et al. to observe the interaction of cinnamaldehyde to evaluate its activity as anthelmintic agent.124 In conclusion, the components of CCDF coming from C. verum were able to block factor Xa which ultimately played a crucial role inhibition of coagulation cascade.
Throughout history, F. vulgare remained an important medicinal plant which had anti-inflammatory, antithrombotic and anticancer properties. It is a rich plant having multiple components; however, ferulic acid and fenchone may be responsible for its anticoagulation properties. The interaction of components of F. vulgare with the proteins of extrinsic factor is demonstrated in Fig. 6, ESI Fig. S1 and S5.† Ferulic acid demonstrated a stronger interaction with coagulation proteins as compared to fenchone which is evident from the higher number of hydrogen hydrophobic bonds between drug ligands and proteins. In addition, the ferulic acid ligand was able to penetrate inside a cavity of protein to block its activity; however, fenchone simply snuggled inside a cavity present on the surface of the protein. Overall, both components were able to attack coagulation cascade proteins from multiple sides and inhibit the activity.
As CCDF specimen was a consortium of C. verum, F. vulgare and A. sinensis, it had multiple anticoagulation components which were able to attack multiple proteins of coagulation cascade resulting in blocking the pathway for a longer period of time. This heightened effect had already been proven by the experimental data from PT and APTT testing as CCDF demonstrated a high anticoagulation potential as compared to individual compositions. The prolongation in blood coagulation plays a crucial role because it affects the endothelial process, the inflammatory response, and thrombus formation.125
Generally, anticoagulants used in biomedical industry belong to either vitamin K dependent antagonists, low molecular weight heparin, direct thrombin blockers or factor Xa blocker. The drug we are proposing belongs to direct coagulation cascade blockers as it blocked not only factor Xa but also inhibited the activity of other coagulation factors making it a more potent drug. On the basis of results of molecular docking, the potential inhibition pathway for proposed drug is explained in Fig. 7 which indicated that in the CCDF specimen, the ligands bound strongly with Xa and VIIa proteins and blocked the coagulation cascade at these two points.
Fig. 7 Proposed mechanism of action indicating that different components of CCDF specimen can bind with Xa and VIIa proteins and block them leading to inhibition of coagulation at the target site. |
Fig. 8 GC-MS analysis of PCGT specimen confirmed the presence of required anticoagulants in the CCDF specimen. |
It was known that eugenol, coumarin, camphor, and cinnamaldehyde were part of C. verum which might be associated with the strong anticoagulation activities and their presence was identified in the drug extract. Cinnamaldehyde was an important component of C. verum and its appearance was identified by comparing the results with GC-MS chromatogram of Friedman et al. which was obtained studying the different foods containing cinnamon.126 Similarly, ferulic acid, estragole and fenchone were found in F. vulgare specimens and senkyunolide was the component of A. sinensis and their presence was confirmed through literature127–133 and labelled accordingly. Overall, the results of GC-MS are in line with literature and FTIR spectrum of the drug previously described in the study.
Thrombosis is one of the major reasons for implant failure in the human body. Major precursors of thrombus formation are blood coagulation and platelet adhesion at the target site and if the rate of platelet adhesion is controlled, the coagulation and thrombus formation may be tailored according to the requirements. This study has shown that CCDF specimen has strong anticoagulation properties which reduces the rate of platelet adhesion, and it may be speculated that it would reduce the rate of thrombosis at target site.
Analysis of adhesion of blood cells to the implant surfaces is commonly tested to observe if the surface of implant can resist the formation of thrombus. As shown by Krajewski et al.,136 both albumin and heparin coatings on cardiac implants reduced blood cell adhesion compared to bare surfaces. Similar results were demonstrated in our study as the drug incorporated in matrix (CCDF) significantly reduces cell attachment, likely due to the anticoagulant drug incorporated into it. Tang et al.137 reported that cardiac implants tend to adhere more platelets on their surface if these are not coated with any polymeric or drug substance which leads to early thrombus formation at site. In another study, Busch et al.138 studied various cardiac implants which had coatings of different polymers including PLLA, P(3HB), P(4HB), and a blend of PLLA and P(4HB) and compared their results with each other. The results showed that while PLLA and P(4HB) individually induced thrombosis, their combined formulation exhibited an antiplatelet adhesion effect. This aligns with the results of our observation as combining an anticoagulant drug with a polymer reduces platelet adhesion, ultimately mitigating thrombus formation.
While GC-MS analysis was able to identify the anticoagulant constituents within the prospective drug, quantification of these anticoagulants was not possible due to lack of specific instrumentation. Thus, future research will be focused on quantification of these constitutes using GC-MS and HPLC. Lastly, this research served as a preliminary investigation which used thin films for initial assessments. In future, more studies will be done to fully evaluate the suitability of the material for real-world biomedical implant applications.
Footnote |
† Electronic supplementary information (ESI) available. See DOI: https://doi.org/10.1039/d4ra00796d |
This journal is © The Royal Society of Chemistry 2024 |