Synthesis and photophysical properties of hyperbranched polyfluorenes containing 2,4,6-tris(thiophen-2-yl)-1,3,5-triazine as the core

Abstract

A series of new hyperbranched polymers containing a 2,4,6-tris(thiophen-2-yl)-1,3,5-triazine core unit and polyfluorene chain arms have been synthesized via Suzuki coupling, and characterized by NMR, IR and GPC. All the polymers exhibit good thermal stability with a high decomposition temperature. By changing the 2,4,6-tris(thiophen-2-yl)-1,3,5-triazine/fluorene ratio the UV-vis absorption and emission spectra can be partially tuned. It has been found that the polymers containing a low ratio of 2,4,6-tris(thiophen-2-yl)-1,3,5-triazine units (P1–P3) have an absorption maximum around 385 nm, localized in the polyfluorene chain, and a shoulder around 425 nm ascribable to a charge transfer state involving the fluorene and the 2,4,6-tris(thiophen-2-yl)-1,3,5-triazine core. Increasing the molar ratio of the 2,4,6-tris(thiophen-2-yl)-1,3,5-triazine unit enhances the charge transfer band which becomes dominant for P4. The LUMO level of these polymers is relatively low due to the electron affinity of the triazine group. The polymers show dual emission, with a structured band in the blue (410–440 nm), attributed to the polyfluorene, and a broad band in the red (470–500 nm) associated with the charge transfer state. All the polymers exhibit two-photon absorption activity in the range of 660 to 900 nm with the maximum two-photon absorption (TPA) cross-section red-shifted from the corresponding linear absorption. The values of the TPA cross-sections vary from 1000 to 5000 GM, following the 2,4,6-tris(thiophen-2-yl)-1,3,5-triazine/fluorene ratio.