Promoting water photooxidation on transparent WO3 thin films using an alumina overlayer

Abstract

Tungsten trioxide (WO₃) is being investigated as one of the most promising materials for water oxidation using solar light. Its inherent surface-related drawbacks (e.g., fast charge recombination caused by surface defect sites, the formation of surface peroxo-species, etc.) are nowadays being progressively overcome by different methods, such as surface passivation and the deposition of co-catalysts. Among them, the role of surface passivation is still poorly understood. Herein, transparent WO₃ (electrodeposited) and Al₂O₃/WO₃ (prepared by atomic layer deposition, ALD) thin film electrodes were employed to investigate the role of an alumina overlayer by using both photoelectrochemical and laser flash photolysis measurements. Films with a 5 nm-alumina overlayer (30 ALD cycles) showed an optimum photoelectrochemical performance, portraying a 3-fold photocurrent and Faradaic efficiency enhancement under voltage biases. Moreover, IPCE measurements revealed that alumina effect was only significant with an applied potential ca. 1 V (vs. Ag/AgCl), matching the thermodynamic potential for water oxidation at pH 1 (0.97 V vs. Ag/AgCl). According to the investigation of electron accumulation through optical absorption measurements, the alumina overlayer dominantly decreased the number of electron trapping sites on the WO₃ surface, eventually facilitating photoelectron transfer to the external circuit in the presence of a positive bias. In addition, the laser flash photolysis measurements of WO₃ and Al₂O₃/WO₃ thin films clearly showed that the electron trapping decreased in the presence of the alumina overlayer whereas the hole trapping relatively increased with alumina, facilitating water photooxidation and rendering a more sluggish recombination process. These results provide a physical insight into the passivation process that could be used as a guideline for further development of efficient photoanodes in artificial photosynthesis.