Liquid oxygen compatible epoxy resin: modification and characterization

Abstract

The bisphenol A epoxy resin was modified by the polycondensation between tetrabromobisphenol A and bisphenol A epoxy resin. After curing using 4,4′-diaminodiphenyl methane (DDM) and 4,4′-diaminodiphenyl sulfone (DDS), the liquid oxygen compatibility of bisphenol A epoxy resin and modified bisphenol A epoxy resin was measured by the mechanical impact test (ASTM D2512-95). The results suggested that the modified bisphenol A epoxy resin curing using 4,4′-diamino diphenylmethane (DDM) was compatible with liquid oxygen. The thermogravimetric analysis (TGA) revealed that the modified bisphenol A epoxy resin has lower temperatures of the initial degradation and the maximum mass loss rate compared with unmodified. The X-ray photoelectron spectroscopy (XPS) measurement results indicated that the C–C/H groups were oxidized to C–O–C/H and/or C[double bond, length as m-dash]O groups during the impact process. The mechanical properties of all samples were measured at room temperature (RT) and nitrogen temperature (77 K). The flame-retardant modification of epoxy resin may be an effective way to obtain the compatible epoxy resin material with liquid oxygen.

Graphical abstract: Liquid oxygen compatible epoxy resin: modification and characterization

Article information

Article type
Paper
Submitted
08 Nov 2014
Accepted
09 Jan 2015
First published
09 Jan 2015

RSC Adv., 2015,5, 11325-11333

Author version available

Liquid oxygen compatible epoxy resin: modification and characterization

Z. Wu, S. Li, M. Liu, Z. Wang and X. Liu, RSC Adv., 2015, 5, 11325 DOI: 10.1039/C4RA14100H

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements