Enhanced cycle life and capacity retention of iron oxide ultrathin film coated SnO2 nanoparticles at high current densities

Abstract

Tin oxide (SnO2) has a high theoretical capacity (∼782 mA h g−1), but it experiences large volume changes during charge and discharge cycles that cause rapid capacity fade, which limits its practical use as an anode material. In an attempt to solve this, we coated these particles with ultrathin electrochemically active iron oxide (FeOx) films that act as an artificial solid electrolyte interphase layer, thus stabilizing the SnO2 particles for better longevity of significantly improved performance at high current densities in a practical voltage window. Since there exists a tradeoff between species transport and protection of particles (expecting long life), a film with an optimum thickness was achieved by atomic layer deposition (ALD) of FeOx on SnO2 particles. With an optimum thickness of about 0.24 nm after 20 cycles of iron oxide ALD (20Fe), an initial capacity of ∼658 mA h g−1 was achieved at a high current density of 1250 mA g−1. After 1000 cycles of charge/discharge at 1250 mA g−1, the 20Fe sample showed a capacity retention of 94% as compared to 52% of the uncoated sample when cycled at room temperature; at 55 °C, the capacity retention of the 20Fe sample was 93% compared to 33% of the uncoated sample.

Graphical abstract: Enhanced cycle life and capacity retention of iron oxide ultrathin film coated SnO2 nanoparticles at high current densities

Supplementary files

Article information

Article type
Paper
Submitted
03 Jan 2016
Accepted
26 Feb 2016
First published
26 Feb 2016

RSC Adv., 2016,6, 24340-24348

Enhanced cycle life and capacity retention of iron oxide ultrathin film coated SnO2 nanoparticles at high current densities

S. A. Palaparty, R. L. Patel and X. Liang, RSC Adv., 2016, 6, 24340 DOI: 10.1039/C6RA00083E

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements