Borohydride stabilized gold–silver bimetallic nanocatalysts for highly efficient 4-nitrophenol reduction

Nathaniel E. Larm , Jason A. Thon , Yahor Vazmitsel , Jerry L. Atwood and Gary A. Baker *
Department of Chemistry, University of Missouri, Columbia, MO 65211, USA. E-mail: bakergar@missouri.edu

Received 15th August 2019 , Accepted 17th October 2019

First published on 30th October 2019


Abstract

Bimetallic AuxAg1−x nanoparticles, prepared using sodium borohydride as the sole reducing and capping agent for various NaBH4[thin space (1/6-em)]:[thin space (1/6-em)]metal molar ratios, were investigated as catalysts for 4-nitrophenol reduction. This approach yielded the highest catalytic activities observed for this model reaction to date.


Noble metal nanoparticles (NPs) are promising catalysts for a variety of organic reactions such as 4-nitroarene reduction using sodium borohydride,1–5 aerobic oxidation of alkyl benzenes to benzaldehydes,6–8 and alkylation of primary amines to secondary amines in the presence of an alcohol.9–11 It is well known that the catalytic potential of noble metal NPs relies heavily on their size, shape, crystallinity, dispersity, and surface chemistry.9,12 In this regard, strong stabilizing ligands typically hinder catalytic activity by creating a diffusion barrier between reactants and the NP surface, with tightly-bound surfactants leading to slower transport of reactants and poor catalytic activity.13 This flaw was turned into a feature by Astruc and co-workers in 2014 when they reported the synthesis of gold nanoparticles (AuNPs) stabilized by NaBH4 for the catalytic reduction of 4-nitrophenol (4-NP) to 4-aminophenol (4-AP) in the presence of NaBH4,14 providing an intriguing circumstance where BH4 participated in the catalytic system as both the catalyst surfactant and as one of the reactants. Their catalyst preparation used clever manipulation of the concentration of NaBH4, a common reducing agent15 but seldom-utilized stabilizing ligand, to produce AuNPs possessing the highest activity for this reaction yet reported.

Bimetallic NPs provide an interesting opportunity to expand the current catalog of nanocatalysts. In particular, bimetallic gold/silver nanoparticles (AuAgNPs) provide an inexpensive alternative to monometallic AuNP catalysts while generally possessing higher catalytic activity for the reduction of nitroarenes.16–22 Herein, we investigate a slightly modified Astruc method for the synthesis of monometallic AuNPs and AgNPs as well as bimetallic AuxAg1−xNPs (where x ranges from 0.9 to 0.1 in 0.1 increments) using NaBH4 as the sole reducing/stabilizing agent. Three distinct molar ratios of reducing agent to metal (denoted herein as R values; specifically, R = 2, 5, and 10) were used to create sets of monometallic/bimetallic NP solutions as shown in Tables S1–S3. These colloidal NP solutions were then used as catalysts in the reduction of 4-NP to 4-AP in the presence of excess NaBH4, which resulted in the highest observed catalytic activity for this reaction when using noble metal NPs in water at room temperature.

The AuxAg1−xNP colloids were initially screened using UV-vis spectrophotometry (Fig. 1 and S1–S11), monitoring for changes in their localized surface plasmon resonance (LSPR) bands over time as an indication of colloid evolution and stability.


image file: c9na00645a-f1.tif
Fig. 1 UV-vis spectra of borohydride-capped AuxAg1−xNPs alongside images of the samples aged for 5 d. The R values provided in the left panels denote the number of equivalents of NaBH4 per metal atom employed in the synthesis. Colloidal instability in the form of black precipitates affiliated with sample decolouration is observed for very low x values (high silver content) in the R = 5 (x = 0.0) and R = 10 (x ≤ 0.4) sample sets.

The LSPR bands of the as-synthesized monometallic solutions indicate the formation of very small AuNPs (LSPRmax of ∼510 nm) and somewhat larger AgNPs (LSPRmax of ∼410 nm) in the x = 1.0 and 0.0 solutions, respectively, while the bimetallic solutions possess intermediate LSPR bands. Within 5 d of synthesis, aggregation in the form of a black precipitate was observed in the R = 5 AgNPs as well as all samples containing more than 50 mol% Ag (x < 0.5) from the R = 10 sample set. After aging for 20 d, the AgNP solutions from the R = 2, 5, and 10 sample sets, bimetallic Au0.1Ag0.9NPs from the R = 5 sample set, and bimetallic AuxAg1−xNPs (for x = 0.1, 0.2, 0.3, 0.4) from the R = 10 sample set also possessed such aggregates. This aggregation is attributed to a decrease in surface potential imparted by electron injection into the NP by BH4, resulting in destabilization of the colloidal dispersion.3 All other samples showed colloidal stability throughout 30 d, with some broadening and red-shifting of the LSPR band evident in some cases. Bubbles were also observed in these aged solutions, indicative of H2 gas production from the hydrolysis of the borohydride to borohydroxides of the form [BHy(OH)4−y].

A comparison of the UV-vis spectrum of an equivolume mixture of AuNPs and AgNPs with that of our bimetallic Au0.5Ag0.5NPs is shown in Fig. S12. The latter sample exhibits peak broadening and a decrease in peak intensity when compared to the spectra from the monometallic samples, consistent with the formation of intermetallic particles. Further, energy-dispersive X-ray spectroscopy (EDS) spot analysis was used to interrogate the atomic composition of our bimetallic R = 5 Au0.5Ag0.5NPs. The proportions of Au and Ag were determined to be 36.7 and 63.3 atom%, respectively, as calculated from the EDS spectrum (Fig. S13). We attribute the discrepancy between the as-prepared (50[thin space (1/6-em)]:[thin space (1/6-em)]50) and as-measured (37[thin space (1/6-em)]:[thin space (1/6-em)]63) atomic ratios to low X-ray counts and the high relative error of the EDS measurement (∼30%), a consequence of the small NP size. We propose that these bimetallic NPs comprise a pseudo-random composition that is primarily governed by the relative concentrations of available metal atoms in solution, although the small NP sizes thwarted our attempts to elucidate the exact atomic composition via EDS mapping.

Transmission electron microscopy (TEM) images were acquired for the following AuxAg1−xNPs samples after aging for 5 d: R = 2 for x = 0.6, 0.3, 0.0 (Fig. 2); R = 5 for x = 1.0, 0.3 (Fig. S14); and R = 10 for x = 0.7, 0.5 (Fig. S15). These representative images and respective histograms indicate narrow size distributions and mostly sub-10 nm particle sizes for all but the R = 2 AgNPs, an anomaly which we are tentatively attributing to the instability of borohydride-capped AgNPs, as the solutions of AgNPs when R = 5 or 10 contained black precipitate at this time point. Further, the TEM images suggest the formation of metal networks either in solution or upon drying on the grid, making NP size assessment difficult (at least 300 NP were counted, with some level of inaccuracy as the branching metal networks were ignored). Notably, these networks were also observed by Astruc et al.14 The smallest observed NPs were associated with the R = 2 Au0.3Ag0.7NP solution, with an average particle size of 4.6 ± 2.4 nm.


image file: c9na00645a-f2.tif
Fig. 2 TEM images and related size histograms for borohydride-capped AuxAg1−xNPs for (A and B) x = 0.6; (C and D) x = 0.3; and (E and F) x = 0.0 (i.e., AgNPs). The borohydride-to-metal molar ratio (R value) is 2 for these samples.

The catalytic activity of 5 d-old AuxAg1−xNPs was measured through the model reduction of 4-nitrophenol (4-NP) to 4-aminophenol (4-AP) in the presence of a large excess (>200-fold) of sodium borohydride (NaBH4), with experimental details provided in the ESI. Briefly, 2.1 mL of aqueous 0.2 mM 4-NP and 0.9 mL of aqueous 0.1 M NaBH4 was added to a poly(methyl methacrylate) (PMMA) cuvette, resulting in a yellow solution of 4-nitrophenolate (λmax = 400 nm). To this solution, 34 μL of aqueous 0.25 mM metal catalyst solution (that is, [Au] + [Ag] = 0.25 mM) was added (a catalyst loading of 2.0 mol% metal to 4-NP was kept constant throughout), and the cuvette was capped, inverted to mix, and placed in the UV-vis spectrometer to begin measuring solution absorbance at 400 nm, similar to techniques used in previous publications.23 It should be noted that samples containing black precipitate were not assessed for catalytic performance due to inaccuracies in calculating the remaining metal concentration. In the presence of excess NaBH4, the reaction proceeds via pseudo-first-order kinetics and a linear relationship between ln(A0/At) versus time is observed, the slope of which equals the catalytic rate (kapp). These plots and the resulting kapp values are summarized in Fig. 3.


image file: c9na00645a-f3.tif
Fig. 3 Plots depicting the pseudo-first-order kinetics of 4-NP reduction and associated catalytic rates (kapp) using 5 d-old borohydride-stabilized AuxAg1−xNP nanocatalysts (R = 2, 5, and 10, top to bottom). Excluded x values for a particular R value indicate the observation of appreciable colloidal precipitation after aging for 5 d.

While it is common during 4-NP reduction to observe an initial induction period wherein dissolved oxygen back-reacts with 4-AP,24 such a delay is only observed during the slower reactions when using AuNPs and AgNPs. We propose that the faster kinetics imparted by our bimetallic NPs greatly shorten this induction period, limiting it to the time required to invert our cuvette for mixing. The reactions were considered complete when the decrease in absorbance at 400 nm slowed substantially (corresponding to a ln(A0/At) value of 3, equivalent to 95% reaction completion), and were terminated after 5 min had passed. Generally, bimetallic AuxAg1−xNPs with medium-to-high silver contents (i.e., x ≤ 0.7) demonstrated higher catalytic rates within a given R value sample set.

Turnover frequency (TOF) should be preferred over kapp when reporting comparative catalytic activity of NPs due to the former's incorporation of the molar ratio of catalyst to substrate. More specifically, this value is calculated by dividing the moles of substrate (in this case, n4–NP) by the product of moles of catalyst (nm) and the reaction time (trxn) in hours, then correcting for reaction completion, as per eqn (1).

 
image file: c9na00645a-t1.tif(1)

Herein, we used 2.0 mol% metal to 4-NP and define the reaction time as the time to attain ln(A0/At) = 3 (95% reaction completion). This reaction completion % has the benefit of incorporating most of the reaction progress while simultaneously negating instrument sensitivity concerns arising when the residual 4-nitrophenolate concentration becomes very small. Under these parameters, Au0.3Ag0.7NPs from the R = 2 sample set demonstrated the highest catalytic activity, with a calculated TOF of 12[thin space (1/6-em)]160 h−1 (Fig. 4A and Table S4). Notably, several of our bimetallic NPs at each R value outperformed the record previously claimed for this reaction using a AuNP catalyst (TOF = 9000 h−1),14 despite our use of more stringent reaction completion conditions (e.g., the above reference reported a completion time corresponding to a ln(A0/At) = 2, or 86% completion, and did not correct for this in their calculation of TOF). To the best of our knowledge, these AuxAg1−xNPs possess the highest catalytic activities for this specific catalytic reaction yet reported. The proposed reason for such a pronounced increase in TOF when using bimetallic NPs is two-fold: first, a size regulating effect is evident for solutions of mixed metals, resulting in populations of smaller NPs and a potential increase in the number of surface atoms available for catalysis. Second, the presence of guest metals within an ordered crystalline structure results in disharmonious, defect-laden surfaces, increasing the number of active sites for catalytic activity and surface rearrangement of stabilizing ligands. Further study is required to fully understand and quantify the amount of catalytic enhancement imparted, in general, when incorporating bimetallic systems.


image file: c9na00645a-f4.tif
Fig. 4 (A) Turnover frequency (TOF) and (B) TOF per U.S. dollar (USD), expressed as functions of the overall nanoparticle composition, for borohydride-stabilized AuxAg1−xNPs applied as nanocatalysts for 4-NP reduction. Panel (B) illustrates the economic viability of replacing Au with Ag in this catalytic system by way of a monotonic increase in the TOF per USD. Economic performance is based on current representative vendor prices for the metal precursors used (see ESI).

A recyclability assessment was performed using Au0.3Ag0.7NPs for R = 2 (Table S5 and Fig. S16). The initial catalytic cycle was performed as specified above, and, once the reaction was complete, the cuvette was spiked with 84 μL of 5.0 mM 4-NP and 90 μL of 0.1 M NaBH4 to restart the reaction. This recycling procedure was performed five sequential times using the same cuvette and catalytic solution. Unfortunately, we find that the TOF experiences an exponential decay in each sequential cycle, dropping from an initial value of 12[thin space (1/6-em)]260 h−1 to 1570 h−1 after six cycles. This is, however, not surprising as the high surface energy of nanoscale colloids invariably results in instability, aggregation, and eventual loss of catalytic activity. Indeed, in practice nanocatalysts are typically protected against colloidal aggregation and oxidation by coating with a suitable polymer (e.g., poly(N-vinyl-2-pyrrolidone) PVP), deposition on a solid inorganic support, or encapsulation within a porous scaffold to yield superior stability, durability, and recoverability relative to the free nanocatalyst.25–27 Nonetheless, the final TOF observed after six catalytic cycles for our unsupported catalysts remains high compared to typical nitroarene reduction nanocatalysts reported in the literature.14

As a metric to compare the price and activity of our bimetallic NPs, we prepared a plot of TOF per USD (h−1 $−1) versus the x value for AuxAg1−xNPs (Fig. 4B). Our aim is to show that not only are these bimetallic NPs the best catalysts for this system yet reported, but they are much more cost effective than the pure, monometallic AuNPs typically utilized. Indeed, higher Ag concentrations (lower x values) yielded higher activities per $; especially noteworthy is the very high activity coupled with reduced cost for the Au0.1Ag0.9NP sets.

In summary, we report a method for synthesizing bimetallic AuxAg1−xNPs capped with NaBH4 which possess higher catalytic activity for the reduction of 4-NP to 4-AP than their corresponding monometallic counterparts when utilizing the same total amount of metal. Displaying TOF values up to 12[thin space (1/6-em)]160 h−1, to the best of our knowledge, these nanoparticles offer the fastest nanocatalytic rates yet observed for nitroarene reduction in water under ambient conditions. Finally, this research suggests wider consideration for the financial and functional benefits of employing silver as a substitute for (or complement to) gold within nanocatalytic systems.

Conflicts of interest

There are no conflicts to declare.

Notes and references

  1. S. Zhao, A. Das, H. Zhang, R. Jin, Y. Song and R. Jin, Pro. Nat. Sci.-Mater., 2016, 26, 483–486 CrossRef CAS.
  2. G. Li and R. Jin, Acc. Chem. Res., 2013, 46, 1749–1758 CrossRef CAS PubMed.
  3. R. Ciganda, N. Li, C. Deraedt, S. Gatard, P. Zhao, L. Salmon, R. Hernández, J. Ruiz and D. Astruc, Chem. Commun., 2014, 50, 10126–10129 RSC.
  4. Y. S. Seo, E.-Y. Ahn, J. Park, T. Y. Kim, J. E. Hong, K. Kim, Y. Park and Y. Park, Nanoscale Res. Lett., 2017, 12, 7 CrossRef PubMed.
  5. T. Aditya, A. Pal and T. Pal, Chem. Commun., 2015, 51, 9410–9431 RSC.
  6. A. V. Biradar and T. Asefa, Appl. Catal., A, 2012, 435–436, 19–26 CrossRef CAS.
  7. A. S. K. Hashmi and G. J. Hutchings, Angew. Chem., Int. Ed., 2006, 45, 7896–7936 CrossRef PubMed.
  8. B. Guan, D. Xing, G. Cai, X. Wan, N. Yu, Z. Fang, L. Yang and Z. Shi, J. Am. Chem. Soc., 2005, 127, 18004–18005 CrossRef CAS PubMed.
  9. H. Lin, L. Xia-Bing, N. Ji, L. Yong-Mei, C. Yong, H. He-Yong and F. Kang-Nian, Chem.–Eur. J., 2010, 16, 13965–13969 CrossRef PubMed.
  10. O. Saidi, A. J. Blacker, G. W. Lamb, S. P. Marsden, J. E. Taylor and J. M. J. Williams, Org. Process Res. Dev., 2010, 14, 1046–1049 CrossRef CAS.
  11. K. Shimizu, M. Nishimura and A. Satsuma, ChemCatChem, 2009, 1, 497–503 CrossRef CAS.
  12. J. T. L. Gamler, H. M. Ashberry, S. E. Skrabalak and K. M. Koczkur, Adv. Mater., 2018, 30, 1801563 CrossRef PubMed.
  13. S. Campisi, M. Schiavoni, C. Chan-Thaw and A. Villa, Catalysts, 2016, 6, 185 CrossRef.
  14. C. Deraedt, L. Salmon, S. Gatard, R. Ciganda, R. Hernandez, J. Ruiz and D. Astruc, Chem. Commun., 2014, 50, 14194–14196 RSC.
  15. M. Dasog, W. Hou and R. W. J. Scott, Chem. Commun., 2011, 47, 8569–8571 RSC.
  16. R. Ferrando, J. Jellinek and R. L. Johnston, Chem. Rev., 2008, 108, 845–910 CrossRef CAS PubMed.
  17. S. Ravula, J. B. Essner, W. A. La, L. Polo-Parada, R. Kargupta, G. J. Hull, S. Sengupta and G. A. Baker, Nanoscale, 2015, 7, 86–91 RSC.
  18. E. W. Harak, K. M. Koczkur, D. W. Harak, P. Patton and S. E. Skrabalak, ChemNanoMat, 2017, 3, 815–821 CrossRef CAS.
  19. S. E. Skrabalak, J. Chen, S. Neretina and D. Qin, Part. Part. Syst. Charact., 2018, 35, 1800111 CrossRef.
  20. J. B. Essner, C. H. Laber and G. A. Baker, J. Mater. Chem. A, 2015, 3, 16354–16360 RSC.
  21. X. Wang, S. Chen, G. Reggiano, S. Thota, Y. Wang, P. Kerns, S. L. Suib and J. Zhao, Chem. Commun., 2019, 55, 1249–1252 RSC.
  22. N. E. Larm, D. Madugula, M. W. Lee and G. A. Baker, Chem. Commun., 2019, 55, 7990–7993 RSC.
  23. N. E. Larm, J. B. Essner, K. Pokpas, J. A. Canon, N. Jahed, E. I. Iwuoha and G. A. Baker, J. Phys. Chem. C, 2018, 122, 5105–5118 CrossRef CAS.
  24. E. Menumerov, R. A. Hughes and S. Neretina, Nano Lett., 2016, 16, 7791–7797 CrossRef CAS PubMed.
  25. K. Zhang, J. M. Suh, J.-W. Choi, H. W. Jang, M. Shokouhimehr and R. S. Varma, ACS Omega, 2019, 4, 483–495 CrossRef CAS PubMed.
  26. H. Hu, J. H. Xin, H. Hu, X. Wang, D. Miao and Y. Liu, J. Mater. Chem. A, 2015, 3, 11157–11182 RSC.
  27. D. Wang and D. Astruc, Chem. Soc. Rev., 2017, 46, 816–854 RSC.

Footnotes

Electronic supplementary information (ESI) available: Experimental details, images of samples, additional spectra, and TEM images. See DOI: 10.1039/c9na00645a
These authors contributed equally to this work.

This journal is © The Royal Society of Chemistry 2019
Click here to see how this site uses Cookies. View our privacy policy here.