Xiansong
Shi
,
Dongwei
Ma
,
Fang
Xu
,
Zhe
Zhang
and
Yong
Wang
*
State Key Laboratory of Materials-Oriented Chemical Engineering, College of Chemical Engineering, Nanjing Tech University, Nanjing 211816, P. R. China. E-mail: yongwang@njtech.edu.cn
First published on 4th December 2019
Two-dimensional covalent organic frameworks (COFs) are gaining tremendous interest for their potential applications in a diversity of fields. However, synthesis of COF nanosheets (CONs) usually suffers from tedious exfoliation processes and low yields. Herein, we present an exfoliation-free and scalable strategy to prepare few-layered CONs based on interface-confined synthesis, in which cheap and recyclable table salt (NaCl) is used as the sacrificial substrate. Salt particles are introduced into the reaction system, creating billions of solid–liquid interfaces. Oligomers formed upon the reaction between monomers are immediately adsorbed on salt surfaces, and the following polymerization leading to crystalline CONs is exclusively confined to salt surfaces. Salts can be easily removed by water washing, producing CONs with the thickness down to a few nanometers and lateral sizes up to hundreds of micrometers depending on the size of salt particles and the concentration of monomers. Four different kinds of CONs, both imine-linked and boron-containing, are synthesized from this generic method. As a demonstration, we prepare highly permeable and selective membranes using resultant CONs as building blocks. Thanks to the defect-free stacking of CONs with thin thicknesses and large lateral sizes on porous substrates, the membranes precisely separate similarly sized dyes while allowing ultrafast water permeation. This interface-confined strategy opens a new platform for the controllable and scalable synthesis of COF nanosheets and is essential for the burgeoning real-world applications of COFs in various fields.
To take full advantage of the nanoporosity and two-dimensional (2D) structure of COFs, it is often required to use them in the form of thin COF nanosheets (CONs).11,17,18 CONs with a few nanometers in thickness not only offer more active sites, but also improve mass transfer efficiency. These features significantly promote the performances of the devices assembled from CONs for applications such as sensing,19,20 ion conductivity,11 and separation.15,21 Unfortunately, turning these polymeric crystalline networks into thin nanosheets with a high yield remains a great challenge due to the strong π–π stacking interaction between adjacent COF monolayers. Extensive efforts have been devoted to synthesize CONs, and two main strategies, namely “top-down” and “bottom-up”, have been developed for this purpose. The “top-down” strategy is usually conducted by exfoliating 2D layered COF particulates with the assistance of ultrasound,22 solvent molecules,23 or mechanical grinding.24 However, this strategy is frequently limited by the entangled drawbacks of tedious exfoliation processes, low yields (<15%), and inhomogeneity in the size and thickness of the produced CONs. Importantly, Banerjee and coworkers developed new exfoliation methods, including chemically delamination by post modification25 and self-exfoliation on guanidinium-based ionic COFs,17 to produce high-quality CONs. Unfortunately, these approaches are only applicable to limited types of specially designed COFs. In contrast, the “bottom-up” synthesis is able to directly synthesize CONs with thicknesses down to the monolayer level. This strategy is usually realized with the assistance of interfaces which play an essential role in guiding the growth orientation of COFs. For instance, Wang and coworkers synthesized highly ordered COF monolayers on the surface of pyrolytic graphite by creating a solid–vapor interface.26 Alternatively, by using solid–liquid interfaces, Dichtel et al. prepared thin COF films on single-layer graphene and Au electrodes.27,28 Bein et al. synthesized 2D COF films with tailored thicknesses on glass substrates via vapor-assisted conversion.29 However, these “bottom-up” methods require the use of costly substrates and face the challenge of removing CONs from the substrates. Moreover, they are also suffering from issues including very low yields and poor scalability. Therefore, a cost-effective and scalable approach for the controllable synthesis of CONs is urgently needed and remains a great challenge.
There have been a large number of reports on the preparation of COF coatings on solid substrates with various materials and structures by solvothermal synthesis.30–33 In these studies, COFs are formed both on the substrate surfaces as coating layers and in the bulk solutions as free particulates. Regrettably, in these uncontrolled syntheses of COFs, the majority of the COF monomers (typically >80%) are consumed by the reaction taking place in the bulk solution, resulting in undesired side products, free COF particulates. Even worse, the particulates may precipitate from the solution and contaminate the COF layers coated on the substrates. That is, under an “ideal” reaction condition where the reaction is exclusively confined to the substrate surfaces, all monomers will convert into COF nanosheets adhered to the substrate surfaces, leaving behind no particulates in the bulk solution. To this end, a strong interfacial confinement effect should be introduced in the reaction system. Interfaces are required here to guide the growth of COFs in one direction to generate 2D nanosheets or thin films. Moreover, the interfaces need to be present in the reaction with the confinement to suppress the growth of COFs in the bulk solution, thus avoiding the formation of free COF particulates. Hence, it is highly possible to convert all monomers into CONs if we can build sufficient confined interfaces during solvothermal synthesis. Herein, we report the scalable synthesis of various imine-linked and boron-based CONs through interface-confined solvothermal synthesis. By introducing a large number of salt particles in the reaction system, the growth of COFs is completely restricted on salt surfaces, producing well-defined CONs without the interference of any bulk particulates. Importantly, the CONs can be easily released from salts by water washing, implying their high efficiency and feasibility of mass production. The size and thickness of CONs can be regulated by changing salt sizes and monomer concentrations. Further, we use the thus-obtained imine-linked CONs as building blocks to prepare membranes by depositing them on porous substrates. The membranes exhibit remarkably high water permeances and tight selectivity, enabling fast separation of dyes with similar sizes.
The Fourier transform infrared (FTIR) spectra of the released CONs clearly indicate the formation of imine-linked frameworks. The TpPa and TpBD CONs show characteristic stretching bands at ∼1575 cm−1 (–CC) and ∼1257 cm−1 (–C–N) (Fig. S6†). The disappearance of CN stretching indicates that the tautomerization occurs in the synthesized CONs (Fig. S7†), implying that they hold a keto form.35 The featured peak at ∼1618 cm−1 for TbPa CONs also indicates the formation of imine bonds (Fig. S8†).36 The disappearance of characteristic peaks originated from monomer pairs also implies the complete consumption of monomers after CON synthesis using this approach. Here, the peaks in FTIR spectra match well with the featured peaks of the corresponding COFs and do not show other redundant stretching bands, demonstrating that there is no side products left after removing salts by water washing. Powder X-ray diffraction (XRD) was then applied to ascertain the ordered structure of the COF particulates synthesized without salts and the released CONs. As shown in Fig. 2, column (i), both the COF particulates and CONs show clear peaks at lower 2θ values, for instance, TpPa (∼4.7°), TpBD (∼3.4°), and TbPa (∼4.6°), which correspond to the reflections from the (100) plane. The XRD results clearly indicate that the thus-prepared CONs maintain their good crystallinity. Furthermore, the broad peak at a higher 2θ value about ∼26–27° originates from the (001) plane reflection, indicating the π–π stacking between successive COF monolayers. Comparing the XRD results of particulates and CONs, a slight decrease in the intensity arising from the (100) plane reflection can be observed. This reduction could be caused by the random stacking of 2D COF sheets which contribute to the homogeneity of COF pores.24 Besides, the (001) plane reflection of CONs is broadened or diminished compared with the COF particulates. The weakened peak here is believed to be due to the remarkable reduction in the number of the stacked layers in these CONs.24 Importantly, compared with the XRD results of sNaCl@TpPa, we do not observe any peaks originated from the (200) plane of NaCl crystals (Fig. S9†), indicating that NaCl was completely removed after water washing. Given that the CONs are soaked in water for long duration to remove salts, the desired crystallinity exhibited by the resultant sheets demonstrates their excellent stability in water. Thermogravimetric analysis (TGA) was performed for TpPa CONs to obtain information about the thermal stability (Fig. S10†). The weight loss within 100 °C should be ascribed to the evaporation of water absorbed in the CON pores. The CONs show thermal stability up to 300 °C, and the gradual weight loss of nearly 100% is observed until 600 °C, corresponding to the complete decomposition of the nanosheets. Fig. 2, column (ii) shows the SEM images of CONs released from sNaCl crystals. These CONs show flat-sheet-like morphologies with lengths and widths of several micrometers. For instance, the average sheet sizes in width for TpPa, TpBD, and TbPa CONs deposited on anodic aluminum oxide (AAO) supports are 4.2, 1.0, and 2.9 μm, respectively (Fig. S11†). AFM characterization reveals that these imine-linked CONs present laminar structures with thicknesses ranging from ∼3–5 nm (Fig. 2, column (iii)), corresponding to only ∼10–15 COF monolayers (Fig. S12†).37,38 Notably, TEM imaging clearly shows the staggered structure of the COF layers, which corresponds to the terrace structure observed from AFM images (Fig. S13†). Hence, we believe that, in the presence of a large amount of salt particles, CONs are formed by layer-by-layer growth between monomer pairs, thus producing layer-stacked frameworks. As shown above, this method is applicable to the synthesis of different imine-linked CONs, and the synthesized few-layered sheets can be stably dispersed in ethanol (Fig. S14†). We then expanded this approach to synthesize other types of COFs to further demonstrate the universality of our method. For instance, the nanosheets of boron-based COF-1 were synthesized on sNaCl crystals. It can be clearly observed that COF-1 nanosheets with an average lateral size of about 0.5 μm are obtained after removing the salt crystals (Fig. S15†).
To reveal the formation mechanism of CONs on salts, we investigated the structural features of CONs grown on NaCl particles with different sizes. In addition to sNaCl particles with an average particle size of ∼12 μm discussed above, big NaCl (bNaCl) particles with an average size of ∼440 μm and a NaCl plate (2 cm × 2 cm × 0.3 cm) were also used as substrates to grow CONs by this approach (Fig. S16†). In the case of bNaCl particles, the prepared TpPa and TpBD CONs present lateral sizes of approximately 11 and 1.5 μm (Fig. S17 and S18†), respectively, which are much larger than those of CONs formed on sNaCl. Besides, the TpBD CON shows a thickness of about 12 nm (Fig. S19†), which is ∼3 times higher than that of CONs synthesized on sNaCl particles. Also, the growth of COFs exclusively occurred on the surface of these bNaCl particles and no free COF particulates were formed in the bulk solution. Based on the above observations, we propose an interface-confined growth mechanism to elucidate the synthesis of CONs along the salt surfaces (Fig. 3a). Upon the contact between amine and aldehyde molecules, the coupling of reactive groups separately carried by two monomers leads to the formation of oligomers in the solution. Since NaCl particles possess a relatively high surface energy, the oligomers prefer to adsorb onto salt surfaces and nucleation takes place, demonstrated by the color change of NaCl particles after a synthesis time of only 5 min (Fig. S20†). Also importantly, the salt-solution (solid–liquid) interface reduces the thermodynamic barrier and accelerates the kinetic control nucleation on the salt surface rather than homogeneous nucleation in the free solution.39 The synergistic effect suppresses the growth of COFs in the free solution to form thermodynamically stable particulates, resulting in the complete condensation of monomers on the salt surface to generate sheet-like products. During the growth of CONs, the sufficient surface nucleation and adsorption of oligomers on salts lead to the merging of discrete nuclei with their neighbors to promote the lateral growth.
The subsequent reaction on the previously formed nuclei is responsible for the vertical growth in the thickness. Besides, the consumption of COF monomers limits the growth vertical to the salt surface, resulting in the formation of sheets with thin thicknesses. This nucleation-growth process of COF growth on solid–liquid interfaces can be confirmed by the distinction between the top and bottom morphologies, which are smooth and rough for the top and bottom, respectively (Fig. 3b). As the initial nucleation leads to an uneven growth of discrete nuclei, the CON side adhered to the salt surface features a rough texture. With further growth, the subsequently formed crystallites may repair this to produce a smooth surface. The lateral extension of sheets duplicates the texture of salt surfaces. To demonstrate this, we also prepared COFs on the NaCl plate with a rough surface (Fig. 3c). Obviously, a tortuous structure is obtained after removing the plate (Fig. 3d and S21†), implying the surface duplication during COF growth. Further, the extremely low dosage of monomer pairs compared to the salt particles leads to unsaturated growth of sheets, thus producing these sheets featuring a few nanometers in thickness (nanosheets). In the case of using bNaCl particles, as the used mass is the same as the sNaCl particles they provide greatly reduced surface areas for CON growth (Table S1†). Consequently, the unit area of the salt surface will share a higher monomer concentration, thus resulting in the formation of CONs with larger thicknesses. Notably, the nanosheets grown on both salt particles are not expected to cover the entire surface of the salt, leading to CONs with the lateral size much smaller than the particle size. By introducing a big 2 cm × 2 cm × 0.3 cm NaCl plate in the process, its surface is totally covered with continuous CONs (Fig. 3e) and a hollowed-out architecture built with these CONs is obtained after removing the plate (Fig. 3f). Notably, we find that there are many bulk COF particulates precipitated at the bottom of the autoclave after synthesis. These particulates are generated by the condensation of monomers in the free solution, implying the vital role of confined interfaces in synthesizing CONs on the substrate surfaces. The thickness of CONs formed on the salt plate is determined to be ∼120 nm (Fig. S22†). That is, a thick COF film rather than thin nanosheets is generated on the surface of the salt plate. This complete coverage of the salt plate, which cannot be observed in the case of salt particles as the substrates, is also related to the accessible surface area for CON growth. The salt plate provides a surface area of ∼10.4 cm2 for CON growth, which is only ∼0.02% of that of sNaCl particles (Table S1†). Interestingly, these continuous films can be transferred to other substrates to form composite structures (Fig. S23†). According to the proposed mechanism, increasing monomer concentration would also enhance the coverage of CONs on salt particles and produces CONs with larger lateral sizes. For example, when the monomer concentration was increased by 30 times, CONs with a greatly increased lateral size of approximately 100 μm are obtained (Fig. 3g). Following this method, high-quality CONs/films with well-controlled sizes and thicknesses can be obtained by tuning the monomer-to-area ratio. As only cheap, water-soluble, and recyclable salts are introduced into the solvothermal synthesis, our approach is much easier and more controllable compared to traditional methods including mechanical grinding and chemical exfoliation under harsh conditions (e.g., H2SO4/HNO3, acetonitrile, and alkaline media).40–42 More importantly, the mild synthesis strategy ensures the production of CONs with high crystallinity.
In the past decade, 2D materials possessing sheet-like structures in nanometer thicknesses, such as graphene oxide (GO) and derivatives,43,44 delaminated metal–organic frameworks (MOFs),45,46 and MXenes,47,48 have attracted increasing interest in membrane separation. Different from nonporous 2D materials such as GO and MXenes, CONs possess permanent and highly ordered pores with diameters of about 1–3 nm. These pores provide additional channels for molecule permeation aside from the spaces between stacked layers if CONs are assembled to use as separation membranes (Scheme S3†).49 This benefit will accordingly enhance the permeance of the CON-based membranes while maintaining tight selectivities. Considering that the facile production of CONs with the assistance of salt substrates is realized in the present work without any tedious delamination, we sought to use these CONs as building blocks to fabricate membranes for molecular separations. TpPa and TpBD CONs, which are highly water stable in nature,35 had the lateral size of a few micrometers after being released from sNaCl and were used as building blocks to produce membranes. A home-made vacuum filtration device (Fig. 4a and S24†) was used to assemble these 2D CONs onto porous AAO substrates. The thus-deposited CON layer possessed a stacked structure of nanosheets (Fig. 4b). As shown in Fig. 4c, the physical appearance change after CON deposition, indicating the successful deposition of CON layers, and the prepared membranes are almost optically transparent, implying the thin thickness of the deposited CON layer. Distinctly different from the AAO substrates having ∼20 nm pores (Fig. 4d), the TpPa and TpBD CONs achieve a complete and relatively smooth coverage on the substrate without any visible defects (Fig. 4e and f). We can observe some sharp edges in the SEM image (boxed area in Fig. 4e, f, and S25†) because of the sheet-like structure of CONs. The cross-sectional morphology of the membrane displays a thin CON layer tightly adhered to the AAO substrate and the thickness of the CON layer is about 250 nm (Fig. 4g). The produced membranes still maintain a moderate hydrophilicity facilitating water permeation (Fig. S26†).
The prepared CON-AAO composite membranes were used to separate a series of dye molecules in water to demonstrate their potential application in molecular separation. Dispersions of TpBD CONs were first measured by UV-vis spectroscopy and a linear relationship between absorbance and CONs concentration can be observed (Fig. S27†). Thus, the thickness of the membranes built using CONs corresponds to the filtered amount of the CON dispersion, suggesting that a controllable separation performance can be realized. Here, the amount of the used CONs for membrane fabrication was presented by using the dosage of sNaCl@CONs. The separation performance of the produced membranes was first evaluated by filtration of Evans blue (EB). Fig. 5a shows the relationship between the dosage of sNaCl@TpPa and permselectivity. Notably, the 20 nm AAO substrate possesses a water permeance of ∼2148 L m−2 h−1 bar−1 but negligible rejection of EB (<10%). After depositing CONs released from only 40 mg sNaCl@TpPa (denoted as TpPa40-AAO), the rejection of EB is improved to ∼48.2% and water permeance is decreased to ∼897 L m−2 h−1 bar−1. Increasing the sNaCl@TpPa dosage from 50 mg to 70 mg significantly elevates the rejection from ∼62.1% to ∼93.5% accompanied by reduced permeance from ∼581 to ∼191 L m−2 h−1 bar−1.
Fig. 5 Separation performances of CON-AAO composite membranes. (a and b) Performance of TpPa and TpD membranes prepared from different sNaCl@CON dosages; (c) the rejection of dyes with different molecular weights of TpBD membranes; (d) schematic presentation for the molecular sieving mechanism through the stacked TpBD CON layer; (e) UV-vis spectra corresponding to the selective removal of EB from a MO and EB mixture; (f) rejection and dyed water permeance in a long-time separation of EB; (g) comparison of separation performance of our membranes with other membranes (for details see Table S1†). |
With 80 mg of dosage, we achieve a rejection of ∼99.2% and a water permeance still as high as ∼122 L m−2 h−1 bar−1. Similarly, for the composite membranes with the deposited TpBD CONs as the selective layers, the water permeance and rejection rate display an opposite tendency with increasing dosages of sNaCl@TpBD (Fig. 5b). Eventually, the TpBD80-AAO membrane presents a rejection of ∼99.2% and a decent water permeance of ∼89 L m−2 h−1 bar−1. Importantly, the water permeance of the thus-produced membranes displays an approximately linear reduction with the increase of the CON dosage, matching well with the Hagen–Poiseuille equation.50 Here, the membrane thickness is gradually increased with increasing dosage of CONs, thus producing more and longer transporting routes to effectively sieve dye molecules.51 For this reason, the rejection of solutes presents a gradually improved tendency while the water permeance declines because of the increased mass transfer resistance. To further assess the separation performance of the CON-based membranes, a series of low molecular weight dyes with molecular weight (Mw) ranging from ∼300 to 1000 Da were used in the rejection tests. As shown in Fig. 5c, the rejection rates for various dyes are gradually improved with increasing Mw, demonstrated by the visible change in color during filtration (inset in Fig. 5c) and UV-vis spectra (Fig. S28†). Moreover, the molecular weight cut-off (MWCO) of TpBD80-AAO is determined to be ∼780 Da based on the 90% rejection of molecules. The TpBD80-AAO membrane was then subjected to a mixture containing methyl orange (MO) and EB to verify the molecular sieving effect. As illustrated in Fig. 5d, the membrane selectively allows the passage of MO molecules (yellow) from the green feed [resulting from blue (EB) and yellow (MO)] (Fig. S29†), which is further confirmed by the UV-vis spectra (Fig. 5e). In addition, the prepared membranes show very stable performance in rejection after a long-term test over a period of 30 h benefiting from the stability of CONs (Fig. 5f and S30†). The moderate reduction (∼25%) in water permeance should be caused by the concentration polarization during the continuous dyed water filtration.52 Remarkably, the synergistic effect of ordered nanopores and few-layered CONs endows the membranes with excellent rejection rates and remarkably high water permeances, which are ∼2–10 times higher than those of membranes built by other 2D materials, e.g. MOFs and GO as building blocks (Fig. 5g and Table S2†). Compared with the TpPa-AAO membrane whose selective layer is built by directly growing TpPa crystallites on the porous substrate,53 a nearly 10-fold improvement in water permeance with similar rejections also convincingly demonstrates the advantage of the COF-based membranes assembled by thin nanosheets. Hence, the membranes prepared with the synthesized CONs present an excellent and stable performance, indicating their great potential in molecular separations. CONs synthesized on small salt particles from the confined-interface strategy exhibit thin thicknesses and large lateral sizes. Because of this large surface area/thickness ratio, these CONs can fully cover the surface of the porous substrates at a low deposition thickness by vacuum filtration, thus forming a thin yet defect-free selective layer. Consequently, small molecules like water quickly pass through the intrinsic ∼2 nm pores in the CON layers while big molecules are rejected, showing an excellent molecular separation performance.
Footnote |
† Electronic supplementary information (ESI) available. See DOI: 10.1039/c9sc05082e |
This journal is © The Royal Society of Chemistry 2020 |