PbTe–PbSnS2 thermoelectric composites: low lattice thermal conductivity from large microstructures

Abstract

Recent advances in the field of thermoelectrics have shown embedding appropriate nanostructures can significantly suppress the lattice thermal conductivity and therefore enhance ZT. Here we report a new class of thermoelectric composites of PbTe–PbSnS2. PbSnS2 is a naturally layered material (space group Pnma) comprised of Sn–Pb bilayers approximately 0.6 nm in thickness. High resolution transmission electron microscopy reveals the PbSnS2 segregates into coherent lamellar structures 50–100 nm in thickness that extend 100 nm to 15 μm in length. Despite the relatively large size of the PbSnS2 precipitates, we find that incorporation of PbSnS2 in PbTe results in significant reduction in lattice thermal conductivity to 0.4–0.65 W m−1 K−1 over the temperature range 300–700 K, a reduction of 50–70% over bulk PbTe. As a result, a maximum ZT of 1.1 is obtained for ingot samples of the PbTe–PbSnS2 6% composition. We provide extensive characterization of the physical, structural, and chemical properties of this materials system including powder X-ray diffraction, infrared reflectivity, scanning and transmission electron microscopy, and thermoelectric properties measurements. The synthesis method is simple and general, opening possibilities for similar systems to yield materials exhibiting low lattice thermal conductivity without it being necessary to embed nanoscale (5–20 nm) features.

Graphical abstract: PbTe–PbSnS2 thermoelectric composites: low lattice thermal conductivity from large microstructures

Supplementary files

Article information

Article type
Paper
Submitted
09 Jun 2012
Accepted
24 Jul 2012
First published
07 Aug 2012

Energy Environ. Sci., 2012,5, 8716-8725

PbTe–PbSnS2 thermoelectric composites: low lattice thermal conductivity from large microstructures

S. N. Girard, T. C. Chasapis, J. He, X. Zhou, E. Hatzikraniotis, C. Uher, K. M. Paraskevopoulos, V. P. Dravid and M. G. Kanatzidis, Energy Environ. Sci., 2012, 5, 8716 DOI: 10.1039/C2EE22495J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements