DOI: 10.1039/D0RA06680J (Paper) RSC Adv., 2021, 11, 1715-1728

The effect of cooling process on the structure and charge/discharge capacities of Li-rich solid-solution layered oxide cathode materials for the Li-ion battery†

Fumihiro Nomuraa, Tatsuya Watanabea, Hiroya Ochiaia, Takao Gunjiab, Takeshi Hagiwarab, Jianfei Wuc and Futoshi Matsumoto*ab
aDepartment of Materials and Life Chemistry, Kanagawa University, 3-27-1, Rokkakubashi, Kanagawa-ku, Yokohama, Kanagawa 221-8686, Japan. E-mail: fmatsumoto@kanagawa-u.ac.jp
bResearch Institute for Engineering, Kanagawa University, 3-27-1, Rokkakubashi, Kanagawa-ku, Yokohama, Kanagawa 221-8686, Japan
cQingdao Industrial Energy Storage Research Institute, Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, No. 189 Songling Road, 266101 Qingdao, China

Received 2nd August 2020 , Accepted 20th November 2020

First published on 6th January 2021

Abstract

The effect of cooling process after calcination at 900 °C in the preparation of cathode materials, on the crystal structure and charging/discharging capacities of Li2MnO3–LiNi1/2Mn1/2O2–LiNi1/3Mn1/3Co1/3O2 Li-rich solid-solution layered oxide (LLO) cathode materials for the lithium ion battery was examined in twenty-one LLO samples having different compositions. This was achieved by applying two types of cooling processes: (i) quenching the calcinated LLO samples with liquid nitrogen (quenched cooling), and (ii) slow cooling of LLO samples in the furnace at a controlled decreasing rate of the temperature (slow cooling). The results of the comparison between discharging capacities observed with LLO samples prepared with two types of cooling processes indicated that the cooling process for LLO samples to exhibit high discharge capacity was not limited to either one. The process that can be more effective for LLO samples to exhibit the high discharge capacity depended on the composition of LLO samples. LLO samples containing Li2MnO3 of over 60% exhibited higher discharge capacity when samples were quenched with liquid nitrogen than those prepared with the slow cooling process. Among LLOs examined, the effect of quenching was maximum when the Li2MnO3 content was 60%. As the LLO composition deviated from the line of 60% Li2MnO3 in the Li[Li0.20Mn0.58Ni0.18Co0.04]O2 sample compositions, the effect of quenching became smaller and the slow cooling process was superior to the quenching process. A connection was thus made between the structural difference of LLO samples prepared with the two types of cooling processes and the cathode performance was observed.

1. Introduction

Li2MnO3–LiMO2 (M: transition metal) Li-rich solid-solution layered oxide (LLO) materials have attracted much attention from researchers and engineers in the area of lithium ion batteries (LIBs) because of their high charging/discharging capacities over 250 mA h g−1 when LLO materials were charged to more than 4.6 V (vs. Li/Li+).1,2 Although many researchers have made efforts toward elucidating the reason why the LLO materials exhibited high charging/discharging capacities,3,4 the mechanism has not been made clear yet. In addition, their capacities degrade with increasing charging/discharging cycling number.5,6 A prevention method for the degradation of the cathode performance is also not known to have been established yet. The answers of how to prepare LLO materials exhibiting high and stable capacities is still pursued. In order to establish knowledge on LLO materials from a multilateral point of view, in the LLO samples composed of Li2MnO3–LiNi1/2Mn1/2O2–LiNi1/3Mn1/3Co1/3O2, we have also examined the best ratios of Li2MnO3, LiNi1/2Mn1/2O2 and LiNi1/3Mn1/3Co1/3O2, the calcination temperature and the cooling process for LLO exhibiting the best cathode performance.7–10 Among these results, it was found that Li[Li0.20Mn0.58Ni0.18Co0.04]O2 (Li2MnO3 (60%)–LiNi0.5Mn0.5O2 (30%)–LiNi1/3Co1/3Mn1/3O2 (10%)) exhibited the best cathode performance among LLOs examined, and the cooling process was one of the key factors in determining the cathode performance.10 Many papers have reported the use of the quenching process, in which LLO samples calcinated at 800–100 °C were suddenly cooled with liquid nitrogen; thus, the importance of quenching process in achieving LLO samples exhibiting high charging/discharging capacities has been suggested.11–14 The difference in the crystal structures between LLO samples prepared with the quenched cooling process, in which calcinated LLO samples were quenched with liquid nitrogen, and the slow cooling process, in which calcinated samples were cooled in the furnace at a controlled decreasing temperature rate, have been discussed.12,15 We also have confirmed the necessity of the quenching process for the LLO samples having the composition of Li[Li0.20Mn0.58Ni0.18Co0.04]O2 (Li2MnO3 (55%)–LiNi0.5Mn0.5O2 (35%)–LiNi1/3Co1/3Mn1/3O2 (10%)).10 In addition, quenching the LLO samples decreased the degree of stacking defaults and disordering between the Li+ and transition metal ions on the transition metal layer in the crystal structure of the LLO samples, resulting in an improvement of the cathode performance. Slow cooling of the LLO samples degraded the degree of the crystal structure of the LLOs, and reduced the charging/discharging cycle performance.10 On the contrary, in the synthesis of layered lithium transition-metal oxides, LiMO2 (M = Co, Ni, Mn), quenched cooling was not applied for the LiMO2 samples that exhibited high and stable cathode performance.16,17 However, there is a paper in which it has been reported that the quenched cooling process is effective in enhancing the cycle stability and storage property in Ni-rich LiMO2.18 From these papers, we doubt that the application of the cooling processes to cathode materials can be divided into the quenched cooling for the LLO materials and slow cooling for LiMO2. So, in this study, we examined the dependence of the charging/discharging capacities on the cooling process in several LLO samples composed of Li2MnO3–LiNi1/2Mn1/2O2–LiNi1/3Mn1/3Co1/3O2. Except for the quenched cooling and slow cooling processes, other cooling processes are considered by changing the cooling rates. In other papers, the quenched cooling and slow cooling processes were used frequently. Therefore, in this study, the quenched cooling and slow cooling processes were examined. It could be confirmed that the necessity of quenched cooling as a cooling process was dependent on the ratio of the Li2MnO3–LiNi1/2Mn1/2O2–LiNi1/3Mn1/3Co1/3O2 in the LLO samples. In addition, what was changed by the difference in the cooling process in the LLO samples was analyzed. Qu et al. reported that in the quenched cooling method case, there was an increase in the interslab thickness and decrease in the degree of cation mixing in the LiNi0.8Co0.15Al0.05O2 sample.18 Chang et al. reported an increase in the content of the Li-rich monoclinic component, as well as a larger lattice in the quenched cooling of the Li1.207Ni0.127Mn0.54Co0.127O2 sample.14

In this study, we also gathered the information on the average crystal structure of LLO samples by the Rietveld refinement method with the pXRD patterns and the results of charging/discharging cycle tests, and tried to find the relationship between the cooling process and the cathode performance from the view point of the average crystal structure of the LLO samples with pXRD data.

2. Experimental

2.1 Preparation of LLO materials

The Li2MnO3–LiNi1/2Mn1/2O2–LiNi1/3Mn1/3Co1/3O2 LLO samples examined in this study were synthesized by a co-precipitation procedure using the following commercial reagents: nickel sulfate hexahydrate (NiSO4·6H2O, 99%, Kanto Chemical. Co., Inc. (Kanto), Japan), manganese sulfate monohydrate (MnSO4·H2O, 99%, Kanto) and cobalt sulfate heptahydrate (CoSO4·7H2O, 99%, Wako Pure Chemical Industries, Ltd. (Wako), Japan). All of the reagents were used without further purification. The targeted compositions of twenty-one synthesized LLOs and the ratios of the Li2MnO3, LiNi1/2Mn1/2O2 and LiNi1/3Mn1/3Co1/3O2 components are summarized in Table 1, and are also presented in the Li2MnO3–LiNi1/2Mn1/2O2–LiNi1/3Mn1/3Co1/3O2 ternary diagram of Fig. 1.
Table 1 Summary of the targeted compositions of synthesized LLO samples
Sample no. Targeted compositions of synthesized LLOs Ratios of Li2MnO3, LiNi1/2Mn1/2O2 and LiNi1/3Mn1/3Co1/3O2 components Ratios of Mn, Co and Ni in LLOs Compositions estimated with ICP-MS
1 Li1.27Ni0.1Mn0.63O2 80[thin space (1/6-em)]:[thin space (1/6-em)]20[thin space (1/6-em)]:[thin space (1/6-em)]0 0.864[thin space (1/6-em)]:[thin space (1/6-em)]0.000[thin space (1/6-em)]:[thin space (1/6-em)]0.136 Li1.269Ni0.096Mn0.635O2
2 Li1.23Ni0.14Mn0.61Co0.02O2 70[thin space (1/6-em)]:[thin space (1/6-em)]25[thin space (1/6-em)]:[thin space (1/6-em)]5 0.793[thin space (1/6-em)]:[thin space (1/6-em)]0.022[thin space (1/6-em)]:[thin space (1/6-em)]0.185 Li1.227Ni0.152Mn0.616Co0.019O2
3 Li1.2Ni0.183Mn0.583Co0.04O2 60[thin space (1/6-em)]:[thin space (1/6-em)]30[thin space (1/6-em)]:[thin space (1/6-em)]10 0.729[thin space (1/6-em)]:[thin space (1/6-em)]0.042[thin space (1/6-em)]:[thin space (1/6-em)]0.229 Li1.209Ni0.173Mn0.590Co0.028O2
4 Li1.17Ni0.22Mn0.56Co0.05O2 50[thin space (1/6-em)]:[thin space (1/6-em)]35[thin space (1/6-em)]:[thin space (1/6-em)]15 0.670[thin space (1/6-em)]:[thin space (1/6-em)]0.060[thin space (1/6-em)]:[thin space (1/6-em)]0.270 Li1.168Ni0.223Mn0.559Co0.050O2
5 Li1.13Ni0.27Mn0.53Co0.07O2 40[thin space (1/6-em)]:[thin space (1/6-em)]40[thin space (1/6-em)]:[thin space (1/6-em)]20 0.615[thin space (1/6-em)]:[thin space (1/6-em)]0.077[thin space (1/6-em)]:[thin space (1/6-em)]0.308 Li1.138Ni0.260Mn0.537Co0.065O2
6 Li1.1Ni0.31Mn0.51Co0.08O2 30[thin space (1/6-em)]:[thin space (1/6-em)]45[thin space (1/6-em)]:[thin space (1/6-em)]25 0.565[thin space (1/6-em)]:[thin space (1/6-em)]0.093[thin space (1/6-em)]:[thin space (1/6-em)]0.343 Li1.10Ni0.310Mn0.510Co0.08O2
7 Li1.07Ni0.35Mn0.48Co0.1O2 20[thin space (1/6-em)]:[thin space (1/6-em)]50[thin space (1/6-em)]:[thin space (1/6-em)]30 0.518[thin space (1/6-em)]:[thin space (1/6-em)]0.107[thin space (1/6-em)]:[thin space (1/6-em)]0.375 Li1.063Ni0.355Mn0.481Co0.101O2
8 Li1.03Ni0.39Mn0.46Co0.12O2 10[thin space (1/6-em)]:[thin space (1/6-em)]55[thin space (1/6-em)]:[thin space (1/6-em)]35 0.474[thin space (1/6-em)]:[thin space (1/6-em)]0.121[thin space (1/6-em)]:[thin space (1/6-em)]0.405 Li1.03Ni0.39Mn0.46Co0.12O2
9 LiNi0.433Mn0.433Co0.133O2 0[thin space (1/6-em)]:[thin space (1/6-em)]60[thin space (1/6-em)]:[thin space (1/6-em)]40 0.433[thin space (1/6-em)]:[thin space (1/6-em)]0.133[thin space (1/6-em)]:[thin space (1/6-em)]0.433 LiNi0.433Mn0.433Co0.133O2
10 Li1.2Ni0.2Mn0.6O2 60[thin space (1/6-em)]:[thin space (1/6-em)]40[thin space (1/6-em)]:[thin space (1/6-em)]0 0.750[thin space (1/6-em)]:[thin space (1/6-em)]0.000[thin space (1/6-em)]:[thin space (1/6-em)]0.250 Li1.200Ni0.200Mn0.600O2
11 Li1.2Ni0.16Mn0.57Co0.07O2 60[thin space (1/6-em)]:[thin space (1/6-em)]20[thin space (1/6-em)]:[thin space (1/6-em)]20 0.708[thin space (1/6-em)]:[thin space (1/6-em)]0.083[thin space (1/6-em)]:[thin space (1/6-em)]0.208 Li1.207Ni0.157Mn0.576Co0.065O2
12 Li1.2Ni0.15Mn0.55Co0.1O2 60[thin space (1/6-em)]:[thin space (1/6-em)]10[thin space (1/6-em)]:[thin space (1/6-em)]30 0.688[thin space (1/6-em)]:[thin space (1/6-em)]0.125[thin space (1/6-em)]:[thin space (1/6-em)]0.188 Li1.203Ni0.149Mn0.550Co0.071O2
13 Li1.2Ni0.133Mn0.533Co0.133O2 60[thin space (1/6-em)]:[thin space (1/6-em)]0[thin space (1/6-em)]:[thin space (1/6-em)]40 0.667[thin space (1/6-em)]:[thin space (1/6-em)]0.167[thin space (1/6-em)]:[thin space (1/6-em)]0.167 Li1.206Ni0.139Mn0.552Co0.103O2
14 Li1.27Ni0.1Mn0.63O2 80[thin space (1/6-em)]:[thin space (1/6-em)]0[thin space (1/6-em)]:[thin space (1/6-em)]20 0.818[thin space (1/6-em)]:[thin space (1/6-em)]0.091[thin space (1/6-em)]:[thin space (1/6-em)]0.091 Li1.273Ni0.090Mn0.637O2
15 Li1.23Ni0.14Mn0.61Co0.02O2 70[thin space (1/6-em)]:[thin space (1/6-em)]5[thin space (1/6-em)]:[thin space (1/6-em)]25 0.750[thin space (1/6-em)]:[thin space (1/6-em)]0.109[thin space (1/6-em)]:[thin space (1/6-em)]0.141 Li1.231Ni0.118Mn0.584Co0.083O2
16 Li1.17Ni0.22Mn0.56Co0.05O2 50[thin space (1/6-em)]:[thin space (1/6-em)]15[thin space (1/6-em)]:[thin space (1/6-em)]35 0.630[thin space (1/6-em)]:[thin space (1/6-em)]0.140[thin space (1/6-em)]:[thin space (1/6-em)]0.2300 Li1.204Ni0.138Mn0.605Co0.053O2
17 Li1.2Ni0.27Mn0.53Co0.07O2 40[thin space (1/6-em)]:[thin space (1/6-em)]20[thin space (1/6-em)]:[thin space (1/6-em)]40 0.577[thin space (1/6-em)]:[thin space (1/6-em)]0.154[thin space (1/6-em)]:[thin space (1/6-em)]0.269 Li1.132Ni0.235Mn0.499Co0.134O2
18 Li1.2Ni0.31Mn0.51Co0.08O2 30[thin space (1/6-em)]:[thin space (1/6-em)]25[thin space (1/6-em)]:[thin space (1/6-em)]45 0.528[thin space (1/6-em)]:[thin space (1/6-em)]0.167[thin space (1/6-em)]:[thin space (1/6-em)]0.306 Li1.193Ni0.312Mn0.490Co0.05O2
19 Li1.07Ni0.35Mn0.48Co0.1O2 20[thin space (1/6-em)]:[thin space (1/6-em)]30[thin space (1/6-em)]:[thin space (1/6-em)]50 0.482[thin space (1/6-em)]:[thin space (1/6-em)]0.179[thin space (1/6-em)]:[thin space (1/6-em)]0.339 Li1.065Ni0.318Mn0.449Co0.168O2
20 Li1.03Ni0.39Mn0.46Co0.12O2 10[thin space (1/6-em)]:[thin space (1/6-em)]35[thin space (1/6-em)]:[thin space (1/6-em)]55 0.440[thin space (1/6-em)]:[thin space (1/6-em)]0.190[thin space (1/6-em)]:[thin space (1/6-em)]0.371 Li1.028Ni0.383Mn0.458Co0.131O2
21 Li1Ni0.43Mn0.43Co0.14O2 0[thin space (1/6-em)]:[thin space (1/6-em)]40[thin space (1/6-em)]:[thin space (1/6-em)]60 0.400[thin space (1/6-em)]:[thin space (1/6-em)]0.200[thin space (1/6-em)]:[thin space (1/6-em)]0.400 Li1.05Ni0.428Mn0.430Co0.10O2


image file: d0ra06680j-f1.tif
Fig. 1 Targeted compositions of synthesized LLO samples represented in the Li2MnO3–LiNi1/2Mn1/2O2–LiNi1/3Mn1/3Co1/3O2 ternary diagram. The numbers 1–21 in the circles indicate the sample number.

In this study, selected samples in the ternary diagrams were examined. The points to select the samples were the vertical lines and the horizon line of the composition in the ternary diagram. In the vertical lines, the ratio of LiNi1/2Mn1/2O2 to LiNi1/3Mn1/3Co1/3O2 was fixed, and then the ratio of Li2MnO3 to LiMO2 was changed to find the dependence of the cooling process on the ratio of Li2MnO3 to LiMO2. In the horizontal line in the ternary diagram, conversely, the ratio of Li2MnO3 was fixed, and then the ratio of LiNi1/2Mn1/2O2 to LiNi1/3Mn1/3Co1/3O2 was changed to find the dependence of cooling process on the ratio of LiNi1/2Mn1/2O2 to LiNi1/3Mn1/3Co1/3O2. The horizon line used in this examination was in the area in which the LLO samples exhibited higher charge/discharge capacity, as mentioned above. We think that an examination of the LLO samples in the two vertical lines and a horizon line was enough to find the relationship between the cooling processes to achieve higher capacity and composition of LLO samples.

The starting material mixture of MnSO4·H2O, NiSO4·6H2O and CoSO4·7H2O with a targeted Ni/MN/Co ratio was added to 100 mL of water, while the total concentration of the transition metal ions in the solution was 2 M. In order to precipitate the transition metal carbonates from the solution, 80 mL of the 2 M sodium carbonate (Na2CO3, 98%, Wako) solution was injected at the rate of 0.5 cm3 s−1 into it (kept at 60 °C) with a burette. During the precipitation, its pH was kept at 7.5 by injecting the NH4OH solution. The precipitates were filtered off, washed several times with hot water until the filtrate exhibited a neutral pH, and dried under vacuum at 100 °C for 5 h. Lithium carbonate (Li2CO3, 98%, Kanto) was mixed with the precipitates using a wet planetary ball-milling machine in a Teflon jar (672 mL) containing Teflon balls (diameter 1.5 cm, 88 balls) and acetone (80 mL) at ambient temperature with a speed of 300 rpm for 3 h. To compensate for any possible losses of Li+ ions by evaporation of Li during the high temperature calcination, the transition metal carbonates were mixed with an excess (7.0%) of Li2CO3, in comparison with the amount calculated based on the stoichiometric mole ratios of Li, Ni, Co and Mn in the target LLOs. After drying the mixture at 120 °C for 4 h under vacuum, a pellet (diameter: 2 mm) of the dried mixture was formed using 30 kN of force. The individual pellets were then calcinated at 900 °C for 12 h in air. Two types of cooling processes after calcination were used: one is a quenched cooling process with liquid nitrogen, while another is a slow cooling process at a controlled cooling rate of 25 °C h−1 in the furnace from 900 to 25 °C. Hereinafter, the former cooling will be called “quenched cooling” and the latter “slow cooling”. The cooled pellets were ground with a mortar to obtain particles having a surface area of 0.8–0.9 m2 g−1. The Li[thin space (1/6-em)]:[thin space (1/6-em)]Ni[thin space (1/6-em)]:[thin space (1/6-em)]Co[thin space (1/6-em)]:[thin space (1/6-em)]Mn elemental ratios in the synthesized cathode materials were measured to confirm the target ratios by ICP-MS using an Agilent 7700x spectrometer. The pXRD experiments were performed using CuKα radiation (Rigaku RINT-Ultima III; λ = 0.1548 nm) at increments of 0.02 degrees over a range from 20 to 80 degrees. An obliquely finished Si crystal (non-reflection Si plate) was used as a sample holder to minimize the background. Brunauer–Emmett–Teller (BET) surface areas of the cathode particles were measured with a TriStar 3000 surface area instrument (Micromeritic Instrument Corporation). X-ray photoelectron spectroscopy (XPS) measurements (JP-9010 MC, JEOL) were performed to analyze the surface composition of the Mn, Ni and Co ions in the samples prepared, and their bulk composition was analyzed with an X-ray fluorescence spectrometer (XRF, ZSX PrimusIV, Rigaku).

In order to investigate the oxidation states of the Mn, Ni and Co ions of the LLO samples prepared with various compositions and cooling conditions, their X-ray absorption fine structures (XAFS) were analyzed using the BL01B1 beam line at the SPring-8 facility (JASRI, Hyogo, Japan). The Mn, Co and Ni K-edge XAFS spectra were measured using quick XAFS (QXAFS) with transmission mode, and a double-crystal Si (111) monochromator was employed to obtain the XAFS data. The energy levels during the XAFS measurement were calibrated by the pre-edge peak in the spectrum of a Cu foil equal to 8980.3 eV. All XAFS spectra were analyzed using the program package Athena software.19

The SEM, XRD and Rietveld refinement analysis data shown in this paper were selected from samples 1, 3, 5, 9, 10 and 13 located in the vertical and horizon lines in the ternary diagram of Fig. 1 due to the space limitation in this paper, and because the comparison of the data obtained from samples 1, 3, 5, 9, 10 and 13 clearly indicates the conclusion of this study. The data of the other samples examined are shown and can be compared in the ESI.†

2.2 Cell preparation and electrochemical tests

An accurately weighed quantity of 1 g of each LLO cathode material, 0.121 g of acetylene black (AB, DENKA BLACK, Denki Kagaku Kogyo Ltd., Japan) and 0.084 g of polyvinylidene difluoride (PVdF, KF polymer #9130, 13 wt% in N-methyl-2-pyrrolidone (NMP), Kureha, Japan) were mixed in NMP (anhydrous 99.5%, Sigma-Aldrich) using planetary mixing equipment (Mazerustar, KK-250S, KURABO, Japan) to form a homogenous mixture. Each mixture (the solid content is 30–40 wt%) had a suitable viscosity for coating it as the cathode film, while preserving the weight% of LLO[thin space (1/6-em)]:[thin space (1/6-em)]AB[thin space (1/6-em)]:[thin space (1/6-em)]PVdF = 83[thin space (1/6-em)]:[thin space (1/6-em)]10[thin space (1/6-em)]:[thin space (1/6-em)]7 in the prepared cathode film. The mixture was coated using a doctor-blade coater (100 μm gap) on an aluminum (Al) current collector. The thin film mixture on the Al was dried at 130 °C for 5 h in a vacuum drying oven. The thus-prepared electrodes were pressed with a roll press machine. The loading amount of each LLO on the Al current collector was 2.5–3.0 mg cm−2. Each prepared cathode layer was kept at the loading density of 1.6 mg cm−3.

The cathode performance tests were performed using a CR2032 coin-type cell. The test cells were composed of a cathode and a lithium metal anode separated by a porous polypropylene film (Celgard 3401). The electrolyte used was a 1 M lithium hexafluorophosphate (LiPF6)–ethylene carbonate (EC)/dimethyl carbonate (DMC) mixture (1[thin space (1/6-em)]:[thin space (1/6-em)]2 by vol., Ube Chemicals, Japan). The charge/discharge cycling was performed using a multichannel battery tester (HJ1001SD8, Hokuto Denko Corporation, Japan). All tests were performed in a constant temperature bath (MIR-154, Panasonic) of 25 °C. The constant-current/constant-voltage (CC-CV) mode was used for the cycling tests. The charge/discharge cycling tests after electrochemical pre-treatment process were performed at a charge/discharge current density of 0.1C-rate. To observe the stable charge/discharge cycle performance, the pre-treatment process developed by Ito et al.20,21 was applied in this study. The discharge voltage limit was fixed at 2.0 V, and the charge voltage limit was increased by 0.1 V stepwise from 4.5 to 4.8 V every two cycles. The C-rate was calculated with the specific capacity of 200 mA h g−1 for all synthesized LLO materials. The cutoff voltages for the charging/discharging tests were 2.0 and 4.8 V. During CV mode, the upper cutoff voltage was held constant for 5 h.

3. Results and discussion

3.1 Characterization of the synthesized LLO cathode materials and charging/discharging cycle tests of the LLO samples

The synthesized LLO samples had the targeted compositions with an error of 15%, which were evaluated with ICP-MS, as shown in Table 1, and the BET surface areas of 0.8–0.9 m2 g−1. All secondary particles of the LLO samples were constructed with primary particles having the diameter of 100–200 nm, as shown in Fig. 2 and S1.† From these results, the synthesized samples almost have the same morphology of particles between the quenched and slow cooling processes, and their compositions were changed systematically as we designed. In order to know the deviation of Mn, Ni and Co ions in the sample particles, the surface and bulk compositions of the samples were analyzed with XPS and XRF, respectively (Table S1†). The bulk composition evaluated with XRF (Table S1†) was in good agreement with the targeted composition (Table 1) on each sample. In all samples irrespective of quenched and slow cooling processes, Ni atom is rich in the particle surface areas when compared with bulk. Conversely, the Mn atom is poor in the surface area when compared with the results of the bulk atomic and surface ratios in Table S1.† Although the surface composition of the Co atom is rich or poor in the sample surfaces, the reason why the trend of the composition of Co could not be observed is due to the low content of Co atom in the LLO samples. The degree of Ni richness in the particle surface increases a little when the slow cooling process was applied to the samples in comparison with one prepared using the quenched cooling process. The degree of Ni richness in the slow cooling process does not depend on the bulk composition. That means that the degree of difference in the composition between the surface and bulk areas was not caused by the difference of the cooling process applied when the samples were prepared.
image file: d0ra06680j-f2.tif
Fig. 2 SEM images of the LLO samples prepared by (A-1, B-1, C-1, D-1, E-1 and F-1) quenching the samples calcinated at 900 °C for 12 h in air with liquid nitrogen, and (A-2, B-2, C-2, D-2, E-2 and F-2) cooling them at a controlled cooling rate of 25 °C h−1 in the furnace from 900 to 25 °C. (A-1, A-2): sample 1, (B-1, B-2): sample 3, (C-1, C-2): sample 5, (D-1, D-2): sample 9, (E-1, E-2): sample 10 and (F-1, F-2): sample 13.

Fig. 3 shows the (A) Mn, (B) Ni and (C) Co K-edge XANES spectra of sample 3 prepared by quenching the calcinated sample with liquid N2. Together with the spectra of sample 3, the spectra of the reference samples of Mn3O4, Mn2O3, MnO2, NiO, CoO, LiCoO2 are also shown in Fig. 3. Comparing the sample spectra with the reference spectra, the oxidation number of Mn ion in the sample 3 might be close to +4 because the sample spectra are similar to those of MnO2. From a similar point of view, the oxidation number of the Ni and Co ions might be +2 and +3. These oxidation numbers of the Mn, Ni and Co ions agree with ones reported in published papers.22–24 Fig. S2† shows the difference in the K-edge XANES spectra of the Mn, Ni and Co ions between the samples 2–8 prepared by quenching the calcinated sample with liquid N2 (black line), and low cooling of the calcinated samples at the controlled rate of 25 °C h−1 (red line). As mentioned in Fig. 3, the slope of the K-edge XANES spectra depended on the oxidation states of the Mn, Ni and Co ions in the LLO samples.25 In the XANES spectra shown in Fig. S2,† the difference (black vs. red lines) in the slopes of the XANES spectra observed with the samples prepared with the quenching and slow cooling processes could not be observed. The XANES spectra of the Co ions in the LLO samples exhibited a small difference between the spectra obtained with the samples prepared with quenching and slow cooling processes. The small difference in the spectra obtained with the samples prepared with the quenching and slow cooling processes is due to the low content of Co ion. These results indicate that the average oxidation states of the Mn, Ni and Co ions in the LLO samples are not affected by changing the cooling process. From all results shown above, the surface morphology, surface composition and the electronic state of ions in the samples are not the factors that exhibit a difference in the discharge capacity of the LLO samples prepared with quenched and slow cooling processes. The difference in the crystal structure of the LLO samples prepared with quenched and slow cooling processes, as shown below, can be discussed to elucidate the effect of the cooling process on the cathode performance.


image file: d0ra06680j-f3.tif
Fig. 3 (A) Mn, (B) Ni and (C) Co K-edge XANES spectra of sample 3 prepared by the quenched cooling with liquid nitrogen and reference samples of Mn3O4, Mn2O3, MnO, NiO2, CoO and LiCoO2.

Fig. 4 shows the charging/discharging voltage–capacity curves observed at the 10th cycle with the samples 1, 3, 5, 9, 10, 13, 14, 17 and 21. The charging/discharging voltage–capacity curves for the other samples are shown in Fig. S3.† In all samples, the charging/discharging voltage–capacity curves exhibited characteristic large voltage hysteresis during the charging and discharging processes, although the conventional LiCoO2 and LiNi1/3Mn1/3Co1/3O2 cathode materials exhibited almost constant voltages in both charging and discharging processes.26 The difference in the shape of the charging/discharging voltage–capacity curves between the samples prepared by quenched and slow cooling processes could not be observed in all LLO samples tested. Depending on the composition of the LLO samples, the observed capacities and the magnitude of the retention of charge/discharge capacities observed were changed. This means that in some compositions, the quenched cooling process was effective for observing the higher capacity. In other compositions, the LLO samples prepared with the slow cooling process exhibited higher capacity. In Fig. S4,† dQ/dV curves calculated with the charging/discharging capacity vs. voltage curves at the 10th cycle are shown. Generally, the difference in the dQ/dV curves between the samples prepared by quenched and slow cooling processes could be observed in the area where the Li2MnO3 percentages in the samples are high (samples 1, 2, 3 and 14 and 15) and low (samples 8, 9, 20 and 21). However, the difference in the dQ/dV curves could not be observed in the area (samples 4, 5, 6, 7, 12, 16, 17 and 18) where the difference in the charging/discharging capacities between the samples prepared by quenching and slow cooling processes could be observed (around 60% Li2MnO3 composition). Therefore, the difference in the cooling process does not influence the redox potentials of the Mn, Ni and Co ions in the LLO samples. Fig. S5† shows the results of the charging/discharging cycle performance tests obtained at 0.1C. Until the 6th cycle, the pre-treatment explained in the experimental section was applied to all cathodes. From the 7th cycle, the charging/discharging cycle tests were started between the cutoff voltages of 4.8 and 2.0 V. The discharge capacities at the 10th cycle are summarized in Table 2. In the LLO samples 3, 11, 12, 13 that contained the Li2MnO3 component with high percentage and exhibited higher discharge capacities in the quenched samples, the discharge capacity decreased with increasing cycle number even though the samples exhibited high discharge capacity. These results indicate that the samples exhibiting high discharge capacity do not always exhibit high cycle durability, and that improvement of the cycle durability of the LLO samples cannot be achieved by selecting the cooling process after calcination of the LLO samples. From Table 2, the difference in the discharge capacities observed at the 10th cycle with the samples prepared by quenched and slow cooling processes was calculated, and their difference in the composition of LLO is summarized in Fig. 5. In Fig. 5, the colored circles show the degree of the difference in the discharge capacities between the quenched and slow cooling samples. The difference in the discharge capacities is defined as follows:

 
Difference of the discharge capacity = {(discharge capacity of the LLO sample prepared by quenching) − (discharge capacity of the LLO sample prepared by slow cooling)} at the 10th discharge cycle (1)


image file: d0ra06680j-f4.tif
Fig. 4 Charging/discharging voltage–capacity curves obtained at the 10th cycle with samples 1 (A), 3 (B), 5 (C), 9 (D), 10 (E), 13 (F), 14 (G), 17 (H) and 21 (I) prepared by the quenched cooling with liquid nitrogen (solid lines), and the slow cooling in the furnace at a controlled rate of 25 °C h−1 (dotted lines). The charging/discharging rate was 0.1C.
Table 2 Summary of the discharge capacity of LLO samples (no. 1–21) at the 10th cycle. The samples were prepared by quenching the samples calcinated at 900 °C for 12 h in air with liquid nitrogen (“quenched cooling”), and cooling them at a controlled cooling rate of 25 °C h−1 in the furnace from 900 to 25 °C (“slow cooling”). The discharging rate was 0.1C
Sample no. Discharge capacity (mA h g−1)
Quenched cooling Slow cooling
1 227 203
2 286 232
3 260 205
4 234 236
5 198 226
6 150 170
7 167 181
8 197 211
9 172 183
10 233 241
11 264 242
12 254 236
13 253 261
14 133 102
15 176 150
16 188 204
17 200 234
18 186 201
19 153 169
20 168 186
21 141 154


image file: d0ra06680j-f5.tif
Fig. 5 Summary of the dependence of the difference in discharge capacity obtained at the 10th cycle on the targeted composition of the LLO samples. The difference in discharge capacity = (discharge capacity of the LLO sample prepared by the quenched cooling) − (discharge capacity of the LLO sample prepared by slow cooling). The difference in discharge capacities: image file: d0ra06680j-u4.tif > 10 mA h g−1, −10 mA h g−1 < image file: d0ra06680j-u5.tif < 10 mA h g−1, image file: d0ra06680j-u6.tif < −10 mA h g−1.

The LLO samples prepared by quenching in the yellow colored circles exhibited higher discharge capacity than those prepared by slow cooling. The samples in the pink area, which adjoined the yellow area, showed that the discharge capacities of the samples prepared with quenching and slow cooling did not have a large difference. In the green circles, the slow cooling process was effective for the samples to display higher discharge capacity. A clear classification of the composition could be observed for the question of which cooling process was effective to observe higher discharge capacity.

3.2 Evaluation of the difference of the crystal structure of the LLO samples after quenching and slow cooling processes with pXDR and Rietveld refinement analysis

In order to elucidate the difference of the crystal structure of the LLO samples prepared with the two types of cooling processes, pXRD patterns of the LLO samples prepared with the two types of cooling processes were obtained. Typical pXRD patterns of samples 1, 3, 5, 9, 10 and 13 are shown in Fig. 6–8, and other results are shown in Fig. S6.† The pXRD Rietveld refinement profiles of the LLO samples are also shown as calculated profiles and the residual difference in Fig. 6–8 and S6.†
image file: d0ra06680j-f6.tif
Fig. 6 XRD Rietveld refinement profiles of samples 1 (A-1, A-2) and 3 (B-1, B-2) prepared by (A-1, B-1) the quenched cooling with liquid nitrogen, and (A-2, B-2) the slow cooling in the furnace at a controlled rate of 25 °C h−1. (—) observed, (—) calculated, (—) the difference of both. The green vertical marks indicate the position of the Bragg reflections. * corresponds to the peaks around 20–25° that result from the ordering of Li+ ions in the transition metal layers.

image file: d0ra06680j-f7.tif
Fig. 7 XRD Rietveld refinement profiles of samples 5 (A-1, A-2) and 9 (B-1, B-2) prepared by (A-1, B-1) the quenched cooling with liquid nitrogen, and (A-2, B-2) the slow cooling in the furnace at a controlled rate of 25 °C h−1. (—) observed, (—) calculated, (—) the difference of both. The green vertical marks indicate the position of the Bragg reflections. * corresponds to the peaks around 20–25° that result from the ordering of Li+ ions in the transition metal layers.

image file: d0ra06680j-f8.tif
Fig. 8 XRD Rietveld refinement profiles of samples 10 (A-1, A-2) and 13 (B-1, B-2) prepared by (A-1, B-1) the quenched cooling with liquid nitrogen, and (A-2, B-2) slow cooling in the furnace at a controlled rate of 25 °C h−1. (—) observed, (—) calculated, (—) the residual difference of both. The green vertical marks indicate the position of the Bragg reflections. * corresponds to the peaks around 20–25° that result from the ordering of Li+ ions in the transition metal layers.

In Table 3 and S2,† the refined structural parameters of the LLO samples obtained from the Rietveld refinement21,27 with the space group of C2/m are summarized. The comparison of the structural parameters obtained is summarized in Table 4. The definition of the colors used in Table 4 is the same as those used for the difference in the discharge capacity between the samples prepared by quenching and slow cooling in Fig. 5. In all XRD patterns, the peaks at around 20–25° that result from the ordering of Li+ ions in the transition metal layers could be observed.28 Considering the composition of samples 9 and 21, the samples do not contain the component of Li2MnO3. Therefore, the sample should have a layered α-NaFeO2-type rock salt structure (LiMO2) with the space group R[3 with combining macron]m. However, in this study, the XRD profiles observed with samples 9 and 21 prepared with the two cooling processes exhibited the peaks at around 20–25°. This indicates the ordering of Li+ ions in the transition metal layers as a result of cation mixing between the transition metal ions in the transition layer, and Li+ ions in the Li+ ion layer in the layered α-NaFeO2-type rock salt structure. The appearance of the peaks might result from the synthesis condition for this study. The results of the Rietveld refinement analysis demonstrate excellent fitting between the observed Rietveld refinement profile and the calculated one with a C2/m space group. In particular, the consistency between the XRD data and simulated pattern around 20–25° could be seen in the entire Rietveld refinement, leading to reliable consequences about the Li/Ni mixing degree (Fig. S7†).

Table 3 The refined structural parameters of LLO samples obtained from the Rietveld refinement with the space of C2/m. The LLO samples were prepared by (1) the quenched cooling with liquid nitrogen, and (2) the slow cooling in the furnace at a controlled rate of 25 °C h−1. Samples: 1 (A), 3 (B), 5 (C), 9 (D), 10 (E) and 13 (F)
(A-1)
S = 1.9821, RB = 4.383, RF = 3.712, Rwp = 13.511
a = 4.9385(3) Å, b = 8.5551(4) Å, c = 5.0326(2) Å, β = 108.997(7)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.975(2)
M 2c 0 0 0.5 0.025(2)
Li 2b 0 0.5 0 0.748(6)
M 2b 0 0.5 0 0.252(6)
Li 4g 0 0.1646(3) 0 0.040(6)
M 4g 0 0.1646(3) 0 0.960(6)
Li 4h 0 0.681(2) 0.5 0.996(1)
M 4h 0 0.681(2) 0.5 0.004(1)
O 4i 0.213(2) 0 0.2169(9) 1
O 8j 0.257(1) 0.3151(6) 0.2270(6) 1
(A-2)
S = 2.0339, RB = 6.018, RF = 5.440, Rwp = 12.940
a = 4.9341(3) Å, b = 8.5419(3) Å, c = 5.0343(2) Å, β = 109.202(4)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.954(3)
M 2c 0 0 0.5 0.046(3)
Li 2b 0 0.5 0 0.546(5)
M 2b 0 0.5 0 0.454(5)
Li 4g 0 0.1697(3) 0 0.054(5)
M 4g 0 0.1697(3) 0 0.946(5)
Li 4h 0 0.699(2) 0.5 0.998(2)
M 4h 0 0.699(2) 0.5 0.002(2)
O 4i 0.208(1) 0 0.220(1) 1
O 8j 0.261(1) 0.3209(7) 0.2195(7) 1
(B-1)
S = 1.7132, RB = 4.117, RF = 3.246, Rwp = 11.975
a = 4.9502(5) Å, b = 8.5725(6) Å, c = 5.0247(3) Å, β = 109.02(7)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.982(2)
M 2c 0 0 0.5 0.018(2)
Li 2b 0 0.5 0 0.605(5)
M 2b 0 0.5 0 0.395(5)
Li 4g 0 0.1642(2) 0 0.031(5)
M 4g 0 0.1624(2) 0 0.969(5)
Li 4h 0 0.681(1) 0.5 0.978(1)
M 4h 0 0.681(1) 0.5 0.022(1)
O 4i 0.217(2) 0 0.213(1) 1
O 8j 0.263(1) 0.3154(6) 0.2303(7) 1
(B-2)
S = 2.5756, RB = 11.247, RF = 7.649, Rwp = 19.371
a = 4.93366(5) Å, b = 8.54179(6) Å, c = 5.02738(3) Å, β = 109.18(7)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.946(5)
M 2c 0 0 0.5 0.054(5)
Li 2b 0 0.5 0 0.596(5)
M 2b 0 0.5 0 0.404(5)
Li 4g 0 0.1642(2) 0 0.059(5)
M 4g 0 0.1624(2) 0 0.941(7)
Li 4h 0 0.681(1) 0.5 0.970(3)
M 4h 0 0.681(1) 0.5 0.030(1)
O 4i 0.216(1) 0 0.220(1) 1
O 8j 0.265(2) 0.3327(7) 0.2250(7) 1
(C-1)
S = 1.8172, RB = 4.806, RF = 5.012, Rwp = 13.040
a = 4.95601(2) Å, b = 8.5612(3) Å, c = 5.0164(1) Å, β = 109.109(4)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.950(8)
M 2c 0 0 0.5 0.050(8)
Li 2b 0 0.5 0 0.349(6)
M 2b 0 0.5 0 0.651(6)
Li 4g 0 0.1646(3) 0 0.098(6)
M 4g 0 0.1646(3) 0 0.902(6)
Li 4h 0 0.681(1) 0.5 0.973(4)
M 4h 0 0.681(1) 0.5 0.027(4)
O 4i 0.215(2) 0 0.221(2) 1
O 8j 0.269(2) 0.3152(6) 0.227(1) 1
(C-2)
S = 2.0646, RB = 4.020, RF = 2.430, Rwp = 15.57
a = 4.9300(3) Å, b = 8.5641(3) Å, c = 5.0221(4) Å, β = 109.060(6)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.958(8)
M 2c 0 0 0.5 0.042(8)
Li 2b 0 0.5 0 0.474(7)
M 2b 0 0.5 0 0.526(7)
Li 4g 0 0.163(4) 0 0.076(7)
M 4g 0 0.163(4) 0 0.924(8)
Li 4h 0 0.692(1) 0.5 0.970(4)
M 4h 0 0.692(1) 0.5 0.030(4)
O 4i 0.233(2) 0 0.216(2) 1
O 8j 0.252(3) 0.320(1) 0.228(1) 1
(D-1)
S = 2.20823, RB = 5.329, RF = 4.797, Rwp = 14.826
a = 4.9560(2) Å, b = 8.5800(3) Å, c = 5.0154(1) Å, β = 109.140(2)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.901(7)
M 2c 0 0 0.5 0.099(7)
Li 2b 0 0.5 0 0.013(9)
M 2b 0 0.5 0 0.997(9)
Li 4g 0 0.1667(6) 0 0.111(9)
M 4g 0 0.1667(6) 0 0.889(9)
Li 4h 0 0.676(3) 0.5 0.980(7)
M 4h 0 0.676(3) 0.5 0.020(7)
O 4i 0.237(3) 0 0.213(2) 1
O 8j 0.232(3) 0.341(1) 0.229(1) 1
(D-2)
S = 2.1854, RB = 5.430, RF = 4.695, Rwp = 15.224
a = 4.9546(2) Å, b = 8.5868(2) Å, c = 5.0164(1) Å, β = 109.129(3)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.912(6)
M 2c 0 0 0.5 0.088(6)
Li 2b 0 0.5 0 0.007(6)
M 2b 0 0.5 0 0.993(6)
Li 4g 0 0.1631(7) 0 0.092(6)
M 4g 0 0.1631(7) 0 0.908(6)
Li 4h 0 0.670(3) 0.5 0.993(3)
M 4h 0 0.670(3) 0.5 0.007(3)
O 4i 0.231(2) 0 0.215(3) 1
O 8j 0.240(2) 0.3313(9) 0.236(2) 1
(E-1)
S = 2.0025, RB = 3.911, RF = 3.000, Rwp = 13.149
a = 4.9556(8) Å, b = 8.5618(9) Å, c = 5.0235(5) Å, β = 109.09(1)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.965(4)
M 2c 0 0 0.5 0.035(4)
Li 2b 0 0.5 0 0.453(2)
M 2b 0 0.5 0 0.547(2)
Li 4g 0 0.1716(3) 0 0.049(6)
M 4g 0 0.1716(3) 0 0.951(6)
Li 4h 0 0.604(1) 0.5 0.986(6)
M 4h 0 0.604(1) 0.5 0.014(6)
O 4i 0.228(2) 0 0.215(1) 1
O 8j 0.245(2) 0.3265(8) 0.2271(9) 1
(E-2)
S = 2.2591, RB = 5.122, RF = 2.480, Rwp = 15.030
a = 4.9488(1) Å, b = 8.56458(1) Å, c = 5.02165(6) Å, β = 109.0637(1)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.941(3)
M 2c 0 0 0.5 0.059(3)
Li 2b 0 0.5 0 0.514(6)
M 2b 0 0.5 0 0.486(6)
Li 4g 0 0.1623(3) 0 0.075(6)
M 4g 0 0.1623(3) 0 0.925(6)
Li 4h 0 0.667(3) 0.5 0.998(2)
M 4h 0 0.667(3) 0.5 0.002(2)
O 4i 0.204(2) 0 0.219(1) 1
O 8j 0.257(2) 0.3142(9) 0.2274(8) 1
(F-1)
S = 1.8354, RB = 3.655, RF = 3.172, Rwp = 11.935
a = 4.9386(5) Å, b = 8.5518(6) Å, c = 5.0174(3) Å, β = 108.997(7)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.968(5)
M 2c 0 0 0.5 0.032(5)
Li 2b 0 0.5 0 0.509(2)
M 2b 0 0.5 0 0.491(2)
Li 4g 0 0.1687(6) 0 0.06(2)
M 4g 0 0.1687(6) 0 0.94(2)
Li 4h 0 0.664(3) 0.5 0.991(2)
M 4h 0 0.664(3) 0.5 0.009(2)
O 4i 0.272(2) 0 0.235(1) 1
O 8j 0.234(1) 0.3480(6) 0.2184(7) 1
(F-2)
S = 2.0422, RB = 6.826, RF = 4.087, Rwp = 15.235
a = 4.93775(2) Å, b = 8.55114(3) Å, c = 5.01752(1) Å, β = 109.0085(4)°
Atom Site x y z Occ-refined
Li 2c 0 0 0.5 0.967(3)
M 2c 0 0 0.5 0.033(3)
Li 2b 0 0.5 0 0.541(5)
M 2b 0 0.5 0 0.459(5)
Li 4g 0 0.1687(8) 0 0.057(5)
M 4g 0 0.1687(8) 0 0.943(5)
Li 4h 0 0.664(2) 0.5 0.990(6)
M 4h 0 0.664(2) 0.5 0.010(6)
O 4i 0.268(1) 0 0.235(1) 1
O 8j 0.231(1) 0.3509(5) 0.2188(6) 1

Table 4 Summary of the occupancy and occupancy difference of Li+ ions at 2c, 2b, 4g and 4h sites. The numbers correspond to those in Fig. 5: 1–3, 11, 12, 14, and 15 (yellow), 4, 10, 13, and 16 (pink), and 5–9 and 17–21 (green)
Sample no. Occupancy of Li+ ions calculated from Rietveld refinement analysis
Prepared by quenched cooling (A) Prepared by slow cooling (B) Ideal values for C2/m (C)
2c 2b 4g 4h 2c 2b 4g 4h 2c 2b 4g 4h
1 0.975 0.748 0.040 0.996 0.954 0.546 0.054 0.998 1 0.8 0 1
2 0.987 0.633 0.044 0.970 0.953 0.552 0.054 0.983 1 0.7 0 1
3 0.982 0.605 0.031 0.978 0.946 0.513 0.059 0.970 1 0.6 0 1
4 0.964 0.456 0.083 0.976 0.941 0.428 0.059 0.957 1 0.5 0 1
5 0.950 0.349 0.098 0.973 0.958 0.474 0.076 0.970 1 0.4 0 1
6 0.869 0.251 0.070 0.972 0.899 0.260 0.071 0.995 1 0.3 0 1
7 0.829 0.283 0.096 0.991 0.885 0.188 0.065 0.995 1 0.2 0 1
8 0.902 0.250 0.092 0.973 0.938 0.139 0.076 0.994 1 0.1 0 1
9 0.901 0.013 0.111 0.980 0.912 0.007 0.092 0.993 1 0 0 1
10 0.965 0.464 0.049 0.986 0.957 0.519 0.070 0.997 1 0.6 0 1
11 0.991 0.516 0.090 0.983 0.980 0.485 0.109 0.977 1 0.6 0 1
12 0.982 0.498 0.040 0.986 0.979 0.464 0.083 0.985 1 0.6 0 1
13 0.968 0.509 0.052 0.999 0.957 0.511 0.057 0.970 1 0.6 0 1
14 0.961 0.703 0.007 0.986 0.930 0.597 0.047 0.975 1 0.8 0 1
15 0.970 0.639 0.037 0.984 0.949 0.568 0.044 0.972 1 0.7 0 1
16 0.949 0.481 0.068 0.981 0.952 0.403 0.076 0.958 1 0.5 0 1
17 0.951 0.348 0.073 0.972 0.962 0.361 0.052 0.987 1 0.4 0 1
18 0.937 0.258 0.065 0.966 0.950 0.296 0.050 0.981 1 0.3 0 1
19 0.877 0.169 0.087 0.975 0.939 0.181 0.062 0.985 1 0.2 0 1
20 0.892 0.227 0.113 0.977 0.948 0.124 0.064 0.970 1 0.1 0 1
21 0.888 0.162 0.022 0.972 0.921 0.074 0.049 0.973 1 0 0 1
Sample no. Occupancy difference of Li+ ions
Occupancy difference at 2c site Occupancy difference at 2b site Occupancy difference at 4g site Occupancy difference at 4h site
(D) = (A) − (C) (E) = (B) − (C) (F) = (A) − (C) (G) = (B) − (C) (H) = (A) − (C) (I) = (B) − (C) (J) = (A) − (C) (K) = (B) − (C)
1 0.03 0.05 0.05 0.25 −0.04 −0.05 0.00 −0.05
2 0.01 0.05 0.07 0.15 −0.04 −0.05 0.03 −0.01
3 0.02 0.05 −0.01 0.09 −0.03 −0.06 0.02 −0.12
4 0.04 0.06 0.04 0.07 −0.08 −0.06 0.02 −0.02
5 0.05 0.04 0.05 −0.07 −0.10 −0.05 0.03 −0.09
6 0.13 0.10 0.05 0.04 −0.07 −0.07 0.03 −0.01
7 0.17 0.12 −0.08 0.01 −0.10 −0.07 0.01 −0.01
8 0.10 0.06 −0.15 −0.04 −0.09 −0.08 0.03 −0.03
9 0.10 0.09 −0.01 −0.01 −0.11 −0.09 0.02 −0.01
10 0.04 0.04 0.14 0.08 −0.05 −0.07 0.01 0.00
11 0.01 0.02 0.08 0.12 −0.09 −0.11 0.02 −0.02
12 0.02 0.02 0.10 0.14 −0.04 −0.08 0.01 −0.05
13 0.03 0.04 0.09 0.09 −0.05 −0.06 0.00 −0.03
14 0.04 0.07 0.10 0.20 −0.01 −0.05 0.01 −0.02
15 0.03 0.05 0.06 0.13 −0.04 −0.04 0.02 −0.05
16 0.05 0.05 0.02 0.10 −0.07 −0.08 0.02 −0.02
17 0.05 0.04 0.05 0.04 −0.07 −0.05 0.03 0.00
18 0.07 0.05 0.04 0.00 −0.07 −0.05 0.03 0.00
19 0.12 0.06 0.03 0.02 −0.09 −0.06 0.03 −0.02
20 0.11 0.05 −0.13 −0.02 −0.11 −0.06 0.02 −0.08
21 0.11 0.08 −0.16 0.07 −0.02 −0.05 0.03 −0.07

The occupancies of Li+ ions in the 2c, 2b, 4g and 4h sites, whose definitions are explained in Fig. 9 and which were analyzed with Rietveld refinement analysis, of the samples prepared by quenching and slow cooling are summarized in Table 4. In order to identify the difference in the crystal structure of the samples prepared by different cooling processes, the occupancies of the Li+ ions in the 2c, 2b, 4g and 4h sites of the samples were compared with the ideal values for the C2/m space group in each composition, and the values are listed in Table 4. By comparing the occupancies listed in Table 4, we tried to find the trend of the preferable cooling process to observe high discharge capacity. Unfortunately, no trend could be found by comparing the occupancies at each site. So, we considered the comparison of the total values of difference between the experimental and ideal values at the 2c, 2b, 4g and 4h sites in each sample to quantify the degree of crystallinity of the samples for the C2/m space group. The total difference is defined by eqn (2). The definitions of D, E, F, G, H, I, J and K are the same as those in Table 4.

 
Total difference = |D| + |F| + |H| + |J| for the samples prepared by quenching = |E| + |G| + |I| + |K| for the samples prepared by slow cooling (2)


image file: d0ra06680j-f9.tif
Fig. 9 Definition of the sites occupied by Li+ ions in the space group of C2/m.

The total differences in the samples prepared by the quenching and slow cooling processes were plotted. Fig. 10 shows these corresponding plots for the LLO samples prepared by (A) quenching and (B) slow cooling processes. The definition of the colors for the bars is the same as that used for the difference in the discharge capacity between the samples prepared by quenching and slow cooling in Fig. 5. In the figure, lower bars mean that the crystal structure of the LLO samples take a more ideal structure with the C2/m space group. Conversely, when the samples showed higher bars, the samples take on a more disordered structure for the C2/m space group. In (A), samples 1, 2, 3, 11, 12, 14 and 15 (yellow bars) exhibiting higher discharge capacity with the quenched cooling process showed a lower total difference of occupancies among the samples. On the other hand, samples 5, 6, 7, 8, 9, 17, 18, 19, 20 and 21 (green bars) showing higher discharge capacity (when the slow cooling process was used) showed a higher total difference of occupancies among the samples. In (B), samples 1, 2, 3, 11, 12, 14 and 15 (yellow bars) have a higher total difference, and samples 5, 6, 7, 8, 9, 17, 18, 19, 20 and 21 (green bars) have a lower total difference. Samples 1, 2, 3, 11, 12, 14 and 15 tend to approach the ideal structure with the C2/m space group when the samples are quenched. Conversely, when the samples are cooled slowly, their structures develop a low degree of ordering of the crystal structure with the C2/m space group. Samples 5, 6, 7, 8, 9, 17, 18, 19, 20 and 21 show the opposite trend. In addition, as the LLO samples have a more ideal structure with the C2/m space group, the samples show higher discharge capacity. Samples 1, 2, 3, 11, 12, 14 and 15 contain a Li2MnO3 content of over 60%. The content rate of Li2MnO3 has control over the degree of crystallinity, and the better cooling process for obtaining higher capacity. It has been observed that the LLOs containing the Li2MnO3 content of over 60% have the crystal structure, which has the ideal form close to the C2/m space group, in the quenched cooling process. However, the LLOs containing the Li2MnO3 at less 60% can also have this crystal structure after the slow cooling process. The reason why this is the case is not understood. This question will be analyzed with molecular dynamics and density functional theory in our next step.


image file: d0ra06680j-f10.tif
Fig. 10 The total differences between the experimental and theoretical occupancies of Li+ ions at 2c, 2b, 4g and 4h sites in the LLO samples. Experimental values were obtained with the samples prepared with the (1) quenched cooling and (2) slow cooling processes. Yellow, pink and green colors correspond to those in Fig. 5, respectively. The experimental and theoretical occupancies of Li+ ions at the 2c, 2b, 4g and 4h sites are taken from Table 3.

4. Conclusions

In this study, in order to clarify the effect of the cooling process of Li-rich solid-solution layered oxide (LLO) materials on the cathode performance in lithium ion batteries, two types of cooling processes were compared. These two processes were (1) the quenching of the LLO samples with liquid nitrogen, and (2) the slow cooling with the controlled decreasing rate of the temperature in the furnace where the LLO samples were placed. The two cooling processes were each applied to the LLO samples, and then the charging/discharging cycle performance of the LLO samples was obtained. From these results, the necessity of the quenching process for the LLO samples to exhibit high charging/discharging capacities depended on the composition of the LLO samples. As the composition of the tested LLO samples deviated from the composition of the Li[Li0.20Mn0.58Ni0.18Co0.04]O2 (Li2MnO3 (60%)–LiNi0.5Mn0.5O2 (30%)–LiNi1/3Co1/3Mn1/3O2 (10%)) sample, which exhibited the highest charging/discharging capacities among the tested LLO samples, the effect of the quenching process on the charging/discharging capacities became weaker. The LLO samples prepared with the slow cooling process exhibited higher charging/discharging capacities when compared with the LLO samples prepared with the quenching process. The structural analysis of the pXRD patterns of the LLO samples indicated that the samples exhibiting high charging/discharging capacities had a high degree of crystallinity of LLO samples for the space group C2/m. This means that there was a low degree of cation mixing between the Li+ and Ni2+ ions, regardless of the type of cooling process. This study showed that the tendency that a high degree of crystallinity of LLO samples for the space group C2/m was needed for the LLO samples to exhibit high charging/discharging capacities. Furthermore, it was found that the cooling process is not restricted for the LLO samples to exhibit high capacities to the quenching process, and which process is better depended on the composition of the LLO samples. Even in the cooling process for the LLO samples that had the same percentage of Li2MnO3 in the LLO samples, the necessity of the quenching process was different. There were also samples that needed the slow cooling process to exhibit higher capacities. The reason why the cooling process required for high capacities is different for samples, depending on the composition, is not clear. The elucidation of this question is in progress.

Conflicts of interest

There are no conflicts to declare.

Acknowledgements

This work was financially supported by the Kato Foundation for the Promotion of Science, Japan (F. Nomura). The authors are grateful to Dr Toshiaki Ina for help with the QXAFS measurements at BL01B01 of SPring-8 (Proposal No. 2019A1316).

References

  1. M. M. Thackeray, S.-H. Kang, C. S. Johnson, J. T. Vaughey, R. Benedek and S. A. Hackney, Li2MnO3-stabilized LiMO2 (M = Mn, Ni, Co) electrodes for lithium-ion batteries, J. Mater. Chem., 2007, 17, 3112–3125 RSC.
  2. J. Zheng, J. Xiao and J.-G. Zhang, The roles of oxygen non-stoichiometry on the electrochemical properties of oxide-based cathode materials, Nano Today, 2016, 11, 678–694 CAS.
  3. L. Riekehr, J. Liu, B. Schwarz, F. Sigel, I. Kerkamm, Y. Xia and H. Ehrenberg, Effect of pristine nanostructure on first cycle electrochemical characteristics of lithium-rich lithiumenickelecobaltemanganeseoxide cathode ceramics for lithium ion batteries, J. Power Sources, 2016, 306, 135–147 CrossRef CAS.
  4. K. A. Jarvis, Z. Deng, L. F. Allard, A. Manthiram and P. J. Ferreira, Atomic Structure of a Lithium-Rich Layered Oxide Material for Lithium-Ion Batteries: evidence of a Solid Solution, Chem. Mater., 2011, 23, 3614–3621 CrossRef CAS.
  5. A. R. Armstrong, M. Holzapfel, P. Novak, C. C. Johnson, S.-H. Kang, M. M. Thackeray and P. G. Bruce, Demonstrating Oxygen Loss and Associated Structural Reorganization in the Lithium Battery Cathode Li[Ni0.2Li0.2Mn0.6]O2, J. Am. Chem. Soc., 2006, 128, 8694–8698 CrossRef CAS.
  6. J. Hong, H.-D. Lim, M. Lee, S.-W. Kim, H. Kim, S.-T. Oh, G.-C. Chung and K. Kang, Critical role of oxygen evolved from layered Li–excess metal oxides in lithium rechargeable batteries, Chem. Mater., 2012, 24, 2692–2697 CrossRef CAS.
  7. F. Nomura, Y. Liu, T. Tanabe, N. Tamura, T. Tsuda, T. Hagiwara, T. Gunji, T. Ohsaka and F. Matsumoto, Optimization of Calcination Temperature in Preparation of a High Capacity Li-rich Solid-Solution Li[Li0.2Ni0.18Co0.03Mn0.58]O2 Material and Its Cathode Performance in Lithium Ion Battery, Electrochim. Acta, 2018, 269, 321–330 CrossRef CAS.
  8. F. Nomura, Y. Liu, T. Tanabe, T. Gunji, T. Tsuda, S. Ugawa, H. Lee, T. Ohsaka and F. Matsumoto, Elucidation of Key Factors of Water-Resistance of Li-Rich Solid-Solution Layered Oxide Cathode Materials Applicable to a Water-Based Cathode Preparation Process for Li-Ion Battery, Electrochim. Acta, 2018, 283, 478–487 CrossRef CAS.
  9. T. Tsuda, H. Kokubun, Y. Asaoka, K. Miyamoto, Y. Mochizuki, T. Gunji, T. Tanabe, S. Kaneko, T. Ohsaka and F. Matsumoto, Dependences of Discharge Capacity, Retention of Discharge Capacity, Average Discharge Voltage and Energy Density, and Rate Capability on the Composition of xLi2MnO3-yLiNi1/2Mn1/2O2-(1-x-y)LiNi1/3Co1/3Mn1/3O2 Li-rich Solid-Solution Cathode Materials for Li-Ion Battery, ECS Trans., 2017, 75(20), 173–187 CrossRef CAS.
  10. F. Nomura, T. Tanabe, T. Gunji and F. Matsumoto, Effect of the Cooling Process on the Structure and Charge/Discharge Cycling Performance in Li[Li0.20Mn0.58Ni0.18Co0.04]O2 Li-rich Solid Solution Layered Oxide Cathode Materials for Li-Ion Battery, ECS Trans., 2018, 85(13), 1497–1505 CrossRef CAS.
  11. E. McCalla, A. W. Rowe, C. R. Brown, L. R. P. Hacquebard and J. R. Dahn, How phase transformations during cooling affect Li-Mn-Ni-O positive electrodes in lithium ion batteries, J. Electrochem. Soc., 2013, 160, A1134–A1138 CrossRef CAS.
  12. B. R. Long, J. R. Croy, F. Dogan, M. R. Suchomel, B. Key, J. Wen, D. J. Miller, M. M. Thacheray and M. Balasubramanian, Effect of Cooling Rates on Phase Separation in 0.5Li2MnO3·0.5LiCoO2 Electrode Materials for Li-Ion Batteries, Chem. Mater., 2014, 26, 3565–3572 CrossRef CAS.
  13. Y. Zhang, Y. Zhang, L. Wang, X. He, J. Yang, Y. Jin and K. Zhang, Effect of cooling on the structure and electrochemical properties of 0.3Li2MnO3·0.7LiNi0.5Mn0.5O2 cathode material, Ionics, 2015, 21, 1819–1825 CrossRef CAS.
  14. A. Jena, C.-H. Lee, W. K. Pang, V. K. Peterson, N. Sharma, C.-C. Wang, Y.-F. Song, C.-C. Lin, H. Chang and R.-S. Liu, Capacity enhancement of the quenched Li-Ni-Mn-Co oxide high-voltage Li-ion battery positive electrode, Electrochim, Acta, 2017, 236, 10–17 CAS.
  15. E. McCalla, C. M. Lowartz, C. R. Brown and J. R. Dahn, Formation of layered–layered composites in the Li–Co–Mn oxide pseudoternary system during slow cooling, Chem. Mater., 2013, 25, 912–918 CrossRef CAS.
  16. N. Yabuuchi and T. Ohzuku, Novel lithium insertion material of LiCo1/3Ni1/3Mn1/3O2 for advanced lithium-ion batteries, J. Power Sources, 2003, 119–121, 171–174 CrossRef CAS.
  17. Y. Makimura and T. Ohzuku, Lithium insertion material of LiNi1/2Mn1/2O2 for advanced lithium-ion batteries, J. Power Sources, 2003, 119–121, 156–160 CrossRef CAS.
  18. X. Li, W. Ge, H. Wang, X. Yan, B. Deng, T. Chen and M. Qu, Enhancing cycle stability and storage property of LiNi0.8Co0.15Al0.05O2 by using fast cooling method, Electrochim. Acta, 2017, 227, 225–234 CrossRef CAS.
  19. B. Ravel and M. Newville, THENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT, J. Synchrotron Radiat., 2005, 12, 537–541 CrossRef CAS.
  20. A. Ito, D. Li, Y. Ohsawa and Y. Sato, A new approach to improve the high-voltage cyclic performance of Li-rich layered cathode material by electrochemical pre-treatment, J. Power Sources, 2008, 183, 344–346 CrossRef CAS.
  21. A. Ito, D. C. Li, Y. Sato, M. Arao, M. Watanabe, M. Hatano, H. Horie and Y. Ohsawa, Cyclic deterioration and its improvement for Li-rich layered cathode material Li[Ni0.17Li0.2Co0.07Mn0.56]O2, J. Power Sources, 2010, 195, 567–573 CrossRef CAS.
  22. C. R. Fell, K. J. Carroll, M. Chi and Y. S. Meng, Synthesis–Structure–Property Relations in Layered, “Li-excess” Oxides Electrode Materials Li[Li1/3−2x/3NixMn2/3−x/3]O2 (x = 1/3, 1/4, and 1/5), J. Electrochem. Soc., 2010, 157, A1202–A1211 CrossRef CAS.
  23. S. Hu, A. S. Pillai, G. Liang, W. K. Pang, H. Wang, Q. Li and Z. Guo, Li-Rich Layered Oxides and Their Practical Challenges: recent Progress and Perspectives, Electrochem. Energy Rev., 2019, 2, 277–311 CrossRef CAS.
  24. S. K. Martha, J. Nanda, G. M. Veith and N. J. Dudney, Electrochemical and rate performance study of high-voltage lithium-rich composition: Li1.2Mn0.525Ni0.175Co0.1O2, J. Power Sources, 2012, 199, 220–226 CrossRef CAS.
  25. A. Ito, Y. Sato, T. Sanada, M. Hatano, H. Horie and Y. Ohsawa, In situ X-ray absorption spectroscopic study of Li-rich layered cathode material Li[Ni0.17Li0.2Co0.07Mn0.56]O2, J. Power Sources, 2011, 196, 6828–6834 CrossRef CAS.
  26. W. Li, B. Song and A. Manthiram, High-voltage positive electrode materials for lithium-ion batteries, Chem. Soc. Rev., 2017, 46, 3006–3059 RSC.
  27. N. Ishida, N. Tamura, N. Kitamura and Y. Idemoto, Crystal and electronic structure analysis and thermodynamic stabilities for electrochemically or chemically delithiatedLi1.2-xMn0.54Ni0.13Co0.13O2, J. Power Sources, 2016, 319, 255–261 CrossRef CAS.
  28. M. Tabuchia, Y. Nabeshima, T. Takeuchi, H. Kageyama, K. Tatsumi, J. Akimoto, H. Shibuya and J. Imaizumi, Synthesis and electrochemical characterization of Fe and Ni substituted Li2MnO3—An effective means to use Fe for constructing “Co-free” Li2MnO3 based positive electrode material, J. Power Sources, 2011, 196, 3611–3622 CrossRef.

Footnote

† Electronic supplementary information (ESI) available. See DOI: 10.1039/d0ra06680j
This journal is © The Royal Society of Chemistry 2021
Click here to see how this site uses Cookies. View our privacy policy here.