DOI: 10.1039/D1RA02453A (Paper) RSC Adv., 2021, 11, 23430-23436

Preparation and study of characteristics of LiCoO2/Fe3O4/Li2B2O4 nanocomposites as ideal active materials for electrochemical hydrogen storage

Mahdi Ranjeha, Omid Amiribc, Masoud Salavati-Niasari*a and Mehdi Shabani-Nooshabadia
aInstitute of Nano Science and Nano Technology, University of Kashan, Kashan, P. O. Box 87317-51167, I. R. Iran. E-mail: salavati@kashanu.ac.ir; Fax: +98 315 5913201; Tel: +98 315 5912383
bFaculty of Chemistry, Razi University, Kermanshah, 6714414971, Iran
cDepartment of Chemistry, College of Science, University of Raparin, Rania, Kurdistan Region, Iraq

Received 28th March 2021 , Accepted 2nd June 2021

First published on 5th July 2021

Abstract

The nanocomposites of LiCoO2/Fe3O4/Li2B2O4 were designed by the Pechini route using different fuels for the optimization of their morphology and structure. Compared to other fuels, citric acid can act as both an ideal fuel and a capping agent. The ratio of the EG[thin space (1/6-em)]:[thin space (1/6-em)]H2O mixture is another parameter, which was studied in terms of its effects on the structural characterization. The optimized sample with a rod shape was selected to compare with the bulk sample through electrochemical hydrogen storage capacity. The discharge capacity for rod-shaped nanocomposites measured was 1284 mA h g−1. However, the discharge capacity for the bulk morphology was calculated to be about 694 mA h g−1. The magnetic, electrochemical and structural analyses were performed to investigate the properties of LiCoO2/Fe3O4/Li2B2O4 nanocomposites.

1. Introduction

At present, the usage of fossil fuels has been restricted due to the release of pollutants from their combustion and the defective origins. In order to meet the energy demands, researchers are designing prevalent and up-to-date replacement sources for energy storage. Electrochemical hydrogen sorption is a potential technique for energy storage in the nano-scale compounds in terms of reproducibility, safety and clean sources because of their availability, supreme proficiency, simple technique and low pollution. Designing novel active materials with improved efficiency, amplified structure or compound, and sustainable consumption is a crucial target in energy storage fields.1–3

The structural stability, structural chemistry, mechanical attributes, and physical properties are remarkable factors for the selection of energy storage materials. The selection of suitable active materials and the design of an improved structure are important tasks for achieving high performance in electrochemical energy storage. Therefore, metal oxide-supported materials are key options to design potential active materials for electrodes utilized in energy storage.4–6

Nano-scale structures with different compositions are synthesized for the energy storage application via chemical procedures, which are simple and afford high yield products. These chemical methods include ultrasonic-based precipitation, microwave-based precipitation, fuel-assisted sol–gel method, solvothermal and thermal treatment routes.7–10 The metal oxide materials applied in the energy storage fields are comprehensive such as borate, vanadate, spinels, and perovskites. The central metals in these structures usually are cobalt, iron, nickel, magnesium, zinc, etc. The important factor for the selection of the central metal is the ability to change the oxidation number in the redox process during electrochemical charge and discharge.11–15

In the recent study, the ternary nanocomposites of LiCoO2/Fe3O4/Li2B2O4 were designed by the one-step Pechini procedure by changing the operational synthesis parameters to achieve an ideal morphology. The ideal morphology of rod-shape in the nano-scale was achieved using citric acid and compared with the bulk structures in terms of electrochemical hydrogen sorption properties. The designed rod-shaped LiCoO2/Fe3O4/Li2B2O4 nanocomposites show a discharge capacity of 1284 mA h g−1 after 15 cycles. Compared to the bulk structures of these nanocomposites with a capacity of 694 mA h g−1, the results confirm the effect of decrease in the size of the sample for hydrogen storage performance of LiCoO2/Fe3O4/Li2B2O4 nanocomposites. Overall, this is the first research to acquire suitable hydrogen capacitor materials synthesized via an easy Pechini method in order to achieve an economic, simple and quick technique.

2. Experiments

Nanocomposites of LiCoO2/Fe3O4/Li2B2O4 were successfully designed through the Pechini route in the presence of diverse fuels. In the first step, Co(NO3)2·6H2O, Fe(NO3)3·9H2O, Li2SO4·H2O and H3BO3 were dissolved in the specified mixing solvent of ethylene glycol and water. The mixture of the solvent was prepared by different ratios of EG and H2O, as summarized in Table 1. Then, the chosen fuel materials were added to the above-mentioned mixture. Four types of structures such as EDTA, phthalic acid, citric acid and tartaric acid could play the dual role in the Pechini reaction as a chelating agent and as a fuel to control the morphology and perform the synthesis reaction. Ethylene diamine was applied in order to control the pH of the reaction at 10. The mixture was heated at 80 °C to form a gel. The obtained gel was dried for 4 h in an oven at 100 °C. Eventually, the dried gel was heat-treated for 4 h at 700 °C to obtain the products.
Table 1 Summary of the synthesized conditions for Pechini-designed nanocomposites
Sample no. Fuel EG[thin space (1/6-em)]:[thin space (1/6-em)]H2O
S1 EDTA 1[thin space (1/6-em)]:[thin space (1/6-em)]1
S2 Phthalic acid 1[thin space (1/6-em)]:[thin space (1/6-em)]1
S3 Citric acid 1[thin space (1/6-em)]:[thin space (1/6-em)]1
S4 Tartaric acid 1[thin space (1/6-em)]:[thin space (1/6-em)]1
S5 Citric acid 2[thin space (1/6-em)]:[thin space (1/6-em)]1
S6 Citric acid 3[thin space (1/6-em)]:[thin space (1/6-em)]1
S7 Citric acid 4[thin space (1/6-em)]:[thin space (1/6-em)]1

In order to investigate the hydrogen sorption capacity of the samples, the electrochemical chronopotentiometry technique was utilized in the assembled cell using Pt (counter electrode), Ag/AgCl (reference electrode) and working electrodes in the electrolyte medium of KOH (2 M). The applied current density is constant 1 mA. Therefore, the potentials of the working electrode versus reference electrode were recorded by applying constant current between the working and counter electrodes. The working electrode was prepared by coating a thin layer of fabricated nanocomposites on the copper substrate, which dried at 60 °C to form a uniform layer on the copper foam.

3. Characterization details

In order to certify the phase purity of the designed nanocomposites, the XRD diffractograms were recorded via the X-ray diffraction technique. As shown in Fig. 1, the three components existed in the texture of composites. LiCoO2 (JCPDS 16-0427), Fe3O4 (JCPDS 89-0951) and Li2B2O4 (JCPDS 11-0407) items can match with the displayed diffracted peaks. The sharp diffracted peaks present a highly crystallized structure for designed nanocomposites. The EDS result for sample 3 is presented in Fig. 2. The result of the energy dispersive spectroscopy confirms that the nanocomposites are composed of B, Co, Fe and O elements (Fig. 2). It is well-known that the EDS pattern reveals the high purity of the product.
image file: d1ra02453a-f1.tif
Fig. 1 XRD diffractogram of sample 3 (synthesized by citric acid).

image file: d1ra02453a-f2.tif
Fig. 2 EDS result for sample 3 (synthesized by citric acid).

The achieved profile for sample 3 is presented in Fig. 3. The situated peaks at 405, 684 and 1132 cm−1 related to Li2B2O4 structures in terms of vibrating Li–O, bending B–O–B and stretching B–O bonds, respectively. The stretching mode of the [CoO6] octahedron is supported by the peak located at 622 cm−1, which corresponds to the LiCoO2 structure. The observed weak peak at 580 cm−1 can be correlated to the Fe3O4 structure. Also, the remaining molecules of water and carboxylic acid create the bonds of O–H and C–O at 3425, 1689 and 1454 cm−1.11,16,17


image file: d1ra02453a-f3.tif
Fig. 3 FT-IR profile for sample 3 (synthesized by citric acid).

The control of the morphology is a significant issue in the design of nanomaterials, which are applied for energy storage applications. In this study, the effects of diverse fuels on the morphology of the as-synthesized nanocomposites were compared as the first parameter due to the chelating agent role of chosen fuel structures. Fig. 4a–d display the FE-SEM images of the designed nanocomposites in the presence of EDTA, phthalic acid, citric acid, and tartaric acid, respectively. The EDTA-assisted Pechini-synthesized nanocomposites having agglomerated structures are shown in Fig. 4a. The FE-SEM images of the as-fabricated nanocomposites using phthalic acid and tartaric acid (Fig. 4b and d) show the formation of large structures in microscale. As shown in Fig. 4c, the nanocomposites fabricated using citric acid possessed rod-shaped structures in nano-scale. The second parameter for controlling the morphology in this study is the ratio of EG[thin space (1/6-em)]:[thin space (1/6-em)]H2O in the reaction medium owing to the role of EG as a gelling agent. Fig. 5a–d represents the ratios of 2[thin space (1/6-em)]:[thin space (1/6-em)]1, 3[thin space (1/6-em)]:[thin space (1/6-em)]1 and 4[thin space (1/6-em)]:[thin space (1/6-em)]1 of EG[thin space (1/6-em)]:[thin space (1/6-em)]H2O, respectively. FE-SEM images for samples 5 and 6 exhibit large and agglomerated structures (Fig. 5a and b). However, sample 7 (Fig. 5c) prepared in the mixture of EG[thin space (1/6-em)]:[thin space (1/6-em)]H2O (4[thin space (1/6-em)]:[thin space (1/6-em)]1) shows porous structures. Comparing the FE-SEM results, it is found that the designed nanocomposites in the presence of citric acid and the ratio of 1[thin space (1/6-em)]:[thin space (1/6-em)]1 for EG[thin space (1/6-em)]:[thin space (1/6-em)]H2O present an ideal morphology and size, which was chosen as the optimum sample (sample 3). To further analyze the morphology and shape of the optimized sample, the TEM images were obtained for sample 3, as shown in Fig. 6. The results of the obtained TEM images confirm the morphology of sample 3.


image file: d1ra02453a-f4.tif
Fig. 4 FE-SEM images of nanocomposites designed by using (a) EDTA, (b) phthalic acid, (c) citric acid, and (d) tartaric acid [sample 1–4].

image file: d1ra02453a-f5.tif
Fig. 5 FE-SEM images of the designed nanocomposites by citric acid in the medium of EG[thin space (1/6-em)]:[thin space (1/6-em)]H2O by different ratios (a) 2[thin space (1/6-em)]:[thin space (1/6-em)]1, (b) 3[thin space (1/6-em)]:[thin space (1/6-em)]1 and (c) 4[thin space (1/6-em)]:[thin space (1/6-em)]1.

image file: d1ra02453a-f6.tif
Fig. 6 TEM images for the synthesized nanocomposites by citric acid (sample 3).

The porosity and surface characteristics were determined using the BET method for sample 3, which is presented in Fig. 7. The BET method was also applied to assess the surface area and pore volume of the designed nanocomposites with rod-shaped structures, as shown in the nitrogen adsorption isotherms measured at 77 K. The specific surface area, pore volume, and average pore size for sample 3 is 1.1896 m2 g−1, 0.010677 cm3 g−1, and 35.902 nm, respectively. The pore size distribution of the nanocomposites is displayed in Fig. 7b. Finally, BET results affirm that the surface area and porosity are important issues for the facile ion transportation to increase the electrochemical performance of the active materials in the electrode matrix.18


image file: d1ra02453a-f7.tif
Fig. 7 (a) BET and (b) BJH plot for sample 3.

The properties of LiCoO2/Fe3O4/Li2B2O4 nanocomposites in terms of magnetic ability were studied by the VSM technique. The hysteresis loop for sample 3 is displayed in Fig. 8. It can be seen that the plots illustrate a ferromagnetic behavior. Also, the maximum saturation magnetization (Ms) obtained for LiCoO2/Fe3O4/Li2B2O4 nanocomposites with the rod-shaped structure is 0.388 emu.


image file: d1ra02453a-f8.tif
Fig. 8 VSM hysteresis of sample 3 at room temperature.

4. Electrochemical hydrogen storage

Size and morphology are significant factors in energy storage materials. The active materials in the nanoscale can show higher performance than bulk materials due to the surface effects between the electrolyte and active sites in the nanomaterials. The hydrogen sorption capacity for the obtained nanocomposites of LiCoO2/Fe3O4/Li2B2O4 with rod-shaped structures was compared with that of bulk structures. For this purpose, chronopotentiometry tests were conducted in the three-electrode cell (including Pt, Ag/AgCl and working electrodes) in the electrolyte medium of KOH (2 M). The applied current density is constant 1 mA. The discharge capacity for the chosen samples was computed using the C = IΔt/mΔV formula.19 The discharge capacity for rod-shaped nanocomposites (sample 3) was 1284 mA h g−1 after 15 cycles. However, the bulk sample 2 had a discharge capacity of 694 mA h g−1 after 15 cycles (Fig. 9a and b).
image file: d1ra02453a-f9.tif
Fig. 9 Electrochemical hydrogen storage profiles for 15 cycles. (a) Discharge profiles for bulk (sample 2) and (b) nano rod-shape (sample 3).

Diverse mechanisms for the hydrogen storage of metal oxide materials have been proposed, which comprise the existence of layered structures, morphology and physisorption process.20–22 The morphology and the shape of electrode materials have an incredible impact on the energy storage proficiency. The borate compounds have open channels and layered structures, which are appropriate for storing the ions and transfer them.23 The structure of LiCoO2/Fe3O4/Li2B2O4 nanocomposites assigns facile, rapid and efficacious electron transportation through the electrolyte due to easy access of the electrolyte with the structure of metal oxides. The one-dimensional structures such as wires, rods, or tubes are the most efficient shape for improving the electrochemical proficiency due to the increased surface areas and the shortened ion diffusion paths. The hydrogen storage outcomes figure out a fast surface charge delivery mechanism and higher ion diffusion performance in the electrode materials with the rod-shaped morphology (sample 3), which has a small diameter.24,25 The comparative hydrogen sorption study between nano rod-shape and bulk structures of LiCoO2/Fe3O4/Li2B2O4 nanocomposites are shown in Fig. 9. Also, Fig. 10 shows the cycling performance for samples 2 and 3. On the other hand, physical adsorption occurs in the metal oxides during the charge and discharge processes. The electrolyte of 2 M KOH separates into OH− and H+ (eqn (1)). Created H+ migrates to the working electrode and adsorbs on the surface of the active materials (cathode reaction). The anodic reaction of the charging process occurs in the Pt electrode through an oxidization mechanism. In discharge direction, H2 transports from the working electrode under the alkaline circumstance and becomes water again while freeing an electron. The generated H+ migrates to the surface of active materials in the fabricated working electrode, which can be adsorbed on the surface of metal oxides. The stored H2 in the working electrode should be migrating in the opposite direction when the cell is discharged and converted into water.26

 
H2O + e− ↔ H + OH− (1)
 
LiCoO2/Fe3O4/Li2B2O4 + xH2O + xe− ↔ LiCoO2/Fe3O4/Li2B2O4 − Hx + xOH− (2)
 
H + H ↔ H2 (3)


image file: d1ra02453a-f10.tif
Fig. 10 Cycling performance of the fabricated nanocomposites for (a) bulk (sample 2) and (b) nano rod-shape (sample 3).

The Heyrovsky process occurred due to the suitable electrocatalyst activity of the as-synthesized electrode materials. The synergic effects of Tafel (eqn (3)) and Heyrovsky (eqn (2)) processes led to hydrogen storage in the active materials of LiCoO2/Fe3O4/Li2B2O4 nanocomposites. According to the electrochemical outcomes, LiCoO2/Fe3O4/Li2B2O4 nanocomposites have a potential for hydrogen sorption as novel active materials in energy storage fields due to physisorption and rod-shaped morphology.

5. Conclusion

In summary, the Pechini-synthesized nanocomposites of LiCoO2/Fe3O4/Li2B2O4 were successfully obtained in the ideal condition using citric acid as a fuel. The hydrogen sorption efficiency is compared with that of the bulk structure and the results show an increase in the discharge capacity from 694 to 1284 from bulk to the nano-sized rod-shaped morphology. Therefore, the magnetic nanocomposites of LiCoO2/Fe3O4/Li2B2O4 as a novel candidate can play a suitable role in the energy storage fields.

Conflicts of interest

The authors declare that there are no conflicts of interest regarding the publication of this manuscript.

Acknowledgements

Professor Masoud Salavati-Niasari and co-authors of the Institute of Nano Science and Nano Technology, University of Kashan, IRAN is kindly acknowledged for providing access to the analysis facility by grant no. 159271/80 from University of Kashan and the council of Iran National Science Foundation (INSF, 97017837).

References

  1. J. Abe, E. Ajenifuja and O. Popoola, Hydrogen energy, economy and storage: review and recommendation, Int. J. Hydrogen Energy, 2019, 15072–15086 CrossRef CAS.
  2. D. J. Durbin and C. Malardier-Jugroot, Review of hydrogen storage techniques for on board vehicle applications, Int. J. Hydrogen Energy, 2013, 38, 14595 CrossRef CAS.
  3. A. S. Arico, P. Bruce, B. Scrosati, J.-M. Tarascon and W. Van Schalkwijk, Nanostructured materials for advanced energy conversion and storage devices, Materials for sustainable energy: a collection of peer-reviewed research and review articles from Nature Publishing Group, World Scientific, 2011, pp. 148–159 Search PubMed.
  4. M. M. Farid, A. M. Khudhair, S. A. K. Razack and S. Al-Hallaj, A review on phase change energy storage: materials and applications, Energy Convers. Manage., 2004, 45, 1597–1615 CrossRef CAS.
  5. C. Liu, F. Li, L. P. Ma and H. M. Cheng, Advanced materials for energy storage, Adv. Mater., 2010, 22, E28–E62 CrossRef CAS PubMed.
  6. M. R. Lukatskaya, B. Dunn and Y. Gogotsi, Multidimensional materials and device architectures for future hybrid energy storage, Nat. Commun., 2016, 7, 1–13 Search PubMed.
  7. M. Ghiyasiyan-Arani and M. Salavati-Niasari, Effect of Li2CoMn3O8 nanostructures synthesized by a combustion method on montmorillonite K10 as a potential hydrogen storage material, J. Phys. Chem. C, 2018, 122, 16498–16509 CrossRef CAS.
  8. M. Ghiyasiyan-Arani and M. Salavati-Niasari, Strategic design and electrochemical behaviors of Li-ion battery cathode nanocomposite materials based on AlV3O9 with carbon nanostructures, Composites, Part B, 2020, 183, 107734 CrossRef CAS.
  9. M. Ghiyasiyan-Arani and M. Salavati-Niasari, New Nanocomposites Based on Li–Fe–Mn Double Spinel and Carbon Self-Doped Graphitic Carbon Nitrides with Synergistic Effect for Electrochemical Hydrogen Storage Application, Ind. Eng. Chem. Res., 2019, 58, 23057–23067 CrossRef CAS.
  10. R. Monsef, M. Ghiyasiyan-Arani and M. Salavati-Niasari, Design of Magnetically Recyclable Ternary Fe2O3/EuVO4/g-C3N4 Nanocomposites for Photocatalytic and Electrochemical Hydrogen Storage, ACS Appl. Energy Mater., 2021, 680–695 CrossRef CAS.
  11. M. Ranjeh, F. Beshkar and M. Salavati-Niasari, Sol-gel synthesis of novel Li-based boron oxides nanocomposite for photodegradation of azo-dye pollutant under UV light irradiation, Composites, Part B, 2019, 172, 33–40 CrossRef CAS.
  12. M. Ranjeh, M. Ghiyasiyan-Arani, M. Slavati-Niasari and H. Moayedi, Li4Zn3B4O11/Li2B2O4 Nanocomposites as a Potential Electrode Material for Electrochemical Hydrogen Storage; Insight of Fabrication and Morphology Controlling, J. Mater. Res. Technol., 2020, 9, 2028–2036 CrossRef CAS.
  13. M. Ranjeh, M. Masjedi-Arani, O. Amiri and M. Salavati-Niasari, Li2MnO3/LiMnBO3/MnFe2O4 ternary nanocomposites: Pechini synthesis, characterization and photocatalytic performance, Int. J. Hydrogen Energy, 2020, 45, 21241–21251 CrossRef CAS.
  14. A. Salehabadi, M. Salavati-Niasari and M. Ghiyasiyan-Arani, Self-assembly of hydrogen storage materials based multi-walled carbon nanotubes (MWCNTs) and Dy3Fe5O12 (DFO) nanoparticles, J. Alloys Compd., 2018, 745, 789–797 CrossRef CAS.
  15. T. Gholami, M. Salavati-Niasari and S. Varshoy, Electrochemical hydrogen storage capacity and optical properties of NiAl2O4/NiO nanocomposite synthesized by green method, Int. J. Hydrogen Energy, 2017, 42, 5235 CrossRef CAS.
  16. N. De Geyter, R. Morent and C. Leys, Surface characterization of plasma-modified polyethylene by contact angle experiments and ATR-FTIR spectroscopy, Surf. Interface Anal., 2008, 40, 608–611 CrossRef CAS.
  17. F. Khatun, M. Gafur, M. Ali, M. Islam and M. Sarker, Impact of lithium composition on structural, electronic and optical properties of lithium cobaltite prepared by solid-state reaction, J. Sci. Res., 2014, 6, 217–231 CrossRef CAS.
  18. F. S. Razavi, M. S. Morassaei, A. Salehabadi, M. Ghiyasiyan-Arani and M. Salavati-Niasari, Structural characterization and electrochemical hydrogen sorption performances of the polycrystalline Ba2Co9O14 nanostructures, J. Alloys Compd., 2019, 777, 252–258 CrossRef CAS.
  19. M. Masjedi-Arani, M. Ghiyasiyan-Arani, O. Amiri and M. Salavati-Niasari, CdSnO3-graphene nanocomposites: ultrasonic synthesis using glucose as capping agent and characterization for electrochemical hydrogen storage, Ultrason. Sonochem., 2020, 61, 104840 CrossRef CAS PubMed.
  20. P. Bénard and R. Chahine, Storage of hydrogen by physisorption on carbon and nanostructured materials, Scr. Mater., 2007, 56, 803–808 CrossRef.
  21. T. Gholami and M. Salavati-Niasari, Effects of copper: aluminum ratio in CuO/Al2O3 nanocomposite: electrochemical hydrogen storage capacity, band gap and morphology, Int. J. Hydrogen Energy, 2016, 41, 15141–15148 CrossRef CAS.
  22. L. Nazar, G. Goward, F. Leroux, M. Duncan, H. Huang, T. Kerr and J. Gaubicher, Nanostructured materials for energy storage, Int. J. Inorg. Mater., 2001, 3, 191–200 CrossRef CAS.
  23. I. Tsuyumoto and A. Kihara, Synthesis, Characterization and Charge-Discharge Properties of Layer-Structure Lithium Zinc Borate, LiZnBO3, Mater. Sci. Appl., 2013, 4, 246 CAS.
  24. M. Ghiyasiyan-Arani, M. Salavati-Niasari and A. F. Zonouz, Effect of Operational Synthesis Parameters on the Morphology and the Electrochemical Properties of 3D Hierarchical AlV3O9 Architectures for Li-Ion Batteries, J. Electrochem. Soc., 2020, 167, 020544 CrossRef CAS.
  25. G. Yang, H. Song, G. Yang, M. Wu and C. Wang, 3D hierarchical AlV3O9 microspheres: first synthesis, excellent lithium ion cathode properties, and investigation of electrochemical mechanism, Nano Energy, 2015, 15, 281–292 CrossRef CAS.
  26. F. S. Razavi, A. Sobhani, O. Amiri, M. Ghiyasiyan-Arani and M. Salavati-Niasari, Green sol-gel auto-combustion synthesis, characterization and investigation of the electrochemical hydrogen storage properties of barium cobalt oxide nanocomposites with maltose, Int. J. Hydrogen Energy, 2020, 45, 17662–17670 CrossRef CAS.
This journal is © The Royal Society of Chemistry 2021
Click here to see how this site uses Cookies. View our privacy policy here.