Open Access Article
This Open Access Article is licensed under a Creative Commons Attribution-Non Commercial 3.0 Unported Licence

Biosynthesis of Ag/almond shell nanocomposite as a cost-effective and efficient catalyst for degradation of 4-nitrophenol and organic dyes

Maryam Bordbar*ab
aDepartment of Chemistry, Faculty of Science, University of Qom, Qom 37185-359, Iran. E-mail: m.bordbare@gmail.com; Fax: +98 25 32850953; Tel: +98 2532103792
bCenter of Environmental Researches, University of Qom, Qom, Iran

Received 9th October 2016 , Accepted 8th November 2016

First published on 22nd December 2016


Abstract

Silver nanoparticles have been immobilized on the surface of waste almond shell using Ruta graveolens sleeves extract as a reducing and stabilizing agent in the present work. FT-IR spectroscopy, photoluminescence spectroscopy, X-ray diffraction (XRD) patterns, field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS) and transmission electron microscopy (TEM) were used to characterize the almond shell supported silver nanoparticles. The diameters of AgNPs on the almond shell were mostly in the 5–15 nm range. The catalytic performance of the synthesized catalysts was studied in reduction of 4-nitrophenol (4-NP), rhodamine B (RhB) and methylene blue (MB) at ambient temperature. AgNPs/almond shell was found to be a highly active and recyclable catalyst in the related reaction, which can be recovered and reused seven times with no appreciable loss of catalytic activity.


1 Introduction

Noble metal nanoparticles (NPs) have been intensively investigated for the past two decades for a wide range of applications including optics, electronics, sensing, catalysis and biomedicine, given their unique and tunable properties.1,2 Silver, among the noble metals, is particularly attractive due to its very high electrical conductivity, anti-bacterial activity and relatively low cost. Silver nanoparticles (AgNPs) can be applied as catalysts in a number of important chemical processes, including selective alkane and alkene oxidation,2 hydrogenation of dyes,3 4-nitrophenol (4-NP) reduction to 4-aminophenol (4-AP), as an intermediate step in the synthesis of pharmaceutical compounds (e.g., paracetamol).4 As catalysts, AgNPs are usually immobilized onto such appropriate substrates as silica,5 alumina,6 zeolites,7 TiO2[thin space (1/6-em)]8 and different types of carbon compounds9,10 so as to (i) prevent their agglomeration and thus the reduction of their catalytic activity, and (ii) increase their efficiency via suitable interaction with the substrate.2 There are several green synthetic methods, on the other hand, for obtaining stable and size controlled AgNPs and prevention of their agglomeration.11–13 Synthesis of plant mediated silver nanoparticles has been reviewed by Ahmed et al.14 Some plant extracts, such as Capsicum annuum L., Jatropha curcas, Argemone mexicana and Citrus limon extracts, have been shown to form stable nanoparticles due to the presence of reducing agents such as alkaloids, polyphenols and flavonoids, which are major phytoconstituents.15–18

There are several green synthetic methods for preparation of AgNPs.8,19–21 However, the green synthesis of the Ag/almond shell nanocomposite, in which Ruta graveolens leaf extract is used as a reducing agent for Ag(I) conversion to Ag(0), has not been reported.

Ruta graveolens (Fig. 1) is an odoriferous herb of Rutaceae family. Ruta graveolens is the Rue or Rue oil source, referred to as Sadab or Satab in Iran. Ruta graveolens has anti-nociceptive, anti-inflammatory and anti-pyretic activities, possibly due to the plant species inhibiting mediators implicated in pain, inflammation and fever. Protocatechuic, vanillic, syringic, p-coumaric acid and coumarins (Fig. 2) have been detected and quantitatively analyzed in the extract of Ruta graveolens leaves.22 Rutin, whose name originates from the rutin containing Ruta graveolens plant, is a flavonoid glycoside of quercetin, found in many plant species.23


image file: c6ra24977a-f1.tif
Fig. 1 Image of Ruta graveolens plant.

image file: c6ra24977a-f2.tif
Fig. 2 Chemical structures of some compounds in Ruta graveolens extract.

In this work, cheap agricultural waste almond shells as a naturally valuable resource and environmentally friendly support have been used for immobilization of silver nanoparticles (AgNPs).

A very important crop throughout the world's different temperate regions, almonds (Prunus amygdalus L.) account for 35–75% of the total fruit weight.24 Thus, about 0.8–1.7 million tons of almond shell is left annually. The ligno-cellulosic material forming the thick endocarp or husk of the almond tree fruit, separated upon processing the fruit to obtain the edible seeds, almond shell is an agricultural waste with no important industrial application, which is usually incinerated or dumped. Air pollution, soil erosion and decreased soil biological activity are caused by burning agricultural wastes. Application of agricultural residues prevents environmental damages and brings about extra income for farmers.25 Iran, a major producer of almond, exports thousands of tons of almond annually. Thus, almond shell is easily accessible in the country as an agricultural waste. Almond shell consists of cellulose, hemicelluloses and lignin.24,26 The structure of almond shell and its components; especially cellulose, on the other hand, make it appropriate for the production of composites.

The leaf extract of Ruta graveolens has been used in this study as a reducing and stabilizing agent to immobilize AgNPs on the almond shell surface as bio-waste support to form Ag/almond shell nanocomposite in the absence of any harmful reducing or capping agents. This is an environmentally benign alternative route, which avoids the application of hazardous materials. The catalytic activity of Ag/almond shell nanocomposite in the reduction of 4-NP, RhB and MB in the presence of NaBH4 in aqueous media has also been studied. Most importantly, only a slight loss is observed in the catalyst activity of Ag/almond shell nanocomposite after several recycles.

2 Experimental

2.1 Instruments and reagents

Highly pure chemicals were purchased from Merck and Aldrich Chemical Companies. FT-IR spectra were recorded on a Varian model 640 spectrophotometer using pressed KBr pellets. UV-Vis spectra were recorded using a double beam Shimadzu UV-2500 spectrophotometer to ensure the formation of nanoparticles. Varian Cary Eclipse spectrofluorometer was used to record the photoluminescence spectra in a 1 cm optical path quartz cuvette (scan speed = 100 nm min−1, slit width = 5/5 nm). X-ray diffraction (XRD) measurements were carried out using a Philips model X'PertPro diffractometer (Cu Kα = 1.5406 Å) at a scanning rate of 2° min−1 in the 2θ range (10–80). Scanning electron microscopy (SEM) was performed by a TESCAN model VEGA3-XMU equipped with energy dispersive spectroscopy (EDS) analysis. A Philips-EM-2085 transmission electron microscope was used to obtain TEM images at an accelerating voltage of 100.0 kV.

2.2 Preparation of Ruta graveolens leaves extract and Ag/almond shell nanocomposite

Dried leaves of Ruta graveolens (10 g) were powdered and refluxed at 80 °C with deionized water (60 mL) for 1 h, after which the mixture was allowed to cool to room temperature. The aqueous extract of Ruta graveolens leaves was then centrifuged at 6500 rpm and the supernatant was separated by filtration.

In a typical Ag/almond shell nanocomposite synthesis, first, waste almond shells were washed, dried at 90 °C for 6 h in an oven, and mechanically pretreated by crushing in a mill, followed by sieving to separate <40 μm particle size fractions. Then the plant extract (30 mL) was added dropwise to 30 mL of an AgNO3 solution (0.3 g) and almond shell powder (1.0 g) under constant stirring at 70 °C for 2 h. The resulting mixture was then allowed to cool, filtered, washed with distilled water and dried at 80 °C in an oven for 12 h.

2.3 Catalytic reduction of 4-NP, RhB and MB by Ag/almond shell nanocomposite

In a typical run, the catalyst (5.0 mg) was added to a 2.5 mM 4-NP aqueous solution (25 mL). 0.25 M aqueous solution of freshly prepared NaBH4 (25 mL) was then added and the mixture obtained was allowed to stir at ambient temperature until the deep yellow color of the solution turned colorless. UV-Vis spectroscopy was used to monitor the reaction progress. Upon completion of the reaction, the catalyst was simply removed from the reaction media by brief centrifugation, washed several times with deionized water and dried for the next cycle.

In addition, the catalyst (5.0 mg) was added to 3.1 × 10−5 M MB aqueous solution (25 mL). 2.6 × 10−3 M freshly prepared NaBH4 aqueous solution (25 mL) was then added and the resulting mixture was allowed to stir at ambient temperature. UV-Vis spectroscopy was used to monitor the reaction progress. Upon completion of the reaction, the catalyst was simply removed from the reaction media by brief centrifugation, washed several times with deionized water and dried for the next cycle. Similar procedures were used in the catalytic reduction of RhB. Equal amounts of NaBH4 and 5.0 mg of the catalyst were used in each catalytic reaction. The concentration of RhB aqueous solution was 2.0 × 10−5 M.

3 Results and discussion

3.1 Mechanism of reduction of AgNO3 to AgNPs by the phytoconstituents of Ruta graveolens

Ruta graveolens leaf extract has been used as a stabilizing and reducing agent in this work to immobilize AgNPs on the almond shell surface to form Ag/almond shell nanocomposite (Fig. 3). The reduction of Ag(I) ions and the formation of the corresponding AgNPs may be accounted for by the presence of antioxidant phenolic compound (protocatechuic, vanillic, syringic, p-coumaric acid and rutin) in the extract functioning as potent reducing agents.
image file: c6ra24977a-f3.tif
Fig. 3 Flowchart of preparation of Ag/almond shell nanocomposite catalytic reduction and degradation of 4-NP, RhB and MB with Ag/almond shell.

Fig. 4 shows the proposed mechanism for the reduction of Ag+. In this figure, Ag+ ions can form intermediate complexes with phenolic OH groups, which are subsequently oxidized to quinone, reducing Ag+ to AgNPs.15


image file: c6ra24977a-f4.tif
Fig. 4 Mechanism involved in the formation of AgNPs.15

3.2 Characterization of aqueous extract of Ruta graveolens and AgNPs

The bands in 300–400 nm regions in the UV spectrum of leaf extract of the Ruta graveolens (Fig. 5) are associated with the transition localized within coumarin group, whereas the band around 260 nm is due to the absorbance of ring related to the benzoyl system. These are related to the π → π* transitions and indicate the presence of polyphenolics as antioxidant source for green synthesis of nanoparticles.8,27
image file: c6ra24977a-f5.tif
Fig. 5 UV-Vis spectrum of the aqueous extract of the leaves of the Ruta graveolens and green synthesized AgNPs.

For the synthesis of AgNPs from silver ion, the phenolic compound present in the extract acting as the reducing agents. The color change (yellowish brown color) during exposure to plant extract clearly indicated the Ag(I) ion reduction into silver nanoparticles, as shown in the UV-Vis spectra (Fig. 5). Maximum absorbance of green synthesized AgNPs occurred at 430 nm due to the surface plasmon absorption of nanosized spherical silver particles, as our results showed.21

Biomolecules possibly responsible for the capping reduction of AgNPs were identified by FT-IR analysis (Fig. 6a). The peaks at 3500–3400, 1680, 1460, and 1250–1050 cm−1 represent free OH in molecule and OH group forming hydrogen bonds, carbonyl group (C[double bond, length as m-dash]O), stretching C[double bond, length as m-dash]C aromatic ring and C–OH stretching vibrations, respectively. The spectrum shows the presence of phenolics in the plant leaf extract due to the presence of the functional groups in the structure of polyphenolics. The reduction of metal ions and formation of nanocomposite is possibly due to the phenolics in the extract. Fig. 6b shows the FT-IR spectra of extract and AgNPs. FT-IR spectra of AgNPs are characteristically different in the shape and location of signals as a result of the interaction between AgNO3 and the phytochemical sites involved in nanoparticle formation (Fig. 6b). Polyphenolics could be possibly adsorbed on the surface of metal nanoparticles by interaction through π-electrons in the absence of other strong ligating agents. The synthetic AgNPs seem to be stabilized by an organic layer originating from the extract of leaves of Ruta graveolens. Polyphenolics well stabilize these nanoparticles via the interaction of AgNPs with the OH functional groups.


image file: c6ra24977a-f6.tif
Fig. 6 FT-IR spectrum of the (a) aqueous extract of leaves of Ruta graveolens and (b) synthesized AgNPs.

The photoluminescence (PL) spectra of AgNPs obtained with 260 nm excitation are shown in Fig. 7. A strong and well defined peak is observed in the PL spectra at around 363 nm. The enhancement of electron density in the polyphenolics compound from leaf extract, adsorbed on the surface of metal nanoparticles probably gives rise to the high photoluminescent intensity. This electron density is the major contributor to photoluminescent emission.


image file: c6ra24977a-f7.tif
Fig. 7 Photoluminescent spectra with the excitation spectra (dashed lines) and emission spectra (solid lines) of green synthesized AgNPs.

3.3 Characterization of almond shell and Ag/almond shell nanocomposite

The FT-IR spectra of almond shells and Ag/almond shell, which are characteristic of cellulose content, are shown in Fig. 8. The presence of hydroxyl group (–OH) stretching is indicated by the broad peaks, observed mainly in raw materials at around 3430 cm−1. The peaks between 2950 and 2850 cm−1 are associated with aliphatic C–H deforming vibration. The presence of atmospheric carbon dioxide is indicated by the small band at 2398 cm−1. The bands around 1740 cm−1 are assigned to C[double bond, length as m-dash]O vibration in carbonyl group or the presence of carboxylic bonds. The bands observed at around 1600 cm−1 are due to the aromatic C[double bond, length as m-dash]O ring stretching (possibly COOH) or C[double bond, length as m-dash]C stretching of aromatic groups in lignin, implying the presence of lignin.28 The broad peak in the 1040–1070 cm−1 region may be due to C–OH stretching vibration of alcoholic groups and carboxylic acids.29
image file: c6ra24977a-f8.tif
Fig. 8 FT-IR spectrum of the (a) almond shell (b) synthesized Ag/almond shell nanocomposite.

The expected crystallinity of AgNPs is shown by the powder XRD patterns for the almond shell and Ag/almond shell nanocomposite. The typical broad peak of the carbonaceous structure in the XRD of the almond shell sample is due to the amorphous organic matter (cellulose, hemicelluloses and lignin) (Fig. 9).28,30 Broad peaks of 2θ values of 38.2, 44.21, 63.2 and 77.3 degrees, assigned to the corresponding 111, 200, 220 and 311 indices of the face centered cubic (FCC) lattice in accordance with Ag immobilization, are shown in Fig. 9.19 The pattern is very clean, showing no sign of impurities such as silver oxide (Ag2O).


image file: c6ra24977a-f9.tif
Fig. 9 XRD powder pattern of almond shell, AgNPs Ag/almond shell nanocomposite.

The crystalline size is determined by applying Debye–Scherrer formula:31

 
D = /β[thin space (1/6-em)]cos[thin space (1/6-em)]θ (1)
where D is the crystalline size, β is the full width half maximum (FWHM) of the 2θ peak, k is the shape of particle factors (it equals to 0.89), θ and l are the incident of angle and wavelength of the X-rays, respectively. The average crystalline size of AgNPs associated with the all diffraction peaks was estimated about 15.20 nm. This result is in close agreement with the particle size determined by TEM.

FE-SEM was used in the characterization of the morphology of almond shell (Fig. 10). Almond shell was shown to have a sheet like structure. In addition, a series of 1 μm pores are observed on the almond surface. The interesting point is that the porous structure is similar to the structure of almond shell and may possess the catalyst porosity for dye absorption and higher efficiency.


image file: c6ra24977a-f10.tif
Fig. 10 SEM images of almond shell.

EDS spectroscopy was used to analyze the elemental composition of seashell, confirming the presence of C, O, N and Ca in the almond shell (Fig. 11).


image file: c6ra24977a-f11.tif
Fig. 11 EDS spectrum of almond shell.

Furthermore, the presence of AgNPs has been verified by EDS analysis (Fig. 13). The amount of Ag incorporated into the Ag/almond shell nanocomposite, determined by EDS, was 7.3 wt%.


image file: c6ra24977a-f12.tif
Fig. 12 FE-SEM images of Ag/almond shell.

image file: c6ra24977a-f13.tif
Fig. 13 EDS spectrum of Ag/almond shell.

The synthesized AgNPs have been immobilized on the almond shell surface, as shown by FE-SEM of Ag/almond shell (Fig. 12). The presence of Ag was also verified by the elemental mapping images (Fig. 14). TEM was used to examine the size and shape of the AgNPs on the surfaces of almond shell (Fig. 15). The particle size of spherical silver NPs on the surface of support is observed to be 10–15 nm. It is observed that size of AgNPs correspond with the calculated size by Scherrer equation.


image file: c6ra24977a-f14.tif
Fig. 14 Elemental mappings for Ag/almond shell nanocomposite; (blue) C, (yellow) O, Ca, and (red) Ag.

image file: c6ra24977a-f15.tif
Fig. 15 Typical TEM images of AgNPs/almond shell.

AgNPs have thus been successfully synthesized and immobilized on the almond shell surface based on the results of XRD, SEM and TEM for the Ag/almond shell nanocomposite.

3.4 Degradation of 4-NP using green synthesized AgNPs/almond shell

The reduction of aqueous solutions of 4-NP in the presence of NaBH4 at ambient temperature was used to evaluate the catalytic activity of the Ag/almond shell nanocomposite (Scheme 1). UV-visible spectroscopy measurements at regular time intervals were used to monitor the progress of the reaction. 4-NP has a maximum absorption at 317 nm in aqueous medium (Fig. 16). In the absence of the catalyst, the peak at 317 nm does not change even after a couple of days. 2.5 mM solution of 4-NP (25.0 mL) was mixed with a freshly prepared solution of 0.25 M aqueous NaBH4 (25.0 mL) and Ag/almond shell nanocomposite (5.0 mg) at ambient temperature to evaluate the catalytic activity of the Ag/almond shell nanocomposite. Upon addition of NaBH4 into 4-NP solution, the light yellow color of the solution changed to intense yellow, showing an absorption peak at about 405 nm due to the formation of 4-nitrophenolate ions under alkaline conditions, which did not change as time passed. When Ag/almond shell nanocomposite was added into the reaction mixture, the peak at 400 nm decreased and a new peak corresponding to the formation of 4-aminophenol (4-AP) appeared at about 300 nm (Fig. 16). The whole peak at 400 nm disappeared after about 4.5 min and the yellow color of the solution changed to white, indicating the conversion of 4-NP to 4-AP. Therefore, pure AgNPs can catalyze 4-NP reduction to 4-AP, but at slower reaction rates than Ag/almond shell nanocomposite. A longer reaction time of 15 minutes was required for complete reduction of 4-NP to 4-AP by NaBH4 using pure AgNPs (Table 1). Thus, Ag/almond shell nanocomposite has a higher catalytic activity in the reduction of 4-NP to 4-AP compared with AgNPs alone. This can be attributed to the possibility of the almond shell support playing an active part in the catalysis, leading to a synergistic effect.8
image file: c6ra24977a-s1.tif
Scheme 1 Mechanism of the catalytic reduction and degradation of 4-NP with Ag/almond shell nanocomposite at room temperature.

image file: c6ra24977a-f16.tif
Fig. 16 UV-visible spectra for catalytic reduction of 4-NP to 4-AP at several interval, conditions: [4-NP] = 2.5 × 10−3 M, [NaBH4] = 0.25 M, Ag/almond shell = 5.0 mg.
Table 1 Completion time for the reduction of 25 mL of RhB and MB dyes (10 ppm) in the presence of 25 mL of NaBH4 (2.6 × 10−3 M) and 4-NP (2.5 mM) in the presence of 25 mL of NaBH4 (0.25 M), using 5 mg of AgNPs, almond shell and Ag/almond shell
Catalyst Time (min)
4-NP RhB MB
a Not completed.
Ag/almond shell 4.5 2 10 s
AgNPs 15 9 5
Almond shell 45a 45a 45a


3.5 Degradation of RhB and MB using green synthesized AgNPs/almond shell

Significant pollution is caused by dyes and other dyestuffs, which are the major effluents from the textile industry.32,33 Most dyes are not biodegradable. Thus, the development of an environmentally friendly method for reduction of these compounds in aqueous media is highly desirable. The reductions of RhB and MB by NaBH4 have been chosen as model reactions to study the performance of the synthesized Ag/almond shell nanocomposite. The sequences of the steps in this reaction are: adsorption of NaBH4 onto the surface of catalyst to form metal hydride, adsorption of MB (RhB) onto the surface of catalyst, and reduction and desorption of MB (RhB) to create a free space for the reaction to continue. The decrease of absorbance at λmax (λmax (RhB) = 550 nm and λmax (MB) = 663 nm) with time was used to spectrophotometrically monitor the reduction of RhB and MB by NaBH4 (Fig. 17). RhB and MB catalytic reduction by NaBH4 proceeded successfully, as expected (Table 1). The effects of the amount of the catalyst and NaBH4 were determined for reduction reaction. No product was obtained in the absence of the catalyst. Thus, indicating that the catalytic reduction occurs at the surface of catalyst. In the absence of catalyst, no significant color change was observed within the reaction time and the peak remained unaltered for a long duration. On the other hand, in the absence of NaBH4, no reduction occurred in the presence of catalyst. Also, no significant color change was observed in the presence of catalyst and in the absence of NaBH4. Thus, the reduction reaction was carried out in the presence of catalyst and NaBH4.
image file: c6ra24977a-f17.tif
Fig. 17 UV-Vis spectra of reduction of (a) RhB (2.1 × 10−5 M) and (b) MB (3.1 × 10−5 M) with [NaBH4] = 2.6 × 10−3 M in presence of Ag/almond shell nanocomposite = 5.0 mg.

The applicability and efficiency of the synthetic catalysts was evaluated by comparison of the results with those of the recently reported methods for the reduction of variety of dyes by NaBH4 (Table 2). The proposed method is the shortest method for the reduction of organic dyes reported so far.

Table 2 Comparison of various catalysts in the reduction of 4-NP, RhB and MB dyes with NaBH4
Substrate Catalyst Time Ref.
4-NP Ag/KCC-1 8.5 min 34
Cu microspheres 18 min 35
Ni NPs 16 min 36
Pd-FG 12 min 37
Ni–PVAm/SBA-15 85 min 38
Fe3O4@SN–Ag 10 min 39
Ag/GO-Dopa 8 min 40
Ag/almond shell 4 min This work
RhB Fe3O4/Ag 15 min 41
PS/Ag 10 min 42
Ag/HLaNb2O7 47 min 3
Ag/zeolite nanocomposite 7.5 min 19
Ag/almond shell 2 min This work
MB Ag/zeolite nanocomposite 50 s 7
AgNPs on silica spheres 7.5 min 3
SiNWAs–Cu 10 min 43
Au@TiO2 12 min 44
Ru nanocrystals 9 min 45
Ag/almond shell 31 s This work


3.6 Catalyst recyclability

The recovery and recyclability of the AgNPs/almond shell was also studied in 4-NP reduction. Upon completion of the reaction, monitored by UV-Vis spectroscopy, the catalyst was removed from the reaction mixture by mild centrifugation, washed several times with distilled water, dried and used in the next reactions. The catalyst was observed to function well up to five catalytic runs with 100% reduction of 4-NP, demonstrating the high stability and catalytic activity of Ag/almond shell under the operating conditions. The recyclability of the AgNPs/almond shell was also studied in the reduction of RhB and MB under the reaction conditions. The results of recycling experiments showed that the catalyst could be recycled at least five times for 100% reduction of RhB and MB.

4 Conclusions

Ag/almond shell nanocomposite has been synthesized via a green method using the extract of leaves of Ruta graveolens. Phenolic acid and flavonoids in the Ruta graveolens leaf extract, both of which act as reducing and stabilizing agents, probably facilitate the formation of the Ag/almond shell nanocomposite by Ag(I) reduction. Strong catalytic activity is shown by Ag/almond shell nanocomposite in the base and ligand free oxidative hydroxylation of phenylboronic acid to phenol and the reduction of 4-NP, RhB and MB at ambient temperature. This simple and versatile protocol has been used in the synthesis of phenol in high yields. The catalyst could be recycled several times with no loss of catalytic activity.

Acknowledgements

The author is thankful to Iran National Science Foundation (INSF) for supporting this project numbered 95823609.

Notes and references

  1. P. K. Jain, X. Huang, I. H. El-Sayed and M. A. El-Sayed, Acc. Chem. Res., 2008, 41, 1578–1586 CrossRef CAS PubMed.
  2. J. M. Campelo, D. Luna, R. Luque, J. M. Marinas and A. A. Romero, ChemSusChem, 2009, 2, 18–45 CrossRef CAS PubMed.
  3. Z.-J. Jiang, C.-Y. Liu and L.-W. Sun, J. Phys. Chem. B, 2005, 109, 1730–1735 CrossRef CAS PubMed.
  4. N. Pradhan, A. Pal and T. Pal, Colloids Surf., A, 2002, 196, 247–257 CrossRef CAS.
  5. E. Qayyum, V. A. Castillo, K. Warrington, M. A. Barakat and J. N. Kuhn, Catal. Commun., 2012, 28, 128–133 CrossRef CAS.
  6. A. Keshavaraja, X. She and M. Flytzani-Stephanopoulos, Appl. Catal., B, 2000, 27, L1–L9 CrossRef CAS.
  7. A. Hatamifard, M. Nasrollahzadeh and S. M. Sajadi, New J. Chem., 2016, 40, 2501–2513 RSC.
  8. M. Atarod, M. Nasrollahzadeh and S. Mohammad Sajadi, J. Colloid Interface Sci., 2016, 462, 272–279 CrossRef CAS PubMed.
  9. H. Li, Y. Zhang, G. Chang, S. Liu, J. Tian, Y. Luo, A. M. Asiri, A. O. Al-Youbi and X. Sun, ChemPlusChem, 2012, 77, 545–550 CrossRef CAS.
  10. P. Zhang, C. Shao, Z. Zhang, M. Zhang, J. Mu, Z. Guo and Y. Liu, Nanoscale, 2011, 3, 3357–3363 RSC.
  11. S. P. Dubey, M. Lahtinen and M. Sillanpää, Process Biochem., 2010, 45, 1065–1071 CrossRef CAS.
  12. A. B. S. Sastry, R. B. Karthik Aamanchi, C. Sree Rama Linga Prasad and B. S. Murty, Environ. Chem. Lett., 2013, 11, 183–187 CrossRef CAS.
  13. S. Basu, P. Maji and J. Ganguly, Appl. Nanosci., 2016, 6, 1–5 CrossRef CAS.
  14. S. Ahmed, M. Ahmad, B. L. Swami and S. Ikram, J. Adv. Res., 2016, 7, 17–28 CrossRef CAS PubMed.
  15. T. J. I. Edison and M. G. Sethuraman, Process Biochem., 2012, 47, 1351–1357 CrossRef CAS.
  16. A. Singh, D. Jain, M. Upadhyay, N. Khandelwal and H. Verma, Digest Journal of Nanomaterials and Biostructures, 2010, 5, 483–489 Search PubMed.
  17. S. Li, Y. Shen, A. Xie, X. Yu, L. Qiu, L. Zhang and Q. Zhang, Green Chem., 2007, 9, 852–858 RSC.
  18. H. Bar, D. K. Bhui, G. P. Sahoo, P. Sarkar, S. Pyne and A. Misra, Colloids Surf., A, 2009, 348, 212–216 CrossRef CAS.
  19. A. Hatamifard, M. Nasrollahzadeh and S. M. Sajadi, New J. Chem., 2016, 40, 2501–2513 RSC.
  20. A. Rostami-Vartooni, M. Nasrollahzadeh and M. Alizadeh, J. Colloid Interface Sci., 2016, 470, 268–275 CrossRef CAS PubMed.
  21. T. N. J. I. Edison, Y. R. Lee and M. G. Sethuraman, Spectrochim. Acta, Part A, 2016, 161, 122–129 CrossRef CAS PubMed.
  22. H. Ekiert, A. Szewczyk and A. Kuś, Die Pharmazie, 2009, 64, 692–694 Search PubMed.
  23. A. L. Dawidowicz, K. Bernacik and R. Typek, Food Analytical Methods, 2016, 9, 213–224 CrossRef.
  24. J. M. Martínez, J. Reguant, M. Á. Montero, D. Montané, J. Salvadó and X. Farriol, Ind. Eng. Chem. Res., 1997, 36, 688–696 CrossRef.
  25. H. Pirayesh and A. Khazaeian, Composites, Part B, 2012, 43, 1475–1479 CrossRef CAS.
  26. M. A. Abedini Najafabadi, S. N. Khorasani and J. M. Esfahani, Polym. Polym. Compos., 2014, 22, 409–416 Search PubMed.
  27. M. Kamiński, R. Kartanowicz, M. M. Kamiński, A. Królicka, M. Sidwa-Gorycka, E. Łojkowska and W. Gorzeń, J. Sep. Sci., 2003, 26, 1287–1291 CrossRef.
  28. M. Konsolakis, N. Kaklidis, G. E. Marnellos, D. Zaharaki and K. Komnitsas, RSC Adv., 2015, 5, 73399–73409 RSC.
  29. S. Hashemian and J. Shayegan, Orient. J. Chem., 2014, 30, 2091–2098 CrossRef CAS.
  30. B. Peters, Fuel Process. Technol., 2011, 92, 1993–1998 CrossRef CAS.
  31. A. L. Patterson, Phys. Rev., 1939, 56, 978–982 CrossRef CAS.
  32. M. Bordbar, B. Khodadadi, N. Mollatayefeh and A. Yeganeh-Faal, J. Appl. Chem., 2013, 8, 1–5 Search PubMed.
  33. B. Khodadadi, M. Bordbar and A. Yeganeh-Faal, J. Sol-Gel Sci. Technol., 2016, 77, 521–527 CrossRef CAS.
  34. Z. Dong, X. Le, X. Li, W. Zhang, C. Dong and J. Ma, Appl. Catal., B, 2014, 158–159, 129–135 CrossRef CAS.
  35. E. S. Abdel-Halim, M. H. El-Rafie and S. S. Al-Deyab, Carbohydr. Polym., 2011, 85, 692–697 CrossRef CAS.
  36. Z. Jiang, J. Xie, D. Jiang, X. Wei and M. Chen, CrystEngComm, 2013, 15, 560–569 RSC.
  37. Z. Wang, C. Xu, G. Gao and X. Li, RSC Adv., 2014, 4, 13644–13651 RSC.
  38. R. J. Kalbasi, A. A. Nourbakhsh and F. Babaknezhad, Catal. Commun., 2011, 12, 955–960 CrossRef CAS.
  39. Z.-Z. Wang, S.-R. Zhai, F. Zhang, Z.-Y. Xiao, B. Zhai and Q.-D. An, J. Sol-Gel Sci. Technol., 2015, 73, 299–305 CrossRef CAS.
  40. E. K. Jeon, E. Seo, E. Lee, W. Lee, M.-K. Um and B.-S. Kim, Chem. Commun., 2013, 49, 3392–3394 RSC.
  41. L. Ai, C. Zeng and Q. Wang, Catal. Commun., 2011, 14, 68–73 CrossRef CAS.
  42. Z. Deng, H. Zhu, B. Peng, H. Chen, Y. Sun, X. Gang, P. Jin and J. Wang, ACS Appl. Mater. Interfaces, 2012, 4, 5625–5632 CAS.
  43. X. Yang, H. Zhong, Y. Zhu, H. Jiang, J. Shen, J. Huang and C. Li, J. Mater. Chem. A, 2014, 2, 9040–9047 CAS.
  44. M. M. Khan, J. Lee and M. H. Cho, J. Ind. Eng. Chem., 2014, 20, 1584–1590 CrossRef CAS.
  45. B. K. Ghosh, S. Hazra, B. Naik and N. N. Ghosh, J. Nanosci. Nanotechnol., 2015, 15, 6516–6523 CrossRef PubMed.

This journal is © The Royal Society of Chemistry 2017